Production method of unsaturated polyester emulsion binder for chopped strand mats

A production method and unsaturated technology, used in adhesives, non-polymer adhesive additives, textiles and papermaking, etc., can solve the problems of long reaction period and complicated process control, and achieve simple and easy operation and good stability of the production method. , the effect of strong adhesion

Active Publication Date: 2010-08-04
JUSHI GRP CO
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the past, unsaturated polyester emulsions were prepared by chemically synthesizing unsaturated polyester resins, and then preparing emulsions by phase inversion method. The reaction cycle is long and the process control is complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare the unsaturated polyester resin emulsion binder according to the phase inversion method, 5.5 parts of unsaturated polyester resin DS-186 (produced by Shanghai Xintianhe Resin Co., Ltd.), 1.5 parts of acetone, and 3 parts of reactive emulsifier ONIST M-20S , put it into a high-speed disperser to stir, the stirring speed is 1000 rpm, after mixing evenly, add deionized water until the viscosity of the system drops suddenly, at this time the continuous phase of the system changes from the unsaturated polyester resin solution to the water phase, and a The amount of water added during phase inversion is 20% of the system. After continuing to stir at a high speed for a period of time, add an appropriate amount of deionized water to dilute to a certain concentration to prepare an unsaturated polyester resin emulsion binder for chopped strand mat. The physical parameters are as follows:

[0025] Viscosity: about 400mPa.S

[0026] Particle size: about 0.15μm

[0027] Sol...

Embodiment 2

[0032] Prepare the unsaturated polyester resin emulsion binder according to the phase inversion method, 6.5 parts of unsaturated polyester resin DS-196 (produced by Shanghai Xintianhe Resin Co., Ltd.), 1 part of acetone, reactive emulsifier ONIST M-20S2. 5 parts, put into a high-speed disperser and stir, the stirring speed is 1500 rpm, after mixing evenly, add deionized water until the viscosity of the system drops suddenly, at this time the continuous phase of the system changes from the unsaturated polyester resin solution to the water phase, When the phase inversion occurs, the amount of water added is 25% of the system. After continuing to stir at high speed for a period of time, add an appropriate amount of deionized water to dilute to a certain concentration to prepare an unsaturated polyester resin emulsion binder for chopped strand mat. The physical parameters are as follows :

[0033] Viscosity: about 550mPa.S

[0034] Particle size: about 0.18μm

[0035] Solid cont...

Embodiment 3

[0040] According to the phase inversion method to prepare unsaturated polyester resin emulsion binder, unsaturated polyester resin DS-161 (produced by Shanghai Xintianhe Resin Co., Ltd.) 7 parts, acetone 1 part, reactive emulsifier ONIST M-20S 2 Put it into a high-speed disperser and stir at a stirring speed of 2000 rpm. After mixing evenly, add deionized water until the viscosity of the system drops suddenly. At this time, the continuous phase of the system changes from an unsaturated polyester resin solution to a water phase, and The amount of water added when the phase is reversed is 30% of the system. After continuing to stir at a high speed for a period of time, add an appropriate amount of deionized water to dilute to a certain concentration to prepare an unsaturated polyester resin emulsion binder for chopped strand mat. The physical parameters are as follows:

[0041] Viscosity: about 500mPa.S

[0042] Particle size: about 0.18μm

[0043] Molecular weight: about 3000 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of an unsaturated polyester emulsion binder for chopped strand mats, which is characterized by comprising the following steps of: putting 55-70 percent of unsaturated polyester resin, 10-15 percent of acetone and 20-30 percent of reactive emulsifier in percent by weight in a high-speed dispersion machine for evenly stirring and mixing; then adding deionized water until the system generates phase inversion; keeping stirring for a while and then adding the deionized water for dilution to obtain an unsaturated polyester emulsion with a certain concentration, wherein the reactive emulsifier is a polymerizable emulsifier which contains double bonds and can participate in reaction. The production method of the unsaturated polyester emulsion binder is simple and easy to operate; the produced unsaturated polyester binder has smaller grain size, good stability, strong binding power and high penetration velocity in cinnamene, thereby being very suitable for preparing glass fibre chopped strand mats.

Description

(1) Technical field [0001] The invention relates to a production method of an unsaturated polyester emulsion, in particular to a production method of an unsaturated polyester emulsion binder for chopped strand mats. (2) Background technology [0002] Glass fiber product is a non-polar non-metallic material with excellent performance. It is an important member of the modern material family and an indispensable supporting basic material for high-tech. It not only has excellent properties such as non-combustibility, high temperature resistance, electrical insulation, high tensile strength, and good chemical stability, but also can use organic coating treatment technology to carry out deep processing of products and expand the application field of products. Reinforced plastics with glass fiber has become one of the hottest industrial subjects today. Therefore, glass fiber products have been more and more widely used in traditional industrial sectors such as transportation, cons...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J167/06C09J11/06D04H1/58
Inventor 张毓强杨国明嵇安然任韦华
Owner JUSHI GRP CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com