Halogen-free antiflaming polyester molding compound composite and preparation method thereof

A composition and polyester technology, applied in the field of flame retardant polyester composition and its preparation, can solve the problems of insufficient flame retardant grade, inability to adapt to the trend of thin and light plastic parts, etc., and achieve the effect of improving flame retardant performance

Inactive Publication Date: 2010-06-02
GUANGZHOU KINGSKY MATERIAL
View PDF1 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] WO2009082096A2[1] adopts compounding of halogen-free flame retardant OP930 and ionic polymer to obtain halogen-free flame-retardant PET with relatively excellent comprehensive performance. The heat distortion temperature is relatively high, but the flame-retardant grade is still insufficient and cannot adapt to the current plastic The trend of light and thin parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free antiflaming polyester molding compound composite and preparation method thereof
  • Halogen-free antiflaming polyester molding compound composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] Preparation method: mix each component in a twin-screw extruder (twin-screw diameter is 75mm, aspect ratio is 38), mix at a temperature of 200-300°C, discharge as strands and cool to a temperature capable of granulation Granulate. After the pellets are dried (usually at 80°C in a vacuum oven for 2 days), the resulting dried pellets are processed at a temperature of 245°C-300°C into standard samples for UL94V tests, and are also made according to GB1040, GB9341 , the standard spline specified in GB1843.

[0031] A: Two PET resins are used as examples, and the intrinsic viscosities are A1: [□] A1 =0.58dl / g, A2: [□] A2 =0.83dl / g

[0032] B: Fiberglass (HP378632MM, Taiwan Bicheng Co., Ltd.)

[0033] C1: Flame retardant, aluminum dialkyl hypophosphite, Exolite 930, 23% phosphorus content, Klein China Co., Ltd.

[0034] C2: flame retardant a: APP flame retardant, grade Exolit AP 423, Klein China Co., Ltd.

[0035] C2: flame retardant b: MCA flame retardant, grade MCA-CO...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a halogen-free antiflaming polyester molding compound composite and a preparation method thereof. The halogen-free antiflaming polyester molding compound composite is composed of the following components in weight percent: 10-60% of polyester, 10-50% of filling intensifier, 5-35% of complex flame retardant and 0.1-8.0% of other auxiliary agents. The antiflaming reinforced polyester composite prepared by the invention greatly improves the antiflaming performance of the PET molding compound composite, in particular to the antiflaming performance of thin-wall products. The molding compound composite can be processed by traditional methods, such as injection molding and extrusion molding. In addition, the antiflaming reinforced polyester composite of the invention does not contain halogen, thus protecting environment.

Description

technical field [0001] The invention relates to a flame-retardant polyester composition and its preparation technology. Background technique [0002] Polyethylene terephthalate (PET) is a semi-crystalline thermoplastic resin with good solubility resistance, high heat resistance, good ductility, high strength and modulus, and is widely used in electronics, Communications equipment, computers, televisions, kitchen and home appliances, industrial equipment, lighting systems, garden and agricultural equipment, pumps, medical devices, food handling systems, handles, power and hand tools, bobbins and spindles, and automotive interior and exterior parts. [0003] When PET resin is used in electronics, communication equipment and lighting systems, etc., the material needs to have certain flame retardant properties. In order to make PET resin flame retardant, organic and inorganic flame retardants are generally added to improve the flame retardant grade of the material. Commonly us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/04C08K7/14C08K5/5313C08K3/32C08K5/3492
Inventor 郑一泉朱文陈伟付学俊殷年伟杨志骅叶南飚
Owner GUANGZHOU KINGSKY MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap