A composition and adhesive technology, applied in the direction of adhesive types, graft polymer adhesives, hydrocarbon copolymer adhesives, etc., can solve problems such as cracking and affecting the service life of products
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0091] After granulating formula 3 and formula 2 respectively, use GEC 3-layer co-extrusion blown film line to co-extrude blown film. The temperature in the processing zone is set at 130-200°C, and the line speed is 12m / min. The formed bi-layer co-extrusion film has a total thickness of 100 μ, and the structure is: 50 μ adhesive film formed from formulation 3-50 μ adhesive film formed from formulation 2.
[0092] Use this double-layer film subsequently as adhesive layer, carry out composite with the stainless steel plate of 0.3mm thick and the aluminum plate of 0.18mm thick with the following method, wherein formula 3 adhesive film one side is bonded with stainless steel plate, formula 2 adhesive film Bonding to aluminum on one side: Preheat the stainless steel plate / double adhesive film / aluminum plate laminate in an oven at 70°C for 5 minutes. Then hot press for 40 seconds under the hot press, the condition is 150 ℃, 3.5kg / cm 2 . Keep it in an oven at 70° C. for 1 minute, t...
Embodiment 2
[0098] After formula 4 was granulated, it was hot-pressed for 10 minutes at 170° C. under a pressure of 3.1 kg / cm to form a thick film of about 180 μ.
[0099] After formulation 2 was pelletized, the film was blown using a GEC 3-layer coextrusion blown film line. The temperature in the processing area is set at 130-200°C, and the line speed is 12m / min. A monolayer film with a thickness of 50 µ was produced.
[0100] The above-mentioned 2 kinds of films are superimposed subsequently to form a composite adhesive layer, and the composite adhesive layer is compounded with the thick stainless steel plate of 0.3mm and the thick aluminum plate of 0.18mm with the following method, wherein one side of the formula 4 adhesive layer is bonded with Bonding of stainless steel plate, one side of the adhesive layer of formula 2 is bonded to aluminum: Preheat the laminate of stainless steel plate / composite adhesive film / aluminum plate in an oven at 70°C for 5 minutes. Then hot press for 40 s...
Embodiment 3
[0106] After formula 5 was granulated, it was hot-pressed for 10 minutes at 170° C. under a pressure of 3.1 kg / cm to form a thick film of about 180 μ.
[0107] After formulation 1 was pelletized, the film was blown using a GEC 3-layer coextrusion blown film line. The temperature in the processing area is set at 130-200°C, and the line speed is 12m / min. A monolayer film with a thickness of 50 µ was produced.
[0108] The above-mentioned 2 kinds of films are superimposed subsequently as composite adhesive layer, and this composite adhesive layer is compounded with the thick stainless steel plate of 0.3mm and the thick aluminum plate of 0.18mm with the following method, wherein formula 5 adhesive layer one side and Bonding of stainless steel plate, one side of the adhesive layer of formula 1 is bonded to aluminum: Preheat the laminate of stainless steel plate / composite adhesive film / aluminum plate in an oven at 70°C for 5 minutes. Then hot press for 40 seconds under the hot pre...
PUM
Property | Measurement | Unit |
---|---|---|
melt flow index | aaaaa | aaaaa |
melt flow index | aaaaa | aaaaa |
adhesion strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap