Composite absorbing agent for processing hydrogen phosphide gas and preparation method thereof

An absorbent, phosphine technology, applied in chemical instruments and methods, separation methods, dispersed particle separation, etc., can solve the problems of many reaction conditions, harsh reaction conditions, small absorption capacity, etc., to achieve simple post-processing and absorption effect. Good and easy post-processing effect

Inactive Publication Date: 2011-11-16
田琳
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The catalytic oxidation method can effectively treat phosphine gas, but due to the many reaction conditions to be controlled (temperature, pressure, pH value, catalyst concentration, gas flow ratio, etc.), the corresponding equipment is more complicated and relatively Difficult to industrialize
Although the adsorption method can also effectively purify phosphine gas, the following problems generally exist in the adsorption method: (1) The regeneration process of the adsorbent is often complicated
Because the adsorbe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite absorbing agent for processing hydrogen phosphide gas and preparation method thereof
  • Composite absorbing agent for processing hydrogen phosphide gas and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] In this embodiment, the raw materials of the composite solid absorbent for processing phosphine gas are constituted in parts by mass: 75 parts of potassium hypochlorite, 20 parts of sawdust, 2 parts of activated carbon powder, 1 part of graphite powder, and 2 parts of talcum powder;

[0027] The composite solid absorbent used to treat phosphine gas in this example is obtained by stirring and mixing by the equal multiplication method, and the specific operation steps are as follows:

[0028] Add activated carbon powder, graphite powder and talcum powder to the mixer under normal temperature and pressure, and mix well to obtain mixture a. Add wood chips to mixture a several times. The volume of wood chips added each time is equal to the volume of the material in the mixer. The volumes are equal, and after each sawdust is added, stir at a speed of 30 rpm for 10 minutes until all the sawdust is added to obtain mixture b;

[0029] Add potassium hypochlorite to the mixture b ...

Embodiment 2

[0033] In this embodiment, the raw materials of the composite solid absorbent for processing phosphine gas are constituted by mass parts: 85 parts of bleaching powder, 10 parts of sawdust, and 5 parts of activated carbon powder;

[0034] The composite solid absorbent used to treat phosphine gas in this example is obtained by stirring and mixing by the equal multiplication method, and the specific operation steps are as follows:

[0035] Add activated carbon powder to the mixer under normal temperature and pressure and stir evenly to obtain mixture a. Add wood chips to mixture a several times. The volume of wood chips added each time is equal to the volume of the material in the mixer. Add wood chips each time Finally, stir at a speed of 30 rpm for 10 minutes until all the sawdust is added to obtain the mixture b;

[0036] Add the bleaching powder several times to the mixture b. The volume of the bleaching powder added each time is equal to the volume of the material in the mix...

Embodiment 3

[0040] In this embodiment, the raw materials of the composite solid absorbent for processing phosphine gas are constituted in parts by mass: 75 parts of bleaching powder, 20 parts of sawdust, 2.5 parts of graphite powder, and 2.5 parts of talcum powder;

[0041] The composite solid absorbent used to treat phosphine gas in this example is obtained by stirring and mixing by the equal multiplication method, and the specific operation steps are as follows:

[0042] Add graphite powder and talcum powder to the mixer under normal temperature and pressure, and mix well to obtain mixture a. Add wood chips to mixture a several times, and the volume of the wood chips added each time is equal to the volume of the material in the mixer. Stir at a speed of 30 rpm for 10 minutes after each sawdust is added, until all the sawdust is added to obtain mixture b;

[0043] Add the bleaching powder several times to the mixture b. The volume of the bleaching powder added each time is equal to the vol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite absorbing agent for processing hydrogen phosphide gas and a preparation method thereof. The raw materials of the composite absorbing agent for processing hydrogen phosphide gas comprise the following components of: by weight, 75-90% of an oxidizing agent, 5-20% of a leavening agent, 0-5% of an absorbing agent, 0-2.5% of an anti-caking agent and 0-2.5% of a dispersing agent. The composite solid absorbing agent is produced by stirring and mixing the above raw materials by equivalence multiplication method. The composite solid absorbing agent is an absorbing agent special for hydrogen phosphide gas, has high absorption efficiency and large absorption capacity, is easy for gases to permeate and is easy to store and transport; the solid residue produced after absorbing hydrogen phosphide gas is easy to process or can be used as the raw material of phosphate fertilizer, thus generating no second pollution.

Description

1. Technical field [0001] The invention relates to a poisonous gas absorbent and a preparation method thereof, in particular to a composite solid absorbent for treating phosphine gas and a preparation method thereof. 2. Background technology [0002] Phosphine (PH 3 ) is a colorless, foul-smelling gas at normal temperature and pressure, mainly produced in grain warehouse fumigation and insecticide, yellow phosphorus production, magnesium powder preparation, acetylene production, sodium hypophosphite production, semiconductor industry and sludge deposition and other processes middle. Phosphine gas is highly toxic. When the phosphine content in the air reaches 0.01mg / L, it will cause poisoning. Adults will die if they are exposed to a concentration of 0.05mg / L for 0.5 to 1 hour. Therefore, the gas containing phosphine must be treated before it can be discharged. [0003] There are many purification methods for phosphine, the most common ones are catalytic oxidation, adsorpt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D53/46
Inventor 田琳
Owner 田琳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap