Novel material spectacle frame processing and forming method

A new type of material, processing and forming technology, applied in the field of material processing, can solve the problems of large equipment investment, easy shrinkage, high cost, etc., and achieve the effect of low production cost, not easy to fade, and good dimensional stability

Inactive Publication Date: 2011-02-02
方国彪
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Considering factors such as price and performance, currently domestic mirror frames are mainly acetic acid sheet frames, but the disadvantage of this material is that it is easily corroded by ketone, vinegar, alkyl liquids, high-concentration acids and alkalis, and it is easy to shrink and deform.
Although the performance of epoxy resin material is extremely good, the one-time molding and polishing process of this material requires a lot of investment in equipment, so the cost is high, and it is only used by some imported high-end famous brand frames.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Step 1: Heat 100 parts by weight of bisphenol A epoxy resin to 50°C and stir at 80 rpm for 0.5 hours, then mix 10 parts by weight of diluent BGE, and stir evenly to obtain group A Take 50 parts by weight of the curing agent polyetheramine 403 and 15 parts by weight of the softener polyetheramine D-400, mix and stir to obtain the B component;

[0035] Step 2: Prepare a mold for the spectacle frame, usually a silicone mold, including spectacle legs, spectacle frames (or spectacle rings) and spectacle accessories. Put these molds in a 70°C oven to preheat for 0.5 hours;

[0036] Step 3: Mix the AB components configured in Step 1 in a weight ratio of 2 to 1, and stir in a mixer at 600 revolutions per minute for 5 minutes to obtain epoxy resin glue;

[0037] Step 4: Put the mixed epoxy resin glue in a vacuum box for deaeration;

[0038] Step 5: Pour the fully degassed epoxy resin glue into the mold that has been preheated in the oven and taken out. At this time, the temperature of ...

Embodiment 2

[0045] Step 1: Heat 100 parts by weight of bisphenol A epoxy resin to 60°C and stir for 0.5 hours at a speed of 80 revolutions per minute, then mix 10 parts by weight of diluent BGE and stir evenly to obtain component A , Take 50 parts by weight of the curing agent polyetheramine 403 and 15 parts by weight of the softener polyetheramine D-400, mix and stir to obtain component B;

[0046] Step 2: Prepare spectacle frame molds, generally silicone molds, including spectacle legs, spectacle frames and spectacle accessories. Put these molds in a 70°C oven to preheat for 1 hour;

[0047] Step 3: Mix the AB components configured in step 1 in a weight ratio of 2 to 1, and add 5% of the red pigment by weight of the epoxy resin, and then stir in the mixer at 700 revolutions per minute for 4 minutes to obtain Epoxy glue;

[0048] Step 4: Put the mixed epoxy resin glue in a vacuum box for deaeration;

[0049] Step 5: Pour the fully degassed epoxy resin glue into the mold that has been preheated...

Embodiment 3

[0056] Step 1: Heat 100 parts by weight of bisphenol A epoxy resin to 70°C and stir at 80 rpm for 1 hour, then mix 10 parts by weight of diluent BGE and stir evenly to obtain component A , Take 50 parts by weight of the curing agent polyetheramine 403 and 15 parts by weight of the softener polyetheramine D-400, mix and stir to obtain component B;

[0057] Step 2: Prepare spectacle frame molds, generally silicone molds, including spectacle legs, spectacle frames and spectacle accessories. Put these molds in a 70°C oven to preheat for 1 hour;

[0058] Step 3: Mix the AB components configured in step 1 in a weight ratio of 2 to 1, and add 5% of the blue pigment by weight of the epoxy resin, and then stir for 3 minutes at 900 revolutions per minute in the mixer. Get epoxy glue;

[0059] Step 4: Put the mixed epoxy resin glue in a vacuum box for deaeration;

[0060] Step 5: Pour the completely degassed epoxy resin glue into the mold that has been preheated in the oven and taken out. At t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
kinematic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides novel material epoxy resin spectacle arm wires, a novel material epoxy resin spectacle frame and a processing and forming method thereof. The material of the spectacle arm wires and the spectacle frame is prepared from an epoxy resin raw material, a diluents, a curing agent and a softener; the processing and forming technique of the spectacle arm wires and the spectacle frame comprises: preparing raw materials, preheating a mold, preparing glue, defoaming, filling mold, curing, cooling, demolding, polishing and assembling. The spectacle arm wires and the spectacle frame processed and formed by the method have the advantages that: the wear is comfort; the appearance is beautiful; the spectacle frame is firm and durable; and the like. The production cost is low and is acceptable for common consumers.

Description

Technical field [0001] The invention relates to the field of material processing, in particular to a method for processing an epoxy resin material into eyeglass legs and eyeglass frames. Background technique [0002] With the continuous improvement of living standards, glasses can not only correct eyesight for people, but also become a kind of decoration. While pursuing comfort, the requirements for the appearance of products are also getting higher and higher. Frame materials currently on the market generally include metallic materials and non-metallic materials. Frames made of ordinary metal materials are relatively heavy, and long-term wear will compress the bridge of the nose and cause discomfort; and metal frames generally require electroplating, and the electroplating layer is likely to cause skin allergies. High-grade metal frames, such as titanium frames, are expensive, although they are made of fine materials. [0003] Non-metal frame materials include natural materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C39/44B29D12/02B29K63/00
CPCB29D12/02
Inventor 方国彪
Owner 方国彪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com