A spray-on plastic release agent

A mold release agent and plastic technology, applied in the field of spray-on plastic mold release agent, can solve the problems that affect the product appearance, mold service life, cracks and wrinkles, environmental pollution, etc., and achieve the improvement of product color, convenient demoulding, and convenient use Effect

Active Publication Date: 2022-02-22
上海济雨实业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Poor quality release agent will cause cracks and wrinkles on the surface of the product, affect the appearance of the product and the service life of the mold, and cause environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A spray-on plastic release agent
  • A spray-on plastic release agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A spray-on plastic mold release agent is composed of A solution, B solution, C solution and D solution, wherein the volume ratio of A, B, C and D is 15:1.6:0.5:0.8.

[0014] Wherein, the A solution is prepared by the following method: 100ml of ethyl acetate, 15ml of eucalyptus oil and 3ml of glycerol carbonate are mixed.

[0015] The B solution was prepared by the following method: 100 mL of ethyl acetate and 15 mL of eucalyptus oil were mixed.

[0016] The C solution was prepared by the following method: dissolve 10 mL of simethicone in 100 mL of ethyl acetate and mix well.

[0017] The D solution was prepared by the following method: a mixed surfactant solution prepared by dissolving 10 g of sodium stearate and 10 g of Tween-80 in 100 mL of water.

[0018] Mix the above-mentioned A solution, B solution, C solution and D solution according to the volume ratio. The appearance of the product of the present invention is a clear solution.

Embodiment 2

[0020] A spray-on plastic mold release agent is composed of A solution, B solution, C solution and D solution, wherein the volume ratio of A, B, C and D is 25:1.6:0.5:0.9.

[0021] Wherein, the A solution is prepared by the following method: 100ml of ethyl acetate, 15ml of eucalyptus oil and 3ml of glycerol carbonate are mixed.

[0022] The B solution was prepared by the following method: 100 mL of ethyl acetate and 15 mL of eucalyptus oil were mixed.

[0023] The C solution was prepared by the following method: dissolve 10 mL of simethicone in 100 mL of ethyl acetate and mix well.

[0024] The D solution was prepared by the following method: a mixed surfactant solution prepared by dissolving 10 g of sodium stearate and 10 g of Tween-80 in 100 mL of water.

[0025] Mix the above-mentioned A solution, B solution, C solution and D solution according to the volume ratio. The appearance of the product of the present invention is a clear solution.

Embodiment 3

[0027] A spray-on plastic mold release agent is composed of A solution, B solution, C solution and D solution, wherein the volume ratio of A, B, C and D is 35:1.6:0.5:1.

[0028] Wherein, the A solution is prepared by the following method: 100ml of ethyl acetate, 15ml of eucalyptus oil and 3ml of glycerol carbonate are mixed.

[0029] The B solution was prepared by the following method: 100 mL of ethyl acetate and 15 mL of eucalyptus oil were mixed.

[0030] The C solution was prepared by the following method: dissolve 10 mL of simethicone in 100 mL of ethyl acetate and mix well.

[0031] The D solution was prepared by the following method: a mixed surfactant solution prepared by dissolving 10 g of sodium stearate and 10 g of Tween-80 in 100 mL of water.

[0032] Mix the above-mentioned A solution, B solution, C solution and D solution according to the volume ratio. The appearance of the product of the present invention is a clear solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A spray-on plastic release agent, which is composed of A solution, B solution, C solution and D solution according to the volume ratio of 15~35:1.6:0.5:0.8~1; the A solution is prepared by the following method Preparation: get 100ml ethyl acetate, 15ml eucalyptus oil and 3ml glycerol carbonate and mix it; the B solution is made by mixing 100mL ethyl acetate and 15mL eucalyptus oil; the C solution is 10mL simethicone Prepared by dissolving in 100mL ethyl acetate; the D solution is a mixed surfactant solution prepared by dissolving 10g sodium stearate and 10g Tween-80 in 100mL water. The mold release agent is used for mold release of plastic products and has good smoothness, isolation and mold release, high and low temperature resistance, chemical stability, no corrosion, non-toxic environmental protection, easy operation, and good use effect.

Description

technical field [0001] The invention relates to a spray-coated plastic release agent, which belongs to the technical field of chemical products. Background technique [0002] A release agent is an interface coating used on two surfaces that tend to stick to each other to make the surface easy to release, smooth and clean. Mold release agents are used in a wide variety of molding operations including metal die casting, polyurethane foams and elastomers, glass fiber reinforced plastics, injection molded thermoplastics, vacuum foamed sheets and extruded profiles. In molding, sometimes other plastic fillers such as plasticizers will seep into the interface, and a surface remover is needed to remove it. Mold release agents are chemically resistant and do not dissolve when in contact with the chemical composition of different resins (especially styrene and amines). The release agent also has heat and stress resistance, and is not easy to decompose or wear; the release agent adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C33/62
CPCB29C33/62
Inventor 宋兴良
Owner 上海济雨实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap