Roll bearing grease lubricant and preparation method thereof

A roll bearing and lubricating grease technology, which is applied in the field of lubricating grease for rotating machinery and its preparation, can solve problems such as abnormal roll operation and affecting the normal operation of steel rolling, so as to improve bearing capacity, ensure lubrication stability and compressive performance, cost saving effect

Active Publication Date: 2012-01-11
AMER TECH CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the prior art, the lubricating grease used by the roll has no special characteristics in terms of pressure resistance, water washing resistance and lubrication stability in the presence of a large amount of water. During use, the roll will run abnormally and affect the normal production of steel rolling. run

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roll bearing grease lubricant and preparation method thereof
  • Roll bearing grease lubricant and preparation method thereof
  • Roll bearing grease lubricant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Roller bearing lubricating grease of present embodiment, lubricating grease raw material comprises following component by weight percentage: high-viscosity base oil A: 28%, high-viscosity base oil B: 30%, stearic acid: 16%, isobutylene adhesive agent : 17%, polymer polyisobutylene oil solution: 0.5%, liquid high molecular weight phenolic ester antioxidant: 1%, aminothioester antiwear agent: 3%, phosphate type extreme pressure agent: 2%, solid benzo Anti-rust agent: 0.3%, barium dinonyl naphthalene sulfonate anti-rust agent: 2.2%;

[0020] The high-viscosity base oil A is a mineral base oil with a viscosity of about 130 at 40°C, and the high-viscosity base oil B is a mineral base oil with a viscosity of about 550 at 40°C.

[0021] The preparation method of the roller bearing grease of the present embodiment may further comprise the steps:

[0022] a. Weigh the raw materials by weight percentage, mix high-viscosity base oil A, high-viscosity base oil B and stearic acid, ...

Embodiment 2

[0032] The roll bearing grease of the present embodiment, the grease raw material comprises the following components by weight percentage: high-viscosity base oil A: 33.9%, high-viscosity base oil B: 26.1%, stearic acid: 12%, isobutylene adhesive : 15%, polymer polyisobutylene oil solution: 1%, liquid high molecular weight phenolic ester antioxidant: 0.5%, aminothioester antiwear agent: 5%, phosphate type extreme pressure agent: 3%, solid benzo Anti-rust agent: 0.5%, barium dinonyl naphthalene sulfonate anti-rust agent: 3%;

[0033] The high-viscosity base oil A is a mineral base oil with a viscosity of about 130 at 40°C, and the high-viscosity base oil B is a mineral base oil with a viscosity of about 550 at 40°C.

[0034] The preparation method of the roller bearing grease of the present embodiment may further comprise the steps:

[0035] a. Weigh raw materials by weight percentage, mix high-viscosity base oil A, high-viscosity base oil B and stearic acid, and add a concent...

Embodiment 3

[0045] The roll bearing grease of the present embodiment, the grease raw material comprises the following components by weight percentage: high-viscosity base oil A: 27.2%, high-viscosity base oil B: 32.9%, stearic acid: 14%, isobutylene adhesive : 18%, polymer polyisobutylene oil solution: 0.8%, liquid high molecular weight phenolic ester antioxidant: 2%, aminothioester antiwear agent: 2%, phosphate type extreme pressure agent: 1%, solid benzo Anti-rust agent: 0.1%, barium dinonyl naphthalene sulfonate anti-rust agent: 2%;

[0046] The high-viscosity base oil A is a mineral base oil with a viscosity of about 130 at 40°C, and the high-viscosity base oil B is a mineral base oil with a viscosity of about 550 at 40°C.

[0047] The preparation method of the roller bearing grease of the present embodiment may further comprise the steps:

[0048] a. Weigh raw materials by weight percentage, mix high-viscosity base oil A, high-viscosity base oil B and stearic acid, and add a concent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a roll bearing grease lubricant and a preparation method thereof. By utilizing a thickening agent, i.e. stearic acid, the roll bearing grease lubricant has a better water-drenching resistance; and the grease lubricant has better adhesivity by matching with adhesive and high-viscosity base oil, so that the grease lubricant is not easy to be washed off by water and has lubrication stability; by combining with addition agents including a water-resisting extreme-pressure anti-wearing agent, an anti-rusting agent and the like, the grease lubricant can guarantee the extreme-pressure lubrication of a bearing in the presence of a lot of water; and therefore, the roll bearing which utilizes the grease lubricant provided by the invention has better water-drenching resistanceand adhesivity, a lubrication stability and a compressive property of the bearing can be guaranteed by the grease lubricant in the presence of a lot of water, the bearing capability of the roll bearing is improved, the service life is prolonged, and the cost is saved.

Description

technical field [0001] The invention relates to lubricating grease for rotating machinery and a preparation method thereof, in particular to a roll bearing lubricating grease and a preparation method thereof. Background technique [0002] The roll is an important part of the rolling mill in the rolling mill. It uses the pressure generated when a pair or a group of rolls roll to roll the steel; to obtain the desired shape of the steel. Since the roll is a rotating part, and its surface is in direct contact with steel, the bearing not only acts as a common rotation support, but also bears a large radial pressure, so it must be lubricated to achieve normal operation. At the same time, due to the harsh operating environment of the roll, in addition to bearing high temperature and heavy load, it will also be impacted by cooling water, so it will seriously affect its lubrication state, and the lubrication state has a decisive effect on the operating state of the bearing. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/00C10M177/00C10N40/02C10N50/10C10N30/06
Inventor 魏芳仕汪小龙
Owner AMER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com