Grade X80 pipe line steel with low yield ratio and manufacturing method thereof

A technology of low yield ratio and pipeline steel, applied in the field of metallurgy, can solve the problems of weak deformation resistance and achieve the effect of increasing strength, improving tensile strength, and excellent resistance to large deformation

Inactive Publication Date: 2010-07-07
NORTHEASTERN UNIV
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, X80 pipeline steel (pipeline steel with yield strength ≥ 555MPa) is typical acicular ferrite or bainite. Most of these structures have high strength, but the yield ratio is generally high ( higher than 0.9), so under special geological conditions, the deformation resistance of this high-grade pipeline steel is relatively weak

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grade X80 pipe line steel with low yield ratio and manufacturing method thereof
  • Grade X80 pipe line steel with low yield ratio and manufacturing method thereof
  • Grade X80 pipe line steel with low yield ratio and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Smelting and pouring into slab according to the set composition, the composition of the slab by weight percentage is: C 0.047%, Si 0.22%, Mn1.89%, S 0.002%, P 0.004%, Al 0.04%, Cu 0.22%, Cr 0.26%, Ni 0.25%, Nb 0.1%, V 0.057%, Ti 0.022%, Mo 0.23%, N 0.0035%, and the rest is Fe.

[0028] Heat the billet to 1180°C and keep it warm for 1h.

[0029] The slab is rolled in two stages, the first rolling temperature is 1150℃, the total reduction is 62.5%; the second rolling temperature is 921℃, the final rolling temperature is 856℃, the second The total reduction of the stage is controlled at 72%.

[0030] After rolling, cool to 710°C at a cooling rate of 80°C / s, air cool for 4 seconds, then cool to 460°C at a cooling rate of 24°C / s; air cool to room temperature.

[0031] The finished product thickness of X80 pipeline steel is 16mm, the yield strength is 585MPa, the tensile strength is 740MPa, the yield strength ratio is 0.790, the elongation after fracture is 18.9%, and the i...

Embodiment 2

[0034] Smelting and pouring into slab according to the set composition, the composition of the slab by weight percentage is C 0.024%, Si 0.24%, Mn1.89%, S 0.002%, P 0.012%, Al 0.035%, Cu 0.22%, Cr 0.08 %, Ni 0.24%, Nb 0.081%, V 0.03%, Ti 0.012%, Mo 0.29%, N 0.003%, Ca 0.0018%, and the rest is Fe.

[0035] Heat the slab to 1200°C and keep it warm for 1.5h.

[0036] The slab is rolled in two stages, the first rolling temperature is 1130℃, the total reduction is 62%; the second rolling temperature is 940℃, the final rolling temperature is 840℃, the second The total reduction of the stage is controlled at 68.4%.

[0037] After rolling, cool to 600°C at a cooling rate of 96°C / s, air cool for 5 seconds, then cool to 490°C at a cooling rate of 18°C / s; air cool to room temperature.

[0038] The finished product thickness of X80 pipeline steel is 12mm, the yield strength is 595MPa, the tensile strength is 745MPa, the yield strength ratio is 0.799, the elongation after fracture is 21....

Embodiment 3

[0041] Smelting and pouring into slab according to the set composition, the composition of the slab by weight percentage is: C 0.06%, Si 0.27%, Mn1.62%, S 0.0019%, P 0.0049%, Al0.045%, Cu 0.15%, Cr 0.11%, Ni 0.25%, Nb 0.072%, V 0.045%, Ti 0.022%, Mo 0.22%, N 0.0043%, and the rest is Fe.

[0042]Heat the billet to 1220°C and keep it warm for 2h.

[0043] The slab is rolled in two stages, the first rolling temperature is 1100℃, the total reduction is 62%; the second rolling temperature is 930℃, the final rolling temperature is 845℃, the second The total reduction of the stage is controlled at 68.4%.

[0044] After rolling, cool to 610°C at a cooling rate of 98°C / s, air cool for 18 seconds, then cool to 340°C at a cooling rate of 30°C / s; air cool to room temperature.

[0045] The finished product thickness of X80 pipeline steel is 12mm, the yield strength is 685MPa, the tensile strength is 860MPa, the yield strength ratio is 0.797, the elongation after fracture is 18.0%, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides grade X80 pipe line steel with low yield ratio and a manufacturing method thereof, belonging to the technical field of metallurgy; the pipe line steel consists of the following components by weight percent: 0.02-0.06% of C, 0.22-0.29% of Si, 1.6-1.9% of Mn, no greater than 0.002% of S, no greater than 0.012% of P, no greater than 0.045% of Al, 0.15-0.25% of Cu, 0.08-0.26% of Cr, 0.2-0.3% of Ni, 0.07-0.11% of Nb, 0.03-0.057% of V, 0.012-0.022% of Ti, 0.22-0.32% of Mo, no greater than 0.0043% of N, no greater than 0.0018% of Ca and the balance Fe. The manufacturing method comprises the following steps: melting and casting to obtain casting blank; heating and preserving warm; rolling the casting blank in two stages, wherein the start rolling temperature of the first stage of rolling is at 1100-1150 DEG C, the start rolling temperature of the second stage of rolling is at 920-940 DEG C, and the total rolling amount of the second stage is 68.4-72%; and after rolling, quickly cooling the casting blank, cooling the casting blank in the air, and cooling the casting blank to 340-490 DEG C at the cooling speed of 5-30 DEG C / s. The product of this invention has comparatively high strength as well as comparatively low yield ratio, namely excellent large-deformation resistance, can be used for normal transportation and supply of oil gas in earthquake-prone zones and constantly frozen zones, and has wide development prospect.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and in particular relates to a low yield ratio X80 grade pipeline steel and a manufacturing method thereof. Background technique [0002] Pipeline transportation is an important way to transport oil and natural gas over long distances. In order to improve the operational efficiency of pipeline transportation and reduce costs, pipeline transportation is developing in the direction of large-caliber and high-pressure transportation. Under the conditions of high pressure and large diameter transportation, more stringent requirements are put forward for the strength, toughness and weldability of materials. [0003] The development trend of oil and natural gas pipelines in the 21st century is mainly reflected in: high-purity steelmaking, high strength and toughness, good welding performance and excellent corrosion resistance; however, with the continuous depletion of energy, pipeline development O...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/58
Inventor 刘振宇周晓光卢敏王国栋吴迪
Owner NORTHEASTERN UNIV
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com