Preparation method of flashing compound for tile

A technology for caulking and ceramic tiles, applied in the field of building materials, can solve the problems of shedding of ceramic tiles, influence of construction quality and decoration aesthetics, and high water absorption rate of caulking agent.

Inactive Publication Date: 2012-02-08
胡舜钦 +1
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramic tiles have become the main building materials in modern buildings and are widely used in the decoration of the interior and exterior walls and floors of buildings. Ordinary buildings use cement fine sand and water to make cement mortar and use it as a joint sealant. The common shortcomings of this kind of joint sealant mixed with ordinary cement and water in construction are low adhesion, fast hardening time, and short-term use. If it is not finished, the sealant will fail, which will cause the sealant to weather and fall off under the influence of natural environmental factors such as wind, sun, and rain soon after the decoration construction is completed, causing rainwater to seep into the gap between the tile and the wall During the time, the adhesive loses its adhesion and the tiles fall off
In addition, this type of caulking agent has a high water absorption rate, and the rainwater seeps in to form soluble salts that flow out with the rainwater to produce "white pulp", which seriously pollutes the wall surface
This not only seriously affects the quality of construction and the appearance of decoration, but also the natural fall of tiles from high places will cause potential harm at any time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0014] Example 2 of the present invention includes Portland cement, quartz sand (70-110 mesh), high-alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, and high-efficiency water reducer; Its mass ratio is Portland cement, quartz sand, high alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, high-efficiency water reducer; the weight percentage of each component is silicon Salt cement 28%, quartz sand (70-110 mesh) 62%, high alumina cement 5%, dispersible latex powder 2%, cellulose ether 1.5%, powder defoamer 0.6%, powder water repellent 0.4% , High-efficiency water reducer 0.5%.

Embodiment 3

[0016] Example 3 of the present invention includes Portland cement, quartz sand (70-110 mesh), high alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, and high-efficiency water reducer; Its mass ratio is Portland cement, quartz sand, high alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, high-efficiency water reducer; the weight percentage of each component is silicon Salt cement 25%, quartz sand (70-110 mesh) 65%, high alumina cement 6%, redispersible latex powder 1.5%, cellulose ether 1%, powder defoamer 0.5%, powder water repellent 0.6% , High-efficiency water reducer 0.4%.

Embodiment 4

[0018] Example 4 of the present invention includes Portland cement, quartz sand (70-110 mesh), high alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, and high-efficiency water reducer; Its mass ratio is Portland cement, quartz sand, high alumina cement, dispersible latex powder, cellulose ether, powder defoamer, powder water repellent, high-efficiency water reducer; the weight percentage of each component is silicon Salt cement 35%, quartz sand (70-110 mesh) 50%, high alumina cement 10%, dispersible latex powder 1.5%, cellulose ether 2%, powder defoamer 0.5%, powder water repellent 0.5% , High-efficiency water reducer 0.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a preparation method of a waterproof and weather-resistant flashing compound special for filling slits between tiles. The flashing compound comprises components by weight of 25-35% of portland cement, 50-68% of quartz sand (70-110 mesh), 5-10% of bauxite cement, 1.5-2% of redispersible emulsion powder, 1-2% of cellulose ether, 0.3-0.6% of powder antifoaming agent, 0.3-0.6% of powder water repellent and 0.3-0.6% of high efficiency water reducing agent. Compared with a flashing compound of a prior art, the flashing compound of the invention has characteristics of wide construction range, strong adhesive force, water resistance, and weather resistance, and can be widely used in slit filling of tiles and other construction materials; therefore, the flashing compound has promising popularization and application values.

Description

1. Technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a preparation method of a ceramic tile waterproof caulking agent. 2. Background technology [0002] Ceramic tiles have become the main building materials in modern buildings and are widely used in the decoration of the interior and exterior walls and floors of buildings. Ordinary buildings use cement fine sand and water to make cement mortar and use it as a joint sealant. The common shortcomings of this kind of joint sealant mixed with ordinary cement and water in construction are low adhesion, fast hardening time, and short-term use. If it is not finished, the sealant will fail, which will cause the sealant to weather and fall off under the influence of natural environmental factors such as wind, sun, and rain soon after the decoration construction is completed, causing rainwater to seep into the gap between the tile and the wall In the meantime, the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B111/27C04B111/21
Inventor 胡舜钦贺江波汤建新许利剑
Owner 胡舜钦
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products