Spinning finish for degradable stent fiber for human bodies

A technology of spinning oil and human body, which is applied in fiber processing, textiles and papermaking, etc., can solve the problems of limiting the application of ordinary spinning oil, not paying attention to the biocompatibility of oil, safety and non-toxicity, etc., and achieves excellent clustering properties, good biocompatibility, and improved stability

Inactive Publication Date: 2011-07-20
DONGHUA UNIV +1
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, most of the spinning oils currently on the market only focus on endowing fibers with softness, smoothness and cohesion, but do not pay attention to the biocompatibility, safety and non-toxicity of the oils, which limits the use of ordinary spinning oils. Application of agent in biodegradable medical fiber materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of spinning finish for human body degradable support fiber, its formula and preparation method are as follows:

[0026] 1. Formula:

[0027] Component A lubricating coagulation agent: corn oil, content is 12 parts;

[0028] Component B emulsifier: sucrose fatty acid ester, the content is 55 parts;

[0029] Component C penetrating agent: polyoxyethylene sorbitan monolaurate, the content is 19 parts;

[0030] Component D antistatic agent: polyethylene glycol content is 8 parts, molecular weight is 200;

[0031] Component E antibacterial agent: chitosan, the content is 6 parts, the degree of N-deacetylation is 85%, and the molecular weight is 100,000.

[0032] The lipophilic and hydrophilic value of the oil agent is 8.

[0033] 2. Preparation method

[0034] Get 12 parts of corn oil, 55 parts of sucrose fatty acid ester, 19 parts of polyoxyethylene sorbitan monolaurate, 8 parts of polyethylene glycol-200, and 6 parts of chitosan. First, heat the corn oil to 50...

Embodiment 2

[0036] A kind of spinning finish for human body degradable support fiber, its formula and preparation method are as follows:

[0037] 1. Formula

[0038] Component A lubricating and coagulating agent: corn oil, the content is 24 parts;

[0039] Component B emulsifier: sucrose fatty acid ester, content is 36 parts;

[0040] Component C penetrating agent: sorbitan polyoxyethylene ether monolaurate, the content is 27 parts;

[0041] Component D antistatic agent: the content of polyethylene glycol is 7 parts, and the molecular weight is 400;

[0042] Component E antibacterial agent: chitosan, the content is 6 parts, the degree of N-deacetylation is 90%, and the molecular weight is 120,000.

[0043] The lipophilic and hydrophilic value of the oil agent is 9.

[0044] 2. Preparation method

[0045] Get 24 parts of corn oil, 36 parts of sucrose fatty acid ester, 27 parts of polyoxyethylene sorbitan monolaurate, 7 parts of polyethylene glycol-200, 6 parts of chitosan. First, hea...

Embodiment 3

[0047] A kind of spinning finish for human body degradable support fiber, its formula and preparation method are as follows:

[0048] 1. Formula

[0049] Component A lubricating and coagulating agent: corn oil, the content is 24 parts;

[0050] Component B emulsifier: sucrose fatty acid ester, the content is 55 parts;

[0051] Component C penetrating agent: polyoxyethylene sorbitan monolaurate, the content is 13 parts;

[0052] Component D antistatic agent: polyethylene glycol content is 5 parts, molecular weight is 600;

[0053] Component E antibacterial agent: chitosan, the content is 3 parts, the degree of N-deacetylation is 95%, and the molecular weight is 150,000.

[0054] The lipophilic and hydrophilic value of the oil agent is 12.

[0055] 2. Preparation method

[0056] Get 24 parts of corn oil, 55 parts of sucrose fatty acid ester, 13 parts of polyoxyethylene sorbitan monolaurate, 5 parts of polyethylene glycol-200, and 3 parts of chitosan. First, heat the corn oil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a spinning finish for a degradable stent fiber for human bodies. The active ingredient of the spinning finish comprises the following components: 12-24 parts of lubricating cohesive agent (corn oil), 36-55 parts of emulsifier (sucrose fatty acid ester), 13-27 parts of penetrant (polyoxyethylene sorbitan monolaurate), 5-8 parts of antistatic agent (polyethylene glycol) and 3-6 parts of antimicrobial agent (chitosan). The spinning finish for a degradable stent fiber for human bodies has favorable antimicrobial effect, avoids the phenomena of molding and deterioration in the storage and use process, has the advantages of obviously enhanced stability, high safety and no toxicity, is degradable, and has favorable biocompatibility with tissues of human bodies.

Description

technical field [0001] The invention relates to an oil agent used in the spinning process of synthetic fibers, in particular to a spinning oil agent for degradable scaffold fibers used in the human body, which is a degradable oil agent used in the human body with good biocompatibility. Spinning finish for scaffold fibers. Background technique [0002] Synthetic fibers do not have the natural colloid and oil film that natural fibers have. They have poor hygroscopicity and are non-conductive. Therefore, static electricity is generated due to constant friction during the spinning process. Auxiliaries must be used to prevent or eliminate static electricity accumulation. The fiber is soft and smooth, so that it can pass through the subsequent process smoothly. This kind of additive is collectively called fiber spinning oil. Fiber spinning oil should have the following characteristics: smooth, antistatic, clustering or cohesion, etc.; good thermal stability, low volatility; no co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/224D06M15/53D06M13/17D06M15/03
Inventor 李文刚王大新张秀芳陈大钟宋月华张军桂冠群罗卫张幼维赵炯心陈南梁
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com