Universal ship bottom antifouling coating

A general-purpose antifouling paint technology, applied in antifouling/underwater paints, biocide-containing paints, coatings, etc., can solve problems such as unsuitable addition of cuprous oxide and loss of antifouling effect of cuprous oxide

Inactive Publication Date: 2009-10-07
上海海悦涂料有限公司
View PDF2 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the waterline part of the ship, long-term sunlight and alternating wet and dry, cuprous oxide (Cu 2 O) It is easy to oxidize and decompose and lose the antifouling effect, and it is not suitable to add

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The present invention is described in detail below by two specific examples:

[0022] Embodiment one of the present invention is " 859 general type ship bottom antifouling paint ", and the formula by weight is:

[0023] (1) Zinc acrylate resin: 30 parts by weight

[0024] (2) Composite organic antifouling agent: 22 parts by weight, wherein 10 parts by weight of cuprous thiocyanate (CuSCN), 5 parts by weight of zinc pyrithione, Seanine 211 (4,5-dichloro-2-n-octyl- 3-isothiazole copper) 3 parts by weight, Zineb (1,2-ethylene bisdithiocarbamate zinc) 4 parts by weight

[0025] (3) Pigment: 3 parts by weight of talcum powder, 10 parts by weight of zinc oxide, 0.2 part by weight of phthalocyanine blue

[0026] (4) The mixed solvent is: 15 parts by weight of xylene, 5 parts by weight of butyl acetate

[0027] (5) The dispersant is: 0.2 grams of methoxypropyl ester solution

[0028] (6) Anti-settling agent: 2 grams of organic bentonite

[0029] The preparation method is a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses universal ship bottom antifouling coating, and relates to universal high-solid self-polishing ship bottom antifouling coating, in particular to novel marine antifouling coating containing an antifouling agent system without cuprous oxide and other internationally non-permissible toxins and reaching the national environment-friendly requirements. The universal ship bottom antifouling coating is characterized by comprising zinc acrylate resin, composite antifouling agents, pigments, fillers, anti-sedimentation agents, solvents, and the like and being of various colors. The coating is applicable to marine engineering or a ship bottom as an antifouling coating, can be used at aluminum substrate surfaces, steel substrate surfaces and waterline positions, can effectively prevent the ship bottom from fouling by marine organisms within 1-2 years, is environment-friendly and constructed conveniently, can keep the speed of a ship uninfluenced, and saves fuel; and the coating further has good overcoatability.

Description

technical field [0001] The invention relates to an antifouling paint, in particular to a general-purpose high-solid self-polishing antifouling paint for ship bottoms, which can be used on the surface of aluminum and steel substrates and waterline parts, and does not contain cuprous oxide and other international Prohibited toxic materials meet the national environmental protection requirements. Background technique [0002] The primary problem encountered by ships navigating in the sea is the attachment and fouling of marine organisms to the bottom of the ship. More than 200,000 species of marine organisms have been preliminarily proven, and some organisms grow by attaching to fixed objects. The bottom of a ship below the waterline is the main base for organisms attaching, and marine organisms attaching to them has brought great harm to ship navigation. The amount of marine organisms in the South my country Sea area is as high as 20 kg per square meter during the peak growth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/02C09D5/16
Inventor 徐建平张光铭沈佩芝
Owner 上海海悦涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com