Tin case aerosol type cleaning agent

A technology of tinplate cans and aerosols, which is applied in the field of aerosol cleaning agents, can solve the problems of ignoring water purity requirements, etc., and achieve low cost, good anti-corrosion effect, and good cleaning effect

Active Publication Date: 2013-04-17
ANHUI TAILONG CHENGYA GRP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although most people are familiar with the corrosiveness of water purity to metals, when it comes to the production of aerosol cleaners for tinplate cans, the purity requirements of water are often ignored, so that when corrosion occurs, it is not known where the problem lies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Nonylphenol polyoxyethylene ether (TX-10) 2 grams

[0029] Fatty alcohol polyoxyethylene ether (AEO-9) 2 grams

[0030] Coconut fatty acid diethanolamide (6501, model 1:1.5) 1 g

[0031] Ethanol 2 grams

[0032] Triethanolamine 1 g

[0033] Sodium Benzoate 1 g

[0034] Sodium molybdate 0.4 g

[0035] Deionized water 90.5 grams

[0036] Essence 0.1 g.

Embodiment 2

[0038] Nonylphenol polyoxyethylene ether (TX-10) 0.5 g

[0039] Fatty alcohol polyoxyethylene ether (AEO-9) 1 g

[0040] Coconut fatty acid diethanolamide (6501, model 1:1.5) 2g

[0041] Triethanolamine 2 g

[0042] Ethanol 5 grams

[0043] Sodium Benzoate 2 g

[0044] Sodium molybdate 0.8 g

[0045] 86.6 grams of deionized water

[0046] Essence 0.1 g.

Embodiment 3

[0048] Nonylphenol polyoxyethylene ether (TX-10) 3 grams

[0049] Fatty alcohol polyoxyethylene ether (AEO-9) 3 grams

[0050] Coconut fatty acid diethanolamide (6501, model 1:1.5) 2g

[0051] Triethanolamine 3 g

[0052] Ethanol 5 grams

[0053] Sodium Benzoate 2 g

[0054] Sodium molybdate 0.8g

[0055] Deionized water 81.1g

[0056] Essence 0.1 g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tin case aerosol type cleaning agent, which comprises a solution consisting of nonylphenol polyoxyethylene ether, fatty alcohol-polyoxyethylene ether, coconut oil fatty acid diethanol amide, triethanolamine, ethanol, sodium benzoate, sodium molybdate, deionized water and essence; and the solution is mixed uniformly and then put into a tin case, a specified amount of propane / butane gas reaching the rated pressure is introduced, and thus the product is obtained. The cleaning agent has good anticorrosive effect on the tin case, does not leak, has good cleaning effect and low cost, and is widely applied to cleaning of various articles in the fields of automobile maintenance, home care and the like.

Description

technical field [0001] The invention relates to an aerosol type cleaning agent, in particular to an aerosol type cleaning agent for a tin can. Background technique [0002] Aerosol-type cleaning agents are widely used in the cleaning of various items in the fields of car maintenance and home care due to their convenience, quickness and reasonable price. Usually aerosol cleaning agents are packed in tinplate cans. However, the cans are easily corroded and leaks often occur. This has long been a common problem for all manufacturers. Metal corrosion is divided into three types: chemical corrosion, electrochemical corrosion, and physical corrosion. The corrosion of tinplate is mainly electrochemical corrosion, which is divided into three processes: the first process is the oxidation of the anode metal and the release of electrons, the tin plating on the outer layer of the tinplate is oxidized and peeled off, and the iron at the bottom begins to be oxidized into iron ions; The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G5/00
Inventor 梁玉斌
Owner ANHUI TAILONG CHENGYA GRP CO LTD