Method for producing silicon mullite abrasive brick
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technology of wear-resistant bricks, which are applied in the production field of silicon molybdenum wear-resistant bricks, can solve problems such as unsatisfactory use effects, increased self-weight, and easy damage to transition zone lining bricks, so as to reduce the number of kiln shutdown maintenance and soften the load High temperature, good thermal shock stability
Active Publication Date: 2010-05-26
郑州真金耐火材料有限责任公司
View PDF0 Cites 27 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The transition zone of large-scale new dry-process cement kiln is not easy to stick to the kiln skin due to the temperature characteristics, so it suffers from mechanical stress and friction. The more prominent point is that according to the requirements of the cement sintering process, the highest temperature point of the sintering zone must be constantly Moving back and forth, due to the constant change of the temperature field, general materials cannot withstand the rapid cooling and heat caused by the change of the temperature field, resulting in the transitional zone lining bricks being easily damaged, and unable to keep pace with the life cycle of the firing zone material. With the gradual increase of the diameter of the new dry process large kiln (from 2 meters to the current 6 meters), and the increase in the speed of the kiln body (the speed of the traditional wet process long kiln is generally 60-70 rpm, and the large new dry process The kiln speed is 180-210 rpm, even as high as 240 rpm), the weight of the lining brick per unit length will increase relatively, and the thermal stress and mechanical stress on the kiln lining are much higher than those of traditional kilns.
Although cheap anti-flaking high-alumina bricks are widely used in cement enterprises with good operation technology and small kiln diameter, high-alumina bricks are restricted by the characteristics of the material itself, and are used in the transition zone of large (diameter more than 4 meters) cement rotary kilns. The effect is not ideal, the longest service life is no more than 8 months, or even only 2-3 months, and the service life of the transition zone lining brick and the firing zone kiln lining cannot be kept in sync. The transition zone kiln lining needs one year Frequent kiln maintenance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] The production method of silicon molybdenum wear-resistant brick of the present invention, it comprises the following steps:
[0018] The first step: crush the material with a jaw crusher or a cone crusher, crush the granules with a ball mill, select 3 parts of bauxite granules with a particle size of 5-3mm by weight, and bauxite with a particle size of 0.075mm<3mm 1 part of soil pellets, 2 parts of brown corundum pellets with a particle size of 3-1mm, 0.4 parts of silicon carbide pellets with a particle size of 3-1mm, 2.5 parts of bauxite powder with a particle size of ≤0.075mm, and silicon carbide with a particle size of ≤0.075mm 0.8 parts of powder, 0.2 parts of metal silicon powder with a particle size of ≤0.075mm, 0.2 part of silicon micropowder with a particle size of <0.019mm, and 0.5 part of clay powder with a particle size of ≤0.075mm;
[0019] The second step: add bauxite, brown corundum, and silicon carbide granules to the wet mill for pre-mixing for 3-5 minu...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size
aaaaa
aaaaa
density
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a method for producing a silicon mullite abrasive brick, comprising the following steps of: firstly, selecting 4 parts of bauxite granules, 2 parts of brown aluminum oxide granules, 0.4 part of carborundum granules, 2.5 parts of bauxite powder, 0.8 part of carborundum powder, 0.2 part of metallic silicon powder, 0.2 part of silicon powder and 0.5 part of clay powder in parts by weight; secondly, adding the bauxite granules, the brown aluminum oxide granules and the carborundum granules into an edge runner wet mill and premixing, then adding lignin liquor accounting for 4-5 percent of the total weight of materials and premixing, adding the bauxite powder, the carborundum powder, and the metallic silicon powder and mixing, adding the clay powder and the silicon powder, mixing and discharging ground ageing mixture; and thirdly, pressing the pug into semi-finished products, feeding the semi-finished products into a drying chamber, drying, feeding semi-finished products into a high-temperature tunnel kiln and sintering to form a finished brick body. The brick body has long service life, can keep synchronous running with a kiln liner in a firing zone, reduces the maintenance times for users to close down the kiln, and simultaneously has the advantages of high softening temperature for load, favorable thermal shock resisting stability, favorable wear-resisting performance and the like.
Description
technical field [0001] The invention relates to a production method of a refractory brick for a cement kiln, in particular to a production method of a silicon molybdenum wear-resistant brick used in the preheating zone of a cement kiln. Background technique [0002] The transition zone of large-scale new dry-process cement kiln is not easy to stick to the kiln skin due to the temperature characteristics, so it suffers from mechanical stress and friction. The more prominent point is that according to the requirements of the cement sintering process, the highest temperature point of the sintering zone must be constantly Moving back and forth, due to the constant change of the temperature field, general materials cannot withstand the rapid cooling and heat caused by the change of the temperature field, resulting in the transitional zone lining bricks being easily damaged, and unable to keep pace with the life cycle of the firing zone material. With the gradual increase of the d...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.