Helicopter composite material paddle fatigue test piece molding method

A composite material and molding method technology, which is used in the testing of mechanical parts, the testing of machine/structural parts, and the preparation of samples for testing, etc. Leaf scrap and other problems, to ensure stability and smoothness, improve the pass rate of one-time inspection, and shorten the manufacturing cycle.

Inactive Publication Date: 2012-06-20
中航直升机股份有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0028] With this method, it is easy to mill off the latitude-free tape when milling the plane, which will greatly weaken the rigidity and strength of the blade fatigue test piece; it is also difficult to ensure the symmetry when assembling the splint, which makes the verticality of the boring hole also large. Affected
In addition, the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Helicopter composite material paddle fatigue test piece molding method
  • Helicopter composite material paddle fatigue test piece molding method
  • Helicopter composite material paddle fatigue test piece molding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0079] 1. Blade cutting, hollowing out

[0080] Remove the iron covering from the formed molded blade, and draw the blade cutting reference line Zx on the blade according to the design requirements, taking the 0-section position of the blade as the reference 1 、Zx 2 , cut off the molded paddle according to the reference line and remove the burrs, and hollow out the foam in the inner cavity of the end of the molded paddle according to the design requirements;

[0081] 2. Paddle filling

[0082] Fill the cavity at the end of the specimen with the chopped fiber mixture, remove air bubbles, and smooth it. Tape the foam blocks at the ends to prevent the flow of the chopped fiber mixture, waiting to cure;

[0083] 3. Paste the vacuum bag, solidify, open the mold

[0084] Curing: heat up to 100±5°C and keep the temperature constant for 6 hours

[0085] 4. Drilling holes for paddle 1

[0086] Use the fatigue test piece drilling jig to determine the hole position required by the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to a composite material molding technology, and relates to helicopter composite material paddle fatigue test piece molding technological process which is suitable for helicopter composite material technological process molding. According to the invention, a platform thickness spacing tool is adopted, an interval between two splints of a paddle fatigue test piece is effectively ensured, and simultaneously the positioning of the spacing tool can insure symmetry of the two splints; and a working procedure of numerical control processing is directly omitted from a technical process, furthermore a manufacturing cycle is also shortened, once alternating detection qualification rate of the paddle fatigue test piece is improved, the rejection rate of the paddle fatigue test piece is zero, and the stability and the smoothness of the assembly process of the paddle fatigue test piece are ensured.

Description

technical field [0001] The invention belongs to composite material forming technology, and relates to a forming process method for a helicopter composite material blade fatigue test piece suitable for forming a helicopter composite material blade fatigue test piece. Background technique [0002] The rotor blade is a flexible, slender elastic body with low natural frequency. When working, the high-speed rotating blade is subjected to high centrifugal force load and alternating aerodynamic load, resulting in high alternating stress. Therefore, during the exploratory period of helicopter development, the blades were easily broken. The fatigue test results carried out on a special fatigue test bench are the most direct indicators to reflect the performance of the blade. Therefore, it is the most critical to manufacture the blade fatigue test piece with excellent fatigue performance. [0003] The traditional process for preparing the blade fatigue test piece is, [0004] 1. Bl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N1/28G01M13/00
Inventor 李丽丽宋文娟李硕强
Owner 中航直升机股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap