A production method and the technology of attapulgite, applied in the field of clay, can solve the problems of being unsuitable for handicrafts, unfavorable for making and molding, unfavorable for promotion and use, etc., and achieve the effect of being conducive to popularization and use, bright in color and non-irritating to the skin

Inactive Publication Date: 2011-02-16
南通江涌投资开发有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantage of the above-mentioned patents is that the main raw materials of the soft clay produced by this technology are polyvinyl chloride paste resin, dizinc grease and calcium carbonate, and the adhesion is not good under normal temperature, which is not conducive to making molding. Dizinc grease belongs to poisonous substance
[0006] The disadvantage of the above-mentioned patent is that the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Below in conjunction with embodiment the present invention will be further described:

[0032] 1. The production method of the white attapulgite soft clay is: ①add the white sandy attapulgite mixture into the running horizontal dough mixer, and slowly add the sodium polyacrylate gel solution into the white sandy attapulgite mixture, Stir to form a white mud-like attapulgite mixture; ② Add the white mud-like attapulgite mixture to the kneading machine, spray methyl silicone oil on the white mud-like attapulgite mixture, and knead it into a white attapulgite soft clay ③Put the semi-finished white attapulgite soft clay into the noodle press and press it repeatedly for 3 times, and finally press it into a flat white attapulgite soft clay, which is sealed and packaged as a finished product;

[0033] 2. The ingredients of the white attapulgite soft clay are composed of the following components by weight percentage: 82% of white sandy attapulgite mixture, 16% of sodium polyacr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing white attapulgite soft clay. Key points of the technical scheme comprise the following steps of: adding a white sand-grain attapulgite mixture into an operating horizontal flour mixing machine, slowly adding solution of sodium polyacrylate gel into the white sand-grain attapulgite mixture and stirring so as to obtain a white clod-shaped attapulgite mixture; and spraying methyl silicone oil onto the white clod-shaped attapulgite mixture, kneading the white clod-shaped attapulgite mixture into semi-finished white attapulgite soft clay, pressing the semi-finished white attapulgite soft clay into flat-plate white attapulgite soft clay, sealing and packaging so as to obtain a finished product. The white attapulgite soft clay has high viscosity, softness and plasticity and small contractibility rate, becomes hard after natural drying, does not need baking, does not crack and has no corrosion and greasy handfeel. After different colors are added into the white attapulgite soft clay, a plurality of colored soft clay can be produced and handicraft articles with clear patterns, bright colors and vivid effects can be made by using attapulgite soft clay with different colors. The white attapulgite soft clay is suitable for molding patterns, molds and handicraft articles.

Description

technical field [0001] The invention relates to clay, in particular to a production method of white attapulgite soft clay. Background technique [0002] The main raw materials of soft clay are polyvinyl chloride and calcium carbonate. The adhesion is not good at room temperature, and it is easy to age and fade after long-term storage. It is easy to foam when baking soft clay. If the temperature exceeds 200 ° C, it will not only make The finished product is scorched and melted, and may even cause combustion, generating irritating and toxic fumes containing chlorine. The sales price of soft clay is relatively high, which is not conducive to popularization and use. [0003] The Chinese patent publication number is: CN 101186736, open date: May 28, 2008, titled "a kind of soft clay and its preparation method", discloses: "a kind of soft clay and its preparation method, which consists of the following weight It is prepared from 15 parts: polyvinyl chloride paste resin 15-40, diz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00B28B1/00B28B3/00
Inventor 许庆华许盛英袁长兵汪成军
Owner 南通江涌投资开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap