Environment-friendly and flame-retardant decorative plate and production method thereof

An environmentally friendly technology for decorative panels, applied in the field of environmentally friendly flame-retardant decorative panels and their preparation, can solve the problems of heavy weight, poor environmental protection effect, brittleness and easy breakage, etc., and achieve the effect of good strength and toughness

Inactive Publication Date: 2013-05-08
孙振芳
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most materials have superior performance, but there are also certain defects. For example, some have poor environmental protection effect and are not flame-retardant. broken, brittle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly and flame-retardant decorative plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An environmentally friendly flame retardant decorative board is composed of the following components:

[0032] Component A: composed of 50kg magnesium oxide and 50kg lignocellulose;

[0033] Component B: 88kg magnesium chloride solution with a concentration of 23%-26%;

[0034] Component C: 1kg of paraffin, 0.3kg of stearic acid, and 3.9kg of water, heated to the boiling point, after making it fully dissolved, then adding 0.039kg of 30% sodium hydroxide solution and stirring to form an emulsion;

[0035] Component D: 1-3 layers of glass fiber cloth;

[0036] and is made by the following steps:

[0037] ① Put the magnesium oxide and lignocellulose in component A into the mixer;

[0038] ②Pour component B into the mixer and mix with component A;

[0039] ③ Pour the prepared component C emulsion into the above mixer, and fully stir with component A and component B;

[0040] ④The stirred material and 1-3 layers of glass fiber cloth are made into plates by a plate makin...

Embodiment 2

[0046] An environmentally friendly flame retardant decorative board is composed of the following components:

[0047] Component A: composed of 80kg magnesium oxide and 20kg lignocellulose;

[0048] Component B: 76kg magnesium chloride solution with a concentration of 23%-26%;

[0049] Component C: 4kg of paraffin, 1.3kg of stearic acid, and 15.9kg of water are heated to the boiling point, and after it is fully dissolved, 0.159kg of 30% sodium hydroxide solution is added, and the mixture is stirred into an emulsion;

[0050] Component D: 1-3 layers of glass fiber cloth.

[0051] The preparation method is the same as that in Example 1.

Embodiment 3

[0053] An environmentally friendly flame retardant decorative board is composed of the following components:

[0054] Component A: composed of 70kg magnesium oxide and 30kg lignocellulose;

[0055] Component B: 80kg magnesium chloride solution with a concentration of 23%-26%;

[0056] Component C: 3kg of paraffin, 1kg of stearic acid, 12kg of water, heated to the boiling point, after making it fully dissolved, 0.12kg of 30% sodium hydroxide solution was stirred into an emulsion;

[0057] Component D: 1-3 layers of glass fiber cloth.

[0058] The preparation method is the same as that in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly and flame-retardant decorative plate, which is produced from 50-80 percent of magnesium oxide, 20-50 percent of lignocellulose, magnesium chloride solution with the concentration of 23-26 percent, emulsion prepared by adding water and sodium hydroxide solution in paraffin and stearic acid as well as 1-3 layers of glass fiber cloth through a stirrer and a plate producer. The environment-friendly and flame-retardant decorative plate disclosed by the invention has the advantages of no poison or odor, environment friendliness, fire resistance, flameretardance, favorable strength and tenacity and no harm to a human body; the environment-friendly and flame-retardant decorative plate is suitably used as a decoration material and an indoor supply, such as office furniture, i.e. the environment-friendly and flame-retardant decorative plate can be used as a floor or a plate of the decoration material. The invention also discloses a production method of the environment-friendly and flame-retardant decorative plate.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant decorative plate and a preparation method. Background technique [0002] At present, the fire-resistant decorative materials used in the construction industry and the furniture industry have attracted much attention and have a wide variety. Most materials have superior performance, but there are also certain defects. For example, some materials have poor environmental protection effect and are not flame retardant. Although some achieve the effect of environmental protection and flame retardant, they have other shortcomings, such as large weight, poor toughness, and easy to use ingot nails. Cracked, brittle and easy to break. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to provide an environment-friendly, flame-retardant, environmentally friendly flame-retardant decorative plate and a preparation method thereof in order to overcome the deficiencies of the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/075B27N3/06B27N1/00
Inventor 孙振芳
Owner 孙振芳