Processing method of magnetic conductive glassware
A technology of glassware and processing methods, applied in the direction of cooking utensils, special materials for cooking utensils, electric heating fuel, etc., to achieve the effects of improving appetite, improving surface hardness and wear resistance, and facilitating clamping
Active Publication Date: 2010-09-29
ZHEJIANG COOKER KING COOKER
View PDF6 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] In order to overcome the disadvantage that existing glassware cannot be used for heating in an induction cooker, the purpose of this invention is to provide a processing method for magnetically conductive glassware with simple and reasonable structure, convenient production and processing, good magnetic and thermal conductivity, and long service life.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0015] figure 1 As shown, the present invention creates a specific embodiment of a processing method for magnetically conductive glassware, wherein the above-mentioned glassware includes a glass pot cover 1, a glass pot body 3, and symmetrical pot ears 2 are provided on the upper edge of the glass pot body 3 , the glass pot cover 1 is matched with the glass pot body 3, and the above-mentioned processing method comprises the following steps:
[0016] (1) Preparation process: Spray a layer of glass-ceramic adhesive on the inner and outer surfaces of silver foil with moderate thickness, then spray a layer of enamel colorant on the outer surface for coloring, and paste roll stickers on the inner surface; Foil is made into the silver disc 4 consistent with the bottom of the glass pot body, and the enamel coloring agent can be the common coloring agent used on the porcelain at present;
[0017] (2), double-bottom process: clean the glass pot body 3; when double-bottoming, first so...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a processing method of magnetic conductive glassware, which comprises the steps of preparation process, bottom-compounding process and sintering process. In the preparation proThe invention discloses a processing method of magnetic conductive glassware, which comprises the steps of preparation process, bottom-compounding process and sintering process. In the preparation prooled after leaving a stove. After adopting the structure, the invention solves the problem that the glassware can not be heated by an induction cooker, and has the characteristics of simple and reasoooled after leaving a stove. After adopting the structure, the invention solves the problem that the glassware can not be heated by an induction cooker, and has the characteristics of simple and reasonable structure, convenient production and processing, good magnetic and heat conduction property, and the like.nable structure, convenient production and processing, good magnetic and heat conduction property, and the like.cess, glass and ceramic adhesive is sprayed on the outer surface and the inner surface of a silver foil, enamel colorant is sprayed on the outer surface of the silver foil, coiled paster is stuck on tcess, glass and ceramic adhesive is sprayed on the outer surface and the inner surface of a silver foil, enamel colorant is sprayed on the outer surface of the silver foil, coiled paster is stuck on the inner surface, and then forming is carried out; in the bottom-compounding process, a glass boil body (3) is washed, a silver disk (4) is dipped in clean water for 10-50min to be stuck on the bottomhe inner surface, and then forming is carried out; in the bottom-compounding process, a glass boil body (3) is washed, a silver disk (4) is dipped in clean water for 10-50min to be stuck on the bottomof the glass boiler body (3), and then the silver disk is naturally dried; and in the sintering process, the glass boiler body (3) is placed in a stove tunnel stream line for sintering, the stove tem of the glass boiler body (3), and then the silver disk is naturally dried; and in the sintering process, the glass boiler body (3) is placed in a stove tunnel stream line for sintering, the stove temperature is controlled to be within 400 DEG C in a first stage for 2h, the stove temperature is controlled to be within 400-700 DEG C in a second stage for 2h, and the glass boiler body is naturally cperature is controlled to be within 400 DEG C in a first stage for 2h, the stove temperature is controlled to be within 400-700 DEG C in a second stage for 2h, and the glass boiler body is naturally co
Description
technical field [0001] The invention relates to a glassware, in particular to a method for processing a magnetically conductive glassware heated by an electromagnetic oven. Background technique [0002] Currently used hot pots can be divided into charcoal hot pots, solid alcohol hot pots, electric hot pots and induction cooker hot pots according to their heating methods. The pot body is generally made of stainless steel or copper products; Troublesome fires, low thermal efficiency, unhygienic, poor safety performance, etc., have been basically eliminated in daily households, and are still used in the catering industry; electric hot pots and induction cooker hot pots are currently the most used hot pots in households and catering industries, and their advantages are fast heating and clean. Hygienic, impact-resistant, and not easy to break, its disadvantages are that the appearance of the pot is not elegant enough, it is easy to burn people, it is impossible to observe the foo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): A47J27/00A47J36/02F24C7/00
Inventor 王鹏徐敏
Owner ZHEJIANG COOKER KING COOKER