Preparation method of nanometer sliver colloid solution

A colloidal solution and nano-silver technology, which is applied in the field of preparation of nano-silver colloidal solution, can solve the problems of complex steps and difficult particle size control, and achieve the effects of high antibacterial efficiency, small particle size of nano-silver, and less dosage.

Active Publication Date: 2011-11-09
ZHANGJIAGANG NELLNANO TECH
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in the preparation process of nano-silver colloidal solution, there are still problems of complicated steps and difficult control of particle size, and it is still a difficult problem to ensure the stability of nano-silver dispersion system and prevent the agglomeration of nano-silver. The use of dispersants and dispersants inevitably brings problems to the application safety of nano-silver colloidal solutions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Dissolve 0.1g of 2-O-nonyl-β-cyclodextrin in 100ml of deionized water to obtain a 0.1% aqueous solution of 2-O-nonyl-β-cyclodextrin;

[0017] 2. Prepare 1.0mol / L silver nitrate solution, add 5 drops of 0.1mol / L sodium hydroxide solution dropwise, then add dropwise 5% ammonia solution until the precipitation disappears, and obtain silver ammonia with a molar concentration of 0.1mol / L solution;

[0018] 3. Mix 0.1% 2-O-nonyl-β-cyclodextrin aqueous solution and silver ammonia solution with a molar concentration of 0.1mol / L at a volume ratio of 1:50, stir at 80°C for 40min, and obtain the particle size It is a nano-silver colloid solution of 5-20nm.

Embodiment 2

[0020] 1. Dissolve 0.1g of 2-O-dodecyl-α-cyclodextrin in 100ml of deionized water to obtain a 0.1% aqueous solution of 2-O-dodecyl-α-cyclodextrin;

[0021] 2. Prepare 1.0mol / L silver nitrate solution, add 5 drops of 0.1mol / L sodium hydroxide solution dropwise, then add 5% diethylenetriamine aqueous solution dropwise until the precipitate disappears, and the molar concentration is 0.1mol / L silver ammonia solution;

[0022] 3. Mix 0.1% 2-O-dodecyl-α-cyclodextrin aqueous solution and silver ammonia solution with a molar concentration of 0.1mol / L at a volume ratio of 1:50, and stir at 100°C for 10 minutes to obtain Nano silver colloid solution with a particle size of 5-20nm.

Embodiment 3

[0024] 1. Dissolve 0.1g of 2,6-di-O-octyl-γ-cyclodextrin in 100ml of deionized water to obtain 0.1% 2,6-di-O-octyl-γ-cyclodextrin aqueous solution;

[0025] 2. Prepare 1.0mol / L silver nitrate solution, add 5 drops of 0.1mol / L sodium hydroxide solution dropwise, then add 5% tetraethylenepentamine aqueous solution dropwise until the precipitate disappears, and the molar concentration is 0.1mol / L silver ammonia solution;

[0026] 3. Mix 0.1% 2,6-di-O-octyl-γ-cyclodextrin and silver ammonia solution with a molar concentration of 0.1 mol / L at a volume ratio of 1:50, and stir at 100°C for 20 minutes, A nano-silver colloid solution with a particle diameter of 5-20 nm is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a safe, environment-friendly and stable preparation method of a nanometer sliver colloid solution, comprising the following steps: mixing the alkylated cyclodextrin aqueous solution and the silver ammonia solution according to the volume ratio of 1:100-1:10, wherein the mass percent of the alkylated cyclodextrin aqueous solution is 0.1-10%, and the mass molar concentration of the silver ammonia solution is 0.01-1.0mol / L; and stirring for 1-120min at 10-100 DEG C to obtain the nanometer sliver colloid solution of which the average grain diameter is 1-100nm. The method of the invention has the advantages of simple preparation process and can ensure the application safety of the nanometer sliver colloid solution, and the prepared nanometer sliver colloid solution has the characteristics of good stability, small grain diameter of nanometer sliver, less dosage and high antibiosis efficiency in the function materials of the nanometer sliver.

Description

technical field [0001] The invention belongs to the field of nanometer materials, in particular to a preparation method of nanometer silver colloidal solution. Background technique [0002] Nano-silver is a simple substance of metallic silver with a particle size of nanometer scale. It is reported that nano-silver has broad application prospects in the fields of antibacterial materials, high-efficiency catalysts, lubricants, light-absorbing materials, coatings, sensors, conductive pastes, high-performance electrode materials, etc., and has become a functional material with special properties. Theoretical research and application important issues for development. For example, adding a small amount of nano-silver to chemical fiber can improve some properties of chemical fiber products and make it have a strong bactericidal ability; doping an appropriate amount of nano-silver in the silicon oxide film can make the glass coated with this film effective. Certain photoluminescen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24
Inventor 张峰姚理荣
Owner ZHANGJIAGANG NELLNANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products