High-strength hot-dip galvanized steel plate and method for producing same

A technology of hot-dip galvanized steel sheet and manufacturing method, which is applied in the direction of manufacturing tools, hot-dip coating process, heat treatment furnace, etc., and can solve the problems that cannot pass through the full-radiant tube heating furnace.

Active Publication Date: 2012-03-14
JFE STEEL CORP
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult to perform such control with the existing technology, and the CGL equipped with a full-radiant tube heating furnace in the annealing furnace cannot use Si-containing high-strength steel sheets as the base material to produce hot-dip coatings with excellent coating peeling resistance during high-load processing. Zinc steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength hot-dip galvanized steel plate and method for producing same
  • High-strength hot-dip galvanized steel plate and method for producing same
  • High-strength hot-dip galvanized steel plate and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0127] Hereinafter, the present invention will be specifically described based on examples.

[0128] A hot-rolled steel sheet having a steel composition shown in Table 1 was pickled to remove black scale, and then cold-rolled under the conditions shown in Table 2 to obtain a cold-rolled steel sheet with a thickness of 1.0 mm.

[0129]

[0130] The cold-rolled steel sheet obtained as above was loaded into the CGL equipped with the full radiant tube heating furnace among the annealing furnaces. In CGL, as shown in Table 2, the steel sheet is passed through under the conditions of controlling the dew point in the temperature range of 750°C or higher in the heating furnace as shown in Table 2, and after annealing, it is carried out using a Zn bath containing Al at 460°C. Hot-dip galvanized treatment.

[0131] It should be noted that the gas components in the atmosphere consist of nitrogen, hydrogen, and unavoidable impurities, and the dew point is controlled by absorbing and r...

Embodiment 2

[0163] The hot-rolled steel sheets having the steel compositions shown in Table 3 were pickled to remove black scale, and then cold-rolled under the conditions shown in Table 4 to obtain cold-rolled steel sheets with a thickness of 1.0 mm.

[0164]

[0165] The cold-rolled steel sheet obtained as above was loaded into the CGL equipped with the full radiant tube heating furnace among the annealing furnaces. In CGL, as shown in Table 4, the steel sheet is passed through under the conditions of controlling the dew point in the temperature range of 600°C or higher in the heating furnace as shown in Table 4, and after annealing, it is carried out using a Zn bath containing Al at 460°C. Hot-dip galvanized treatment.

[0166] It should be noted that the gas components in the atmosphere consist of nitrogen, hydrogen, and unavoidable impurities, and the dew point is controlled by absorbing and removing moisture in the atmosphere. The hydrogen concentration in the atmosphere is base...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Adhesion amountaaaaaaaaaa
Login to View More

Abstract

Provided is a method for producing a high-strength hot-dip galvanized steel plate having a galvanized layer formed on the surfaces of a steel plate containing, in terms of mass%, C (0.01 to 0.18%), Si (0.02 to 2.0%), Mn (1.0 to 3.0%), Al (0.001 to 1.0%), P (0.005 to 0.060%), S (0.01% or less), and Fe and unavoidable impurities as the remainder such that the amount of adhesion of zinc per surface is from 20 to 120 g / m2, wherein, when the steel plate is subjected to annealing and hot-dip galvanizing treatments in continuous hot-dip galvanizing equipment, the temperature in an annealing furnace in a range of 750 DEG C or higher is regulated such that the dew point of the atmosphere is -40 DEG C or lower. According to this production method, a high-strength hot-dip galvanized steel plate having excellent corrosion resistance and also excellent resistance to galvanized coat peeling when subjected to a high degree of processing is obtained.

Description

technical field [0001] The present invention relates to a high-strength galvanized steel sheet having excellent workability using a high-strength steel sheet containing Si and Mn as a base material and a method for producing the same. Background technique [0002] In recent years, hot-dip galvanized steel sheets and alloyed hot-dip galvanized steel sheets among surface-treated steel sheets for imparting rust resistance to base steel sheets have been widely used in the fields of automobiles, home appliances, and building materials. In addition, from the viewpoint of improving the fuel efficiency of automobiles and improving the crash safety of automobiles, it is strongly desired to reduce the thickness of the body material by increasing the strength of the body material, thereby reducing the weight and increasing the strength of the body itself. Therefore, the application of high-strength steel sheets to automobiles has been promoted. [0003] Generally, a hot-dip galvanized...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/02C21D1/74C21D9/46C22C18/00C22C38/00C22C38/06C22C38/58C23C2/06C23C2/28