Polyester composite for forming thermoset films

A composition and heat-curing technology, applied in the fields of instruments, optics, nonlinear optics, etc., can solve problems such as difficulty in applying planarized film production lines, reduced planarization and transparency, low solubility of ester solvents, etc., and achieve high Effects of solvent resistance, high heat resistance, and high planarization

Active Publication Date: 2012-03-07
NISSAN CHEM IND LTD
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, attempts to create a planarized film for color filters have resulted in problems such as a significant decrease in planarization and transparency.
In addition, although polyimide and polyamic acid are soluble in solvents such as N-methyl-2-pyrrolidone and γ-butyrolactone, they have low solubility in diol-based solvents and ester-based solvents, making it difficult to apply to flat surfaces. Chemical film production line

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester composite for forming thermoset films
  • Polyester composite for forming thermoset films
  • Polyester composite for forming thermoset films

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0164] The following examples are given to illustrate the present invention in more detail, but the present invention is not limited to these examples.

[0165] [Abbreviated symbols used in Examples]

[0166] The meanings of the abbreviated symbols used in the following examples are as follows.

[0167]

[0168] HBPDA: 3,3'-4,4'-Dicyclohexyltetracarboxylic dianhydride

[0169] BPDA: biphenyltetracarboxylic dianhydride

[0170] BPADA: 4,4'-(4,4'-isopropylidenediphenoxy)bisphthalic anhydride

[0171] HBPA: hydrogenated bisphenol A

[0172] THPA: 1,2,5,6-tetrahydrophthalic anhydride

[0173]

[0174] BTEAC: Benzyltriethylammonium Chloride

[0175]

[0176] DA-4P: 1,3-bis(4-aminophenyl)benzene

[0177] DA-1M: 4,4'-bis(4-aminophenoxy)diphenylsulfone

[0178] TA: 1,2,4-trimesic anhydride

[0179] DDM: 4,4'-Diaminodiphenylmethane

[0180]

[0181] CBDA: Cyclohexanetetracarboxylic dianhydride

[0182] pDA: p-phenylenediamine

[0183]

[0184] MAA: methacrylic acid...

Synthetic example 1

[0200] 18.0 g of HBPDA, 4.54 g of BPDA, 15.9 g of HBPA, 2.01 g of THPA, and 0.19 g of BTEAC were reacted in 95.1 g of PGMEA at 120° C. for 19 hours to obtain a polyester solution (solid content concentration: 30.0% by mass) (P1 ). Mn of the obtained polyester was 1,510, and Mw was 3,570.

Synthetic example 2

[0202] HBPDA 12.0g, HBPA 10.2g, THPA 0.95g, and BTEAC 0.22g were reacted in PGMEA54.48g at 120 degreeC for 19 hours, and the polyester solution (solid content concentration: 30.0 mass %) was obtained (P2). Mn of the obtained polyester was 2,280, and Mw was 4,200.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

Provided is a polyester composite for forming thermoset films, said composite having, after forming a thermoset film, high resistance to solvents and heat, good liquid crystal orientation, high transparency, and high planarizability. Said composite can also, when forming a thermoset film, be dissolved in glycol solvents and lactate ester solvents that can be applied to production lines for planarized color filter films. The composite contains: a component (A) which is a polyester obtained by reacting a tetracarboxylic dianhydride with a diol compound; a component (B) which is an epoxy compound having at least two epoxy groups; and a component (C) which is an amino-group-containing carboxylic compound obtained by reacting a diamine compound with a dicarboxylic anhydride.

Description

technical field [0001] The present invention relates to a thermosetting film-forming polyester composition and a cured film obtained from the thermosetting film-forming polyester composition. More specifically, the present invention relates to a polyester composition for forming a thermosetting film and a cured film thereof having high transparency, flattening property, liquid crystal orientation capability, high solvent resistance, and heat resistance, and to the cured Membrane application. This polyester composition for thermosetting film formation is suitable especially as a color filter overcoat agent which has a liquid-crystal orientation function in a liquid crystal display. Background technique [0002] In general, optical devices such as liquid crystal display elements, organic EL (electroluminescent) elements, and solid-state imaging elements are provided with a protective film to prevent the element surface from being exposed to solvents and / or heat during the man...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G59/40G02F1/1337
CPCC08G59/42C08G59/54C08G59/56C08J5/18C08J2367/00C08L63/00C08L67/00C08L2666/22
Inventor 畑中真安达勲
Owner NISSAN CHEM IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka