Optical laminated body and manufacturing method thereof
A technology of optical laminates and adhesive layers, applied in chemical instruments and methods, optics, nonlinear optics, etc., can solve problems such as peeling of polarizing plates, cracking of polarizing films, and inability to reuse liquid crystal cells, etc., to achieve adhesion Good, thickness-reducing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0144] (a) Preparation of polyvinyl alcohol-based adhesive composition
[0145] Acetoacetyl-modified polyvinyl alcohol with a saponification degree of 99.1 mol% (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., trade name "Gohsefimer Z-200", the viscosity of a 4% aqueous solution is 12.4 mPa·sec) was dissolved in pure In water, make a concentration of 10% aqueous solution. In this aqueous solution of acetoacetyl-modified polyvinyl alcohol, mix glyoxal as a crosslinking agent and 3-glycidoxypropyltrimethoxysilane as a silane coupling agent to modify the acetoacetyl group Polyvinyl alcohol: crosslinking agent: the solid component weight ratio of silane coupling agent is 1: 0.5: 0.1, further dilutes with pure water so that the acetoacetyl modified polyvinyl alcohol is 3 parts with respect to 100 parts of water, thereby Prepare an adhesive composition.
[0146] (b) Preparation of optical laminated body
[0147] A polarizing plate was prepared in which a protective ...
Embodiment 2
[0149] The crosslinking agent was changed to methylol melamine, and other operations were performed in the same manner as in (a) of Example 1 to prepare an adhesive composition. An optical layered body was produced by the method similar to (b) of Example 1 using this composition.
Embodiment 3~21
[0151] As polyvinyl alcohol, in addition to "Gohsefimer Z-200" shown in Example 1 (abbreviated as "Z-200" in Table 1 below), the following were used. In Table 1 below, the following items are represented by the symbols shown at the top, respectively.
[0152] T-330: anionized polyvinyl alcohol having a degree of saponification of 96.5 mol% (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., trade name "Gohsenol T-330", viscosity of 4% aqueous solution: 30.0 mPa·sec).
[0153] KL-318: anion-modified polyvinyl alcohol having a degree of saponification of 87.5 mol% (manufactured by Kuraray Japan, trade name "KL-318", viscosity of 4% aqueous solution is 25.0 mPa·sec).
[0154] Z-100: Acetoacetyl-modified polyvinyl alcohol with a saponification degree of 99.2 mol% (manufactured by Nippon Synthetic Chemical Industry Co., Ltd., trade name "Gohsefimer Z-100", the viscosity of a 4% aqueous solution is 5.2 mPa·sec) .
[0155] Z-210: Acetoacetyl-modified polyvinyl alcohol wi...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap