Twinning induced plasticity alloy steel with columnar crystal structure and preparation method thereof

A twin-induced plasticity, columnar crystal structure technology, applied in the aerospace field, can solve the problems of limited temperature gradient and cooling rate, and achieve the effect of large plasticity, high specific strength, and improved longitudinal mechanical properties

Active Publication Date: 2011-10-05
HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] The HRS method is cooled by radiation heat exchange, and the temperature gradient and cooling rate that can be obtained are very limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0025] Embodiment: Twin-induced plasticity alloy steel with columnar grain structure, wherein the contents of chemical components are: Mn: 30%, Al: 3%, Si: 2.9%, C: 0.06%, Fe: 64.04%.

[0026] A method for preparing a twin-induced plastic alloy steel with a columnar grain structure, comprising the following steps:

[0027] (1) Smelting: Mix a certain proportion of raw materials such as Mn, Al, Si, C, and Fe, and put them into a vacuum induction smelting furnace for smelting, and the protective atmosphere is argon to obtain a casting with a relatively uniform structure;

[0028] (2) Directional solidification: use smelted castings as raw materials, first select a certain size of material at a suitable casting part, put it into a directional solidification furnace and melt it under the protection of an argon atmosphere, and the preparation temperature is 1500 ° C, and then make the directional solidification The crucible in the solidification furnace is slowly lowered, and the l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses twinning induced plasticity alloy steel with a columnar crystal structure and a preparation method thereof. The preparation method mainly comprises the following steps of: mixing Mn, Al, Si, C and Fe elementary substances in a certain chemical ratio; and performing procedures of smelting, directional solidification and heat treatment. The structure of the alloy steel can be controlled to be columnar crystals, the horizontal crystal boundary is eliminated, the longitudinal mechanical properties of a material is greatly improved, and the mechanical properties of the alloy steel are regulated in a higher level; moreover, twin crystals are continuously formed, so that higher strength and plasticity are achieved; and compared with the traditional alloy steel, the twinning induced plasticity alloy steel has the characteristics of high specific strength, high specific rigidity, high energy absorptivity and the like, and has wide application prospect in various fields.

Description

technical field [0001] The invention relates to a twin-induced plasticity alloy steel with a columnar crystal structure and a preparation method thereof, in particular to a preparation method of a high-strength ultra-high plasticity alloy suitable for aerospace and other fields. Background technique [0002] Twin-induced plasticity alloys continue to form twins during the deformation process, significantly delaying necking, thereby obtaining higher strength and greater plasticity. Compared with traditional alloy steels, they have high specific strength, high specific stiffness and high energy absorption rate. It is a new material with integrated structure and function. As a structural material, it has the characteristics of light weight and high strength; as a functional material, it has the characteristics of efficient energy absorption, and has broad application prospects in many fields. For example, it can be used in bumpers, deep-drawn automotive parts, etc. Due to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/06B22D27/04C21D1/40C30B11/00C30B29/52C30B33/02
Inventor 段先锋韩福生汪聃王新福王幸福
Owner HEFEI INSTITUTES OF PHYSICAL SCIENCE - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com