A strip steel hot-dip galvanizing process
A technology of hot-dip galvanizing and strip steel, applied in hot-dip galvanizing process, metal material coating process, coating, etc., can solve the problem of unsatisfactory effect improvement, and achieve excellent peeling resistance and corrosion resistance Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0017] Example one
[0018] A hot-dip galvanizing process for strip steel, the composition of the strip steel is C: 0.2-0.25%, Mn: 1.2-1.5%, Si: 0.8-1.2%, P: ≤ 0.015%, S: ≤ 0.02% , The rest is Fe; the process includes the following steps:
[0019] (1) Strip cleaning treatment: After the strip is uncoiled, pickling is performed to remove the oxide film. The pickling solution is 25% hydrochloric acid, Tween-60 0.8% and water. Mechanical stirring is used while pickling; Then electrolytic degreasing treatment is carried out directly without clear water. The formula of electrolytic degreasing solution is 10 parts by weight sodium carbonate, 25 parts sodium phosphate, 60 parts sodium hydroxide and 300 parts water. The temperature of electrolytic degreasing is 60℃; Then enter the clean water tank for cleaning;
[0020] (2) Strip annealing treatment: The strip after degreased and cleaned is quickly blown dry with a nitrogen nozzle and enters a continuous annealing furnace under nitrogen pr...
Example Embodiment
[0025] Example two
[0026] A hot-dip galvanizing process for strip steel, the composition of the strip steel is C: 0.2-0.25%, Mn: 1.2-1.5%, Si: 0.8-1.2%, P: ≤ 0.015%, S: ≤ 0.02% , The rest is Fe; the process includes the following steps:
[0027] (1) Strip cleaning treatment: After the strip is uncoiled, pickling is performed to remove the oxide film. The pickling solution is hydrochloric acid with a concentration of 30%, Tween-60 0.5% and water. The pickling uses ultrasonic stirring at the same time; The electrolytic degreasing treatment is carried out directly without clear water. The formula of the electrolytic degreasing solution is 15 parts by weight sodium carbonate, 20 parts sodium phosphate, 70 parts sodium hydroxide and 270 parts water. The temperature of electrolytic degreasing is 80℃; after electrolytic degreasing Enter the clean water tank for cleaning;
[0028] (2) Strip annealing treatment: The strip after degreasing and cleaning is quickly blown dry with a nitrogen ...
Example Embodiment
[0033] Example three
[0034] A hot-dip galvanizing process for strip steel, the composition of the strip steel is C: 0.2-0.25%, Mn: 1.2-1.5%, Si: 0.8-1.2%, P: ≤ 0.015%, S: ≤ 0.02% , The rest is Fe; the process includes the following steps:
[0035] (1) Strip cleaning treatment: After the strip is uncoiled, pickling is performed to remove the oxide film. The pickling solution is 28% hydrochloric acid, Tween-60 0.6% and water. The pickling is carried out with ultrasonic stirring; then The electrolytic degreasing treatment is carried out directly without clean water. The formula of the electrolytic degreasing solution is 13 parts by weight sodium carbonate, 23 parts sodium phosphate, 65 parts sodium hydroxide and 280 parts water. The temperature of electrolytic degreasing is 70℃; after electrolytic degreasing Enter the clean water tank for cleaning;
[0036] (2) Strip annealing treatment: the strip steel after degreasing and cleaning is quickly blown dry with a nitrogen nozzle, and e...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap