Manufacturing process of simulation stone chip

A production process and technology of stone flakes, which are used in manufacturing tools, supply devices, ceramic molding machines, etc., can solve the problems of inability to meet the special performance requirements of modeling, poor construction technology, and small plasticity, and achieve simple and fast construction methods. Good, malleable effect

Inactive Publication Date: 2012-01-25
冷贝生
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this production process are: 1. The material itself is heavy and low in strength; 2. It needs to use real stone, which causes great pollution, wastes resources and high cost; 3. The construction process is poor and the plasticity is small, which cannot meet the special shape. performance requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A manufacturing process of artificial stone flakes. The manufacturing process includes the following steps:

[0018] 1) Use silica gel to develop a simulated stone chip module that meets the requirements; you can use silica gel to develop a module on real stones that exist in nature.

[0019] 2) Fill the artificial stone flake module with unsaturated polyester resin and calcine powder, and use glass fiber as the skeleton, plus curing agent and accelerator to obtain the required artificial stone flakes. Among them, unsaturated polyester resin and calcine The mass ratio of powder, curing agent and accelerator is 100 parts: 200 parts: 3 parts: 4 parts. The unsaturated polyester resin adopts 885 resin produced by Changzhou Tianma Ruisheng Composite Material Co., Ltd. The curing agent and the accelerator are all products produced by Changzhou Jinlong Chemical Group, wherein the curing agent is H type and the accelerator is colorless A type.

Embodiment 2

[0021] Yet another artificial stone chip manufacturing process, the manufacturing process includes the following steps:

[0022] 1) Use silica gel to develop a simulated stone chip module that meets the requirements; you can use silica gel to develop a module on real stones that exist in nature.

[0023] 2) Fill the artificial stone flake module with unsaturated polyester resin and calcine powder, and use glass fiber as the skeleton, plus curing agent and accelerator to obtain the required artificial stone flakes. Among them, unsaturated polyester resin and calcine The mass ratio of powder, curing agent and accelerator is 100 parts: 300 parts: 4 parts: 3 parts. The unsaturated polyester resin adopts 885 resin produced by Changzhou Tianma Ruisheng Composite Material Co., Ltd. The curing agent and accelerator are all products produced by Changzhou Jinlong Chemical Group, wherein the curing agent is H type and the accelerator is colorless A type.

Embodiment 3

[0025] Yet another artificial stone chip manufacturing process, the manufacturing process includes the following steps:

[0026] 1) Use silica gel to develop a simulated stone chip module that meets the requirements; you can use silica gel to develop a module on real stones that exist in nature.

[0027] 2) Fill the artificial stone flake module with unsaturated polyester resin and calcine powder, and use glass fiber as the skeleton, plus curing agent and accelerator to obtain the required artificial stone flakes. Among them, unsaturated polyester resin and calcine The mass ratio of powder, curing agent and accelerator is 100 parts: 400 parts: 5 parts: 5 parts. The unsaturated polyester resin adopts 885 resin produced by Changzhou Tianma Ruisheng Composite Material Co., Ltd. The curing agent and the accelerator are all products produced by Changzhou Jinlong Chemical Group, wherein the curing agent is H type and the accelerator is colorless A type.

[0028] Research shows that the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing process of a simulation stone chip, which comprises the following steps: adopting silica gel to issue a simulation stone chip module which meets relevant requirements; and filling unsaturated polyester resin and limestone powder into the simulation stone chip module, taking glass fibers as a skeleton, adding curing agent and accelerator to obtain the required simulation stone chip, wherein the mass ratio of the unsaturated polyester resin to the limestone powder to the curing agent to the accelerator is 100 parts: 200 to 400 parts: 3 to 5 parts: 3 to 5 parts. The simulation stone chip has the advantages of high strength and light weight, can meet the special performance requirements on the shape, and the manufacturing process of the simulation stonechip is widely applied to the manufacturing of rockery.

Description

Technical field [0001] The invention relates to a process for making rockery landscapes, in particular to a process for making artificial stone chips. Background technique [0002] Rockery is an excellent traditional art in Chinese gardens, with a history of more than two thousand years. The selection of materials in its production process is very important. The production of large rocks, whether it is hard or soft, and whether it is water-absorbing or non-absorbing, requires a unified stone and a unified specification (block or strip). In the current rockery landscape production process, real stone flakes in nature are used for processing, and granite rubble or sandstone rubble is generally used. The disadvantages of this manufacturing process are: 1. The material itself is heavy in quality and low in strength; 2. It needs to use real stone, which causes great pollution, wastes resources and high cost; 3. The construction process is poor, and the plasticity is small, which cann...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28B1/52B28B13/02C04B26/18
Inventor 冷贝生
Owner 冷贝生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More