Textile coating method with water urethane emulsion

A urethane, water-based technology, applied in the direction of fabric surface trimming, heating/cooling fabric, liquid/gas/vapor removal by air jet method, etc., which can solve the problems of water resistance, moisture permeability, washing resistance and hand feeling. Processing performance and other issues, to achieve the effect of excellent surface smoothness, cost saving and elasticity improvement

Inactive Publication Date: 2010-09-15
梁淇坪
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006]Therefore, the demand for water-dispersible polyurethane as a recognized environmentally friendly product is very urgent, but fabrics coated with water-based polyurethane have not yet solved the problems of water repellency, moisture permeability, washing resistance However, it has not been practically used in the field of fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1: preparation according to coating agent of the present invention and fabric (I)

[0048] Choose thinner fabrics from nylon and polyester, and perform pretreatment processes such as refining, dyeing, and water-repellent treatment.

[0049] A water-dispersible polyurethane resin mixture comprising the following composition was prepared: 30% by weight polyol polymer of aliphatic isocyanate, 0.5% triethylamine as chain extender, 2% N-methyldiethanolamine as ionomer material, and 67.5% water; prepare a thickener comprising the following composition: by weight 30% basic copolymer compound, 1.5% basic polyoxyethylene sodium sulfate, 0.07% potassium sulfate, and 68.43% Water; every 100 parts by weight of the water-dispersible polyurethane resin mixture was mixed with 4.5 parts by weight of the thickener and 50 parts by weight of water, and the above mixture was stirred to prepare a coating agent with a viscosity of 7,000 cps.

[0050] Apply 20-50g / yds of wet coati...

Embodiment 2

[0052] Embodiment 2: preparation according to the coating agent of the present invention and fabric (II)

[0053] Choose thicker fabrics from nylon and polyester, and first carry out pretreatment processes such as refining, dyeing, and water-repellent treatment.

[0054] A water-dispersible polyurethane resin mixture comprising the following composition was prepared: 30% by weight polyol polymer of aliphatic isocyanate, 0.5% triethylamine as chain extender, 2% N-methyldiethanolamine as ionomer material, and 67.5% water; prepare a thickener comprising the following composition: by weight 30% basic copolymer compound, 1.5% basic polyoxyethylene sodium sulfate, 0.07% potassium sulfate, and 68.43% 100 parts by weight of the water-dispersible polyurethane resin mixture was mixed with 3 parts by weight of the thickener and 50 parts by weight of water, and the mixture was stirred to prepare a coating agent with a viscosity of 6,000 cps.

[0055] Apply 20-50g / yds of wet coating agent...

Embodiment 3

[0057] Embodiment 3: preparation according to the coating agent of the present invention and fabric (III)

[0058] Select blended fabrics from nylon / cotton, polyester / cotton, polyester microfiber, etc., and perform pretreatment processes such as refining, dyeing, and water-repellent treatment.

[0059] A water-dispersible polyurethane resin mixture comprising the following composition was prepared: 30% by weight polyol polymer of aliphatic isocyanate, 0.5% triethylamine as chain extender, 2% N-methyldiethanolamine as ionomer material, and 67.5% water; prepare a thickener comprising the following composition: by weight 30% basic copolymer compound, 1.5% basic polyoxyethylene sodium sulfate, 0.07% potassium sulfate, and 68.43% Water; 5 parts by weight of the thickener and 80 parts by weight of water per 100 parts by weight of the water-dispersible polyurethane resin mixture were mixed, and the above mixture was stirred to prepare a coating agent with a viscosity of 5,000 cps.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Disclosed is a method of coating a textile with aqueous urethane textile having excellent water proofness and moisture permeability, wherein aqueous urethane coating agent prepared by employing a water dispersed polyurethane resin mixture and a thickener is applied to textile fabric, the coated fabric is heat dried, and then is hardened. Accordingly, the fiber product according to the present invention is very eco-friendly product, satisfies strict standard for an advance country since formalin is not detected, and in addition, has high functionality such as water proofness, moisture permeability and cleaning durability.

Description

technical field [0001] The present invention relates to a method of applying water-based polyurethane to coat fabrics to obtain fabrics with excellent water resistance and moisture permeability. More specifically, the present invention relates to a method of coating fabrics with water-based urethane to obtain fabrics having excellent water repellency, moisture permeability, and wash resistance, which is generally used for the use of water-dispersible polyurethanes containing environmentally friendly Mixture of coating agents for fabrics. Background technique [0002] Until 1980, the urethane industry in South Korea developed centered on the clothing, shoes, bags, toys, sofas, beds and other daily necessities material industries. Now urethane is widely used as a material in automobiles, electronics, Heavy chemical industries such as civil engineering and shipbuilding, as well as aerospace engineering and medicine. The application of polyurethane coating technology in the fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564
CPCD06N3/14D06B15/09D06C7/02D06M15/564D06N3/08D06M2200/12D10B2401/022D10B2401/021
Inventor 梁淇坪
Owner 梁淇坪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap