Water-borne permeable crystalline waterproofing material and preparation method thereof
A technology of infiltrating crystalline and waterproof materials, applied in the field of construction engineering, can solve the problems of construction trouble, no chemical composition, affecting the waterproof effect, etc., and achieve the effect of eliminating the impact.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0022] The first step is to weigh 24.40kg of deionized water and place it in the reactor, slowly add 0.013kg of nonylphenol polyoxyethylene ether under the environment of medium-speed mechanical stirring at a speed of 150-200rpm and continue stirring for 5 minutes , slowly add 0.022kg of alkylbenzenesulfonic acid, stir for 10 minutes, add 0.121kg of isopropanol, perform low-speed mechanical stirring at a speed of 50-60rpm for 15 minutes, cover the reactor lid, and let it slowly cool to room temperature, And let stand for 24 hours. An organic active medium solution is formed.
[0023] Second step, take by weighing 24.40kg deionized water and be placed in reactor, under the environment that carries out medium-speed mechanical stirring under the rotating speed of 150~200rpm, slowly add 19.212kg mass percent concentration and be the sodium silicate aqueous solution of 50%, in Perform medium-speed mechanical stirring at a rotational speed of 150-200 rpm for 15 minutes, slowly add ...
Embodiment 2
[0027] The first step is to weigh 26.94kg of deionized water and place it in the reactor, slowly add 0.075kg of nonylphenol polyoxyethylene ether under the environment of medium-speed mechanical stirring at a speed of 150-200rpm and continue stirring for 5 minutes , slowly add 0.01kg of alkylbenzenesulfonic acid, stir for 10 minutes, add 0.05kg of isopropanol, perform low-speed mechanical stirring at a speed of 50-60rpm for 15 minutes, cover the reactor lid, and let it slowly cool to room temperature, And let stand for 24 hours. An organic active medium solution is formed.
[0028] The second step is to weigh 26.94kg of deionized water and place it in the reactor, and slowly add 7.5kg of sodium silicate aqueous solution under the environment of medium-speed mechanical stirring at a speed of 150-200rpm, and carry out at a speed of 150-200rpm Stir at a medium speed for 15 minutes, slowly add the organic active medium solution, and carry out mechanical stirring at a low speed fo...
Embodiment 3
[0032]The first step is to weigh 22.31kg of deionized water and place it in the reactor, slowly add 0.005kg of nonylphenol polyoxyethylene ether under the environment of medium-speed mechanical stirring at a speed of 150-200rpm and continue stirring for 5 minutes , slowly add 0.07kg of alkylbenzenesulfonic acid, stir for 10 minutes, add 0.175kg of isopropanol, perform low-speed mechanical stirring at a speed of 50-60rpm for 15 minutes, cover the reactor lid, and let it slowly cool to room temperature, And let stand for 24 hours. An organic active medium solution is formed.
[0033] The second step is to weigh 22.31kg of deionized water and place it in the reactor, slowly add 25.0kg of sodium silicate aqueous solution under the environment of medium-speed mechanical stirring at a speed of 150-200rpm, and carry out at a speed of 150-200rpm Stir at a medium speed for 15 minutes, slowly add the organic active medium solution, and carry out mechanical stirring at a low speed for 1...
PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| purity | aaaaa | aaaaa |