An expansion agent and water-reducing technology, applied in the field of concrete expansion agent, can solve the problems of insufficient synchronization of compensation and shrinkage, low expansion efficiency and high alkali content, and achieve the effects of strong adaptability, good compatibility and low alkali content.

Inactive Publication Date: 2009-06-17
广西云燕特种水泥建材有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a water-reducing concrete expansion agent with three expansion sources, which can overcome technical defects such as low expansion rate of water-reducing composite expansion agents on the market, insufficient synchronization of compen

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water reduction type three-expansion source cement expansive material
  • Water reduction type three-expansion source cement expansive material
  • Water reduction type three-expansion source cement expansive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] (1), the preparation process formula is shown in Table 1:

[0053] Table 1 (unit: kg)

[0054]

hard rock

ointment

High aluminum cooked

Material

high calcium sulfur

Aluminum clinker

Calcined magnesite

mine

water slag

Superplasticizer

polycarboxylate

salt (external

mixed) Aquasorb

HPMC (external

mixed) 50 10 25 3 12 3.0 0.02

[0055] (2), preparation process:

[0056] The bulk raw material gypsum, high alumina clinker, high calcium sulfur aluminum clinker and calcined magnesite are passed through the Bucket→Second Homogenization Store→Get Ordinary Expansion Agent→Add external materials according to Table 1, add water reducer polycarboxylate and water retaining agent cellulose ether HPMC→Mix in the third mill→Third Storage hopper→third homogenization storage→water-reducing concrete expansion agent with three expansion sources→packing hopper→packing machine→warehous...

Embodiment 2

[0061] (1), the preparation process formula is shown in Table 3

[0062] Table 3 (unit: kg)

[0063]

Anhydrite

High alumina clinker

High Calcium Sulfur Aluminum

Clinker

Calcined magnesite

mine

water slag

Water reducer poly

Carboxylate

(external mixing) Aquasorb

HPMC (external

mixed) 55 10 30 2 3 3.0 0.02

[0064] (2), preparation process:

[0065] The bulk raw material gypsum, high alumina clinker, high calcium sulfur aluminum clinker and calcined magnesite are passed through the Bucket→Second Homogenization Storage→Ordinary Expansion Agent→According to Table 1, mix external materials, add water reducing agent polycarboxylate and water retaining agent cellulose ether HPMC→mix in the third mill→third storage Bucket→third homogenization storehouse→water-reducing concrete expansion agent with three expansion sources→packing bucket→packing machine→warehouse→testing→delivery.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a slushing type three expansion source concrete expansion agent, which is characterized by comprising preparation of raw materials such as anhydrite, high alumina chamotte, high-calcium sulphoaluminate chamotte, calcined magnesite and so on by weight portion and externally doped slushing agent and water retention agent. The preparation method of the expansion agent comprises steps of crushing, common mixture, mixing and grinding and external doping mixture and finish product forming. The product has low alkali content, excellent expansion performance, synchronous shrinkage-compensating effect and strong suitability with concrete; and newly mixed concrete has small bleeding rate and high vicidity of slurry, and the slurry has strong function of coating and supporting aggregate to greatly reduce the phenomenon of sinking of coarse aggregate, so that the newly mixed concrete keeps good homogenization in the construction process and balanced mechanical property after hardening, and is simple and convenient to use and easy to control quality in construction. The slushing type three expansion source concrete expansion agent is suitable for multiple kinds of concrete for construction.

Description

technical field [0001] The present invention relates to concrete, especially concrete expansive agent. technical background [0002] With the large-scale application of commercial and high-performance concrete in my country, the prominent contradiction is that the probability of cracks in concrete engineering increases, and harmful cracks are directly related to the durability of structures. Commercial housing has involved people's livelihood issues, and users have strongly responded to this. In recent years, the Ministry of Construction and engineering circles have attached great importance to the control of concrete cracks. From the material point of view, concrete expansion agent, shrinkage reducer, steel fiber and synthetic organic fiber are all effective measures to reduce or disperse cracks, but in terms of material price and construction convenience, expansion agent has more advantages. Academician Wu Zhongwei of my country pointed out that "micro-cracks to visible c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/38C04B22/14
CPCC04B40/0039Y02W30/91C04B7/32C04B7/323C04B11/06C04B22/066C04B28/02C04B18/141
Inventor 李光达黄芳许建兴
Owner 广西云燕特种水泥建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap