Glass product and production method thereof

A glass product and glass technology, applied in the field of glass products, can solve the problems of easy warping of the plastic layer and large dimensional tolerance, and achieve the effect of preventing warping

Inactive Publication Date: 2013-05-29
佛山市高明新永业玻璃制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the defects that the plastic layer of the laminated glass and plastic parts produced in the prior art is easy to warp and the size tolerance is large, the present invention provides a glass product whose plastic layer is not easy to warp and has accurate product dimensions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment is used to illustrate the glass product provided by the present invention and the production method of the glass product.

[0029] (1) Glass processing

[0030] The glass sheet was cut into 10 cm×5 cm×3 mm glass plates using an automatic glass cutting machine (BX400, Ruite Optical Instrument Factory); the thickness of the glass was determined to be 2.5 mm by rough grinding and polishing. A step structure is formed at the edge of the glass by carving, the width of the step structure is 3 mm, the step structure has 3 steps of equal height, the total depth is 1.5 mm, and the edge of the glass has a width of 5 mm Ring area.

[0031] (2) Cleaning and applying adhesive

[0032] Gently wipe the surface of the glass plate and the step structure formed at the edge of the glass with alcohol to ensure that there is no debris. Then, 0.1 g of hot melt adhesive (product model P26-5, Guangzhou Lushan Chemical Material Co., Ltd.) was applied on the side of the step structure ...

Embodiment 2

[0037] This embodiment is used to illustrate the glass product provided by the present invention and the production method of the glass product.

[0038] (1) Glass processing

[0039] The glass sheet was cut into 10 cm×5 cm×3 mm glass plates using an automatic glass cutting machine (BX400, Ruite Optical Instrument Factory); the thickness of the glass was determined to be 2.5 mm by rough grinding and polishing. A step structure is formed at the edge of the glass by carving, the width of the step structure is 4 mm, the step structure has 2 steps of equal height, the total depth is 1 mm, and the edge of the glass has a width of 5 mm Ring area.

[0040] (2) Cleaning and applying adhesive

[0041] Gently wipe the surface of the glass plate and the step structure formed at the edge of the glass with alcohol to ensure that there is no debris. Then, 0.12 grams of hot melt adhesive (product model P26-5, Guangzhou Lushan Chemical Material Co., Ltd.) was applied on the side of the step structu...

Embodiment 3

[0046] This embodiment is used to illustrate the glass product provided by the present invention and the production method of the glass product.

[0047] (1) Glass processing

[0048] The glass sheet was cut into 10 cm×5 cm×3 mm glass plates using an automatic glass cutting machine (BX400, Ruite Optical Instrument Factory); the thickness of the glass was determined to be 2.5 mm by rough grinding and polishing. A circular through hole structure is formed at the edge of the glass by carving, the shortest distance between the edge of the through hole and the glass extension is 1.5 mm, the diameter of the through hole is 2 mm, and the distance between two adjacent through holes It is 5 mm, and the edge of the glass is an annular area with a width of 5 mm.

[0049] (2) Cleaning and applying adhesive

[0050] Gently wipe the surface of the glass plate and the through-hole structure formed at the edge of the glass with alcohol to ensure that there is no debris. Then, 0.2 grams of quick-dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A glass article is provided. The glass article may comprise: a glass body with convex-concave and / or via hole structures formed on at least a part of periphery of the glass body; a plastic layer adhered to the periphery of the glass body with adhesive coated therebetween. The plastic layer may be adhered to the glass body via the convex-concave and / or via hole structures. A method of forming the glass article as described above is also provided.

Description

Technical field [0001] The invention relates to a glass product and a production method of the glass product. Background technique [0002] The glass has good permeability, no pollution, strong fashion, rich shapes, wide applications and low cost. The glass mold has precise molding dimensions, which can produce thin and light products, with rich colors and exquisite craftsmanship. The simple classification of glass is mainly divided into flat glass and special glass. Among them, there are many varieties of special glass, with their own different properties, and a wide range of uses. Glass is usually mainly used in construction, daily use, medical treatment, chemistry, electronics, instrumentation, nuclear engineering and other fields. [0003] Glass itself has the characteristics of poor impact resistance, fragility, and difficulty in combining with other materials, which limits its application in some fields. In order to overcome the disadvantages of poor impact resistance and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)