Method for fabricating peony porcelain

A technique of making peony porcelain, which is applied to clay products, other household utensils, household utensils, etc., to achieve the effect of lifelike images, improved quality of finished products, and bright colors

Active Publication Date: 2012-06-27
李学武
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] It can be seen from the above that ceramics, as a kind of utensils that can be preserved for a long time, can keep flowers blooming forever if they are combined with flower making. After searching, no combination of ceramics and flowers has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A manufacturing process of peony porcelain, which uses porcelain clay base material, glaze raw material and colored china clay for firing, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0060] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentage of each raw material is: 20% of aluminum oxide, 0.3% of iron oxide, 0.3% of Calcium 0.01%, Magnesium Oxide 0.01%, Potassium Oxide 2.5%, Sodium Oxide 0.14%, Titanium Dioxide 0.04% and Quartz 77%;

[0061] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 6%, quartz 10%, calcite 4%, kaolin 15% %, alumina 5%, clay 30%, porcelain stone 15%, potassium feldspar 15%;

[0062] The red china clay is ...

Embodiment 2

[0080] A manufacturing process of peony porcelain, which uses porcelain clay base material, glaze raw material and colored china clay for firing, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0081] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentage of each raw material is: 30% of aluminum oxide, 0.3% of iron oxide, 0.3% of Calcium 0.01%, magnesium oxide 0.01%, potassium oxide 2.4%, sodium oxide 0.14%, titanium dioxide 0.04% and quartz 67%;

[0082] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 10%, quartz 4%, calcite 6%, kaolin 17% %, alumina 3%, white clay 25%, porcelain stone 17%, potassium feldspar 18%;

[0083] The red china cl...

Embodiment 3

[0101] A manufacturing process of peony porcelain, which uses porcelain clay base material, glaze raw material and colored china clay for firing, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0102] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentages of each raw material added are: aluminum oxide 26.7%, iron oxide 0.36%, oxide Calcium 0.01%, magnesium oxide 0.01%, potassium oxide 2.7%, sodium oxide 0.18%, titanium dioxide 0.04% and quartz 70%;

[0103] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material added is: white feldspar 4%, quartz 6%, calcite 10%, kaolin 20% %, alumina 4%, clay 18%, porcelain stone 18%, potassium feldspar 20%;

[0104] The red china...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for fabricating peony porcelain, which is calcined from basic material of china clay, raw material of glaze and chromatic china clay, wherein the chromatic china clay includes red china clay, pink china clay, yellow china clay and green china clay. The method for fabricating peony porcelain comprises the following steps: preparing a clay blank; preparing color mud;making enamel frit; making porcelain body; biscuit firing; glazing; dough molding; calcining and taking out of a kiln when temperature of the kiln falls to a value below 100 DEG C to obtain the peonyporcelain. The peony porcelain fabricated by the method of the invention can combine porcelain flowers and porcelain in the calcination process.

Description

technical field [0001] The invention relates to a method for making porcelain, in particular to a method for making ornamental flower peony porcelain. Background technique [0002] As we all know, peonies, roses, chrysanthemums, peonies and other ornamental flowers have a short flowering period, but the flowers are very bright, which can add a lot of bright spots to indoors or celebrations, but as the saying goes: "Flowers don't always bloom, youth doesn't always exist" , which means that although flowers are good, they only bloom for a limited time, and the flowering period is very short; flowers need corresponding ecological conditions to grow and open. [0003] It is known that ceramics, as a common utensil "including daily necessities such as cups, teapots, and bowls", have existed for thousands of years. In my country, pottery was invented as early as about 8000-2000 BC (Neolithic Age). . The main components of ceramic materials are silicon oxide, aluminum oxide, potas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/24
Inventor 李学武
Owner 李学武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com