Production method for cardanol modified phenolic resin

A technology of phenolic resin and production method, which is applied in the field of copper clad laminate production, can solve the problems of reducing hardness and flexibility, cost reduction, long reaction time, etc., and achieve good flatness and heat resistance, good flexibility, and simple method Effect

Active Publication Date: 2012-04-11
JIANGSU SUNYUAN AEROSPACE MATERIAL
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is complicated, the reaction time is long, and the efficiency is low, and cardanol only replaces part of tung oil, and the cost reduction is limited
[0005] In addition, because tung oil has a long-chain structure, its molecular formula contains two double bonds, while the molecular structure of cardanol has a benzene ring on one side, with only one double bond, so the network structure formed after the reaction of cardanol is more complex than that formed after the reaction of tung oil. There is less mesh structure, which reduces the hardness and flexibility of the product, causing the worthwhile copper clad laminate to crack easily when punching holes, seriously affecting product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Preparation of modified phenolic resin solution:

[0032] The mass part proportioning of raw materials for the preparation of the modified phenolic resin solution is as follows:

[0033] 150 parts of phenol;

[0034] Cardanol 14 parts;

[0035] 230 parts of formaldehyde;

[0036] 0.1 part of triethylamine;

[0037] 2.0 parts of ammonia water;

[0038] 350 parts of methanol;

[0039] During preparation, add phenol, cardanol, formaldehyde, triethylamine and ammonia water in the above ratio into the reaction kettle, stir, heat up to 95-98°C within 25 minutes, then keep the temperature for 120-130 minutes, and the measured gel value is 240 -250 seconds, vacuum dehydration, the temperature rises to above 80°C, stop the vacuum, measure the gel value for 80-90 seconds, then add methanol as a solvent to prepare a phenolic resin solution;

[0040] Two, preparation of modified phenolic resin composition

[0041] Take 100 parts of phenolic resin solution, add 11 parts of...

Embodiment 2

[0043] The preparation method in this embodiment is identical with embodiment 1, and its difference is only in:

[0044] In the first step:

[0045] 201 parts of phenol;

[0046] Cardanol 150.8 parts;

[0047] 241.2 parts of formaldehyde;

[0048] 2.0 parts of triethylamine;

[0049] 3.0 parts of ammonia water;

[0050] 380 parts of methanol;

[0051] In the second step:

[0052] 100 parts of phenolic resin solution, 15 parts of silicon micropowder, 12 parts of epoxy soybean oil (supplier: Zhejiang Tongxiang Chemical Co., Ltd., model: ESO).

Embodiment 3

[0054] The preparation method in this embodiment is identical with embodiment 1, and its difference is only in:

[0055] In the first step:

[0056] 210 parts of phenol;

[0057] Cardanol 185 parts;

[0058] 260 parts of formaldehyde;

[0059] 2.3 parts of triethylamine;

[0060] 4.2 parts of ammonia water;

[0061] 400 parts of methanol;

[0062] In the second step:

[0063] 100 parts of phenolic resin solution, 18 parts of silicon micropowder, 15 parts of epoxy soybean oil (supplier: Zhejiang Tongxiang Chemical Co., Ltd., model: ESO).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a production method for cardanol modified phenolic resin, wherein the method comprises the following steps: 1, preparing modified phenolic resin solution, the raw materials for preparing the modified phenolic resin solution based on mass parts proportioning are as follows: 150-210 parts of phenol, 148-185 parts of cardanol, 230-260 parts of formaldehyde, 0.1-2.3 parts of triethylamine, 2.0-4.2 parts of ammonia water and 350-400 parts of methanol, wherein when preparing, adding the phenol, cardanol, formaldehyde, triethylamine and ammonia water based on the proportioning into a reaction kettle to react, and adding methanol as dissolvent to prepare phenolic resin solution; 2, preparing modified phenolic resin composite: taking 100 parts of phenolic resin solution and adding 11-18 parts of silicon micro-powder and 10-15 parts of epoxidized soybean oil into the solution, and fully mixing them to obtain the finished product. The invention is characterized by simple technology and low production cost. The prepared copper-clad plate has good flexibility.

Description

technical field [0001] The invention relates to a production method of cardanol-modified phenolic resin, which is mainly used in the field of copper-clad laminate production. Background technique [0002] Copper-clad laminate is a plate material made by impregnating electronic glass fiber cloth or other reinforcing materials with resin, covering one or both sides with copper foil and hot pressing. It is called copper-clad laminate (Copper-clad laminate) Clad Laminate, CCL), referred to as copper clad laminate. [0003] Copper clad laminate is an extremely important basic material for printed circuit boards. Printed circuit boards of various forms and functions are selectively processed, etched, drilled and copper-plated on copper clad laminates. Different printed circuits (single-sided, double-sided, multilayer). As the substrate material in the manufacture of printed circuit boards, copper clad laminates mainly play the role of interconnection, insulation and support for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/34C08K3/34C08K5/1515C08G14/073
Inventor 王忠义
Owner JIANGSU SUNYUAN AEROSPACE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap