High-elastic wear-resistant calendered film production process

A technology for calendering film and production process, applied in the field of high-elasticity and wear-resistant calendering film production technology, can solve the problems of increased torque, insufficient elasticity and wear resistance, etc., to increase power, increase effect and change, Satisfy the effect of high elasticity and wear resistance

Inactive Publication Date: 2009-09-16
FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing ordinary PVC calendered film does not meet the requirements of elasticity and wear resistance in actual use. Although TPU polyurethane elastomer material is added to the formula for modification, due to the addition of elastomer in the production process,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-elastic wear-resistant calendered film production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The raw material formula of the high elastic and wear-resistant calendered film is according to the conventional PVC calendered film formula; or, according to the following raw material ingredients: PVC-K-60: 100PHR; DOP: 28 PHR; DOA: 6PHR; ultraviolet absorber UV-531: 0.18 PHR ; Liquid barium-zinc composite stabilizer CRV-301H: 1.8 PHR; Pigment 3PHR; Calcium carbonate CaCO 3 : 5phr.

[0034] Wherein, that is to say, the K value of the PVC used is 60-65.

[0035](1) Batching: The various ingredients of the high-elastic wear-resistant calendered film are weighed according to a certain ratio, the so-called production formula, and the metering of the liquid is carried out; the batching step can be automatically obtained from the storage tank according to the required formula. measurement;

[0036] (2) High-speed stirring: Put the mixed materials into a high-speed mixer for stirring. The low-speed stirring time is 20 seconds, the high-speed stirring time is 200 seconds, t...

Embodiment 2

[0045] The raw material formula of the high elastic and wear-resistant calendered film is according to the conventional PVC calendered film formula; or, according to the following raw material ingredients: PVC-K-65: 100 PHR; DOP: 42 PHR; DOA: 12 PHR; UV absorber UV-531: 0.25 PHR; liquid barium zinc composite stabilizer CRV-301H: 1.8 PHR; pigment 10PHR; calcium carbonate CaCO 3 : 10 PHR.

[0046] The K value of the PVC used is 60-65.

[0047] The specific process steps are

[0048] (1) Batching: The various ingredients of the high-elastic wear-resistant calendered film are weighed according to a certain ratio, the so-called production formula, and the metering of the liquid is carried out; the batching step can be automatically obtained from the storage tank according to the required formula. measurement;

[0049] (2) High-speed stirring: Put the mixed materials into a high-speed mixer for stirring. The low-speed stirring time is 20 seconds, the high-speed stirring time is 2...

Embodiment 3

[0058] The raw material formula of the high elastic and wear-resistant calendered film is according to the conventional PVC calendered film formula; or, according to the following raw material ingredients: PVC-K-63: 100PHR; DOP: 35PHR; DOA: 10 PHR; UV absorber UV-531: 0.20 PHR ;Liquid Barium Zinc Composite Stabilizer CRV-301H: 1.8 PHR; Pigment 7 PHR; Calcium Carbonate CaCO 3 : 8 PHR.

[0059] The K value of the PVC used is 63.

[0060] The specific process steps are

[0061] (1) Batching: The various ingredients of the high-elastic wear-resistant calendered film are weighed according to a certain ratio, the so-called production formula, and the metering of the liquid is carried out; the batching step can be automatically obtained from the storage tank according to the required formula. measurement;

[0062] (2) High-speed stirring: Put the mixed materials into a high-speed mixer for stirring. The low-speed stirring time is 20 seconds, the high-speed stirring time is 230 sec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-elastic wear-resistant calendered film production process which comprises the steps of: material preparation, high-speed stirring, plastification by an internal mixer, filtering feeding by a double-screw extruder, molding by a calendar, distraction device, cooling sizing, surface embossing processing, cooling sizing, trimming and rolling. The technical flow is scientific and reasonable; material reaction is sufficient; yield and product quality are significantly improved, and market competition capability of the product is improved, therefore, the production process has obvious economic benefit and is suitable for large-scale promotion and application.

Description

technical field [0001] The invention belongs to the field of chemical industry, and more specifically relates to a production process of a high-elastic and wear-resistant rolling film. Background technique [0002] The existing ordinary PVC calendered film does not meet the requirements of elasticity and wear resistance in actual use. Although TPU polyurethane elastomer material is added to the formula for modification, due to the addition of elastomer in the production process, the torque in the plasticizing stage Increase, need to carry out transformation to original equipment and technological process, so this patent except increasing the power of internal mixer, changes original open mill process and uses twin-screw extruder technological process instead. Contents of the invention [0003] The purpose of the present invention is to provide a high-elastic wear-resistant calendering film production process, the process flow is scientific and reasonable, the material reac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C69/02B29C47/92B29C47/68B29C43/24B29C43/58B29C55/02B29C35/16B29C59/04B29B7/28B29K27/06B29K105/00B29L7/00B29C48/40B29C48/92
CPCB29C48/08B29C48/40
Inventor 张宏旺黄万能李如晓蒋石生
Owner FUJIAN SIJIA ENVIRONMENTAL PROTECTION MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap