Composite polyester fiber non-woven fabric for ultra-filtration membrane supporting layer and production method thereof
A polyester fiber and a manufacturing method technology are applied to the polyester fiber composite non-woven fabric and its manufacturing field, which can solve the problems of large pore size distribution, film leakage, poor surface smoothness and thickness uniformity, etc., and achieve uniformity. good effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0023] A kind of polyester fiber composite non-woven fabric for ultrafiltration membrane support layer, it comprises the ultrafiltration of 0.80-1dtex*38-52mm (that is 0.8 to 1 decitex, fiber length 38 to 52 millimeters) proportioning by weight 80-90 parts of fine denier polyester fibers and 10-20 parts of thermally bonded polyester fibers of 5-5.5dtex*38-52mm (that is, 5 to 5.5 dtex, fiber length 38 to 52 mm); its quantitative value is 80± 10g / m 2 , the thickness is 0.10±0.010mm, the apparent density is 0.85±0.10g / cm 3 , Quantitative unevenness CV ≤ 4%, longitudinal tension ≥ 300N / 50mm width, transverse tension ≥ 55N / 50mm width. Quantitative: Refers to the mass per unit area.
[0024] A kind of above-mentioned manufacture method of the polyester fiber composite non-woven fabric that is used for ultrafiltration membrane support layer, it comprises the steps:
[0025] 1. Selection of raw materials: Use 0.80-1dtex*38-52mm ultra-fine polyester fiber and 5-5.5dtex*38-52mm therm...
Embodiment 2
[0032] A kind of manufacture method of the polyester fiber composite non-woven fabric that is used for ultrafiltration membrane support layer, it comprises the steps:
[0033] 1. Selection of raw materials: Select 0.80-1dtex*38-52mm ultra-fine polyester fiber and 5-5.5dtex*38-52mm thermally bonded polyester fiber, proportion by weight, ultra-fine polyester fiber 80 -90 parts, heat-bonded polyester fiber 10-20 parts.
[0034] 2. Make polyester fiber non-woven fabric: make polyester fiber non-woven fabric by blending, opening, carding, hot-rolling, and winding the above-mentioned raw materials; After that, it is mechanically carded into a web, hot-rolled and bonded, and rolled to produce a weight of 20±3g / m 2 , The thickness is 0.035±0.005mm polyester fiber non-woven fabric.
[0035] 3. Hot rolling composite: take two volumes of the polyester fiber non-woven fabric obtained in the second step above, and roll it at a temperature of 225±2°C, a pressure of 4-4.5MPa, and a speed of ...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap