Method for preparing anodic alumina template by using plastic packaging process and application thereof

A technology of anodized aluminum and aluminum oxide templates, which is applied in the direction of surface reaction electrolytic coating, electrolytic coating, coating, etc., can solve the problems that have not been reported or disclosed, and achieve the improvement of preparation success rate, significant economic benefits, and reduction of The effect of preparation costs

Inactive Publication Date: 2012-02-22
JINAN UNIVERSITY
View PDF11 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, no attempt in this direc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing anodic alumina template by using plastic packaging process and application thereof
  • Method for preparing anodic alumina template by using plastic packaging process and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Cut the high-purity aluminum sheet (purity 99.999%, Beijing Nonferrous Metals and Rare Earth Application Research Institute) into a square of 70×50mm, and clean it ultrasonically (ultrasonic frequency 40kHz) in acetone (analytical purity, mass fraction greater than 99.5%) After 5 minutes, rinse with deionized water, and then ultrasonically clean (ultrasonic frequency 40 kHz) in absolute ethanol (analytical grade, mass fraction greater than 99.7%) for 15 minutes, and air-dry.

[0032] (2) The aluminum sheet was annealed in a box-type high-temperature furnace (KSL-1100X, Hefei Kejing Material Technology Co., Ltd.) for 5 hours at an annealing temperature of 500°C.

[0033] (3) Use an ordinary rectangular plastic sleeve with a size of 95×75mm, and cut out a rectangular window with a size of 60×40mm on one side; place the annealed aluminum sheet in the plastic sleeve for plastic sealing (Qixin F9061 plastic sealing machine).

[0034] (4) Electrochemical polishing was per...

Embodiment 2

[0042] (1) Cut the high-purity aluminum sheet (purity 99.999%, Beijing Nonferrous Metals and Rare Earth Application Research Institute) into a square of 70×50mm, and clean it ultrasonically (ultrasonic frequency 40kHz) in acetone (analytical purity, mass fraction greater than 99.5%) After 5 minutes, rinse with deionized water, and then ultrasonically clean (ultrasonic frequency 40 kHz) in absolute ethanol (analytical grade, mass fraction greater than 99.7%) for 15 minutes, and air-dry.

[0043] (2) The aluminum sheet was annealed in a box-type high-temperature furnace (KSL-1100X, Hefei Kejing Material Technology Co., Ltd.) for 5 hours at an annealing temperature of 500°C.

[0044] (3) Use an ordinary rectangular plastic sleeve with a size of 95×75mm, and cut out a rectangular window with a size of 60×40mm on one side; place the annealed aluminum sheet in the plastic sleeve for plastic sealing (Qixin F9061 plastic sealing machine).

[0045] (4) Electrochemical polishing was per...

Embodiment 3

[0053] (1) Cut the high-purity aluminum sheet (purity 99.999%, Beijing Nonferrous Metals and Rare Earth Application Research Institute) into a square of 70×50mm, and clean it ultrasonically (ultrasonic frequency 40kHz) in acetone (analytical purity, mass fraction greater than 99.5%) After 5 minutes, rinse with deionized water, and then ultrasonically clean (ultrasonic frequency 40 kHz) in absolute ethanol (analytical grade, mass fraction greater than 99.7%) for 15 minutes, and air-dry.

[0054] (2) The aluminum sheet was annealed in a box-type high-temperature furnace (KSL-1100X, Hefei Kejing Material Technology Co., Ltd.) for 5 hours at an annealing temperature of 500°C.

[0055] (3) Use an ordinary rectangular plastic sleeve with a size of 95×75mm, and cut out a rectangular window with a size of 60×40mm on one side; place the annealed aluminum sheet in the plastic sleeve for plastic sealing (Qixin F9061 plastic sealing machine).

[0056] (4) Electrochemical polishing was per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing an anodic alumina template by using a plastic packaging process and application thereof. The core point of the method is that the plastic packaging process is utilized for insulation blocking on one surface needing no reaction or treatment of an aluminum sheet, and the method comprises the following steps that: during electrochemical polishing of the aluminum sheet, one surface of the aluminum sheet is sealed by using the plastic packaging process, and the other surface of the aluminum sheet is exposed for polishing; during anodic oxidation of the aluminum sheet, only the surface exposed for polishing is subjected to anodic oxidation due to insulation blocking resulting from plastic packaging; during removal of an aluminum base, by utilizing sealing protection of plastic packaging to the alumina template, a surface of the aluminum base is exposed in a solution and removed so as to obtain the anodic alumina template. The anodic alumina template prepared by the method is colorless and transparent, has a high degree of order and is easy to preserve. According to the invention, high quality alumina templates can be prepared by using plastic package glue cover without any special equipment, and preparation of an alumina template with a large area is made to be simple and easy, thereby greatly improving a success rate of preparing templates, reducing preparation cost for the templates and having remarkable economic benefits.

Description

technical field [0001] The invention relates to the electrochemical preparation of templates, in particular to a method and application for preparing anodized aluminum templates by using a plastic sealing process. Background technique [0002] A template refers to a film containing high-density columnar holes with a thickness of tens to hundreds of microns. Porous alumina template is the most widely used template so far. The micropores in the membrane are highly ordered and have good thermal and chemical stability. It is an ideal inorganic template for preparing nanoelectronic materials with highly uniform and ordered shapes. Porous alumina templates can be prepared by anodic oxidation of high-purity aluminum in acidic solution. This type of film has many cylindrical pores arranged in a hexagonal array with uniform pore diameters, and the pores are parallel to each other and perpendicular to the membrane surface. The pore diameter of the aluminum oxide film is up to 200 na...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25D11/12C23F1/02C23F1/20
Inventor 乐松严振升
Owner JINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap