High-performance polypropylene nano composite material and preparation method thereof

A nano-composite material and polypropylene technology, applied in the field of high-performance polypropylene nano-composite material, composite material preparation, polypropylene nano-composite material, can solve problems such as failure to meet product performance indicators and cost requirements, and achieve improvement The effect of forming processability, reducing production cost and improving material properties

Active Publication Date: 2014-11-05
SHANGHAI PRET COMPOSITES
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although adding a small amount of nanoparticles alone can obtain considerable performance improvement, it often fails to meet the end-use performance index and cost requirements of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polypropylene nano composite material and preparation method thereof
  • High-performance polypropylene nano composite material and preparation method thereof
  • High-performance polypropylene nano composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Weigh 30% of polypropylene by weight, 50% of organoclay Nanocor I.44P, 20% of maleic anhydride grafted polypropylene, 0.2% of Irganox 1010, 0.2% of Igrafos 168, and 0.4% of Negonox DSTP. Dry-mix in the mixer for 5 minutes, then add to the twin-screw extruder to melt and extrude to granulate. The head temperature is 200°C, the speed of the twin-screw extruder is 600 rpm, and the clay masterbatch M50 is prepared.

Embodiment 2

[0044] Take by weight 97.5% of polypropylene, the clay masterbatch M50 that embodiment 1 makes is 2%, Irganox 1010 is 0.1%, Igrafos 168 is 0.1%, Negonox DSTP is 0.3%, dry mixes 5 in high-speed mixer Minutes, then add to the twin-screw extruder to melt and extrude to granulate, wherein the temperature in the screw barrel is: 180°C in the first zone, 190°C in the second zone, 190°C in the third zone, 190°C in the fourth zone, 200°C in the head, twin-screw The extruder rotational speed was 500 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

Embodiment 3

[0046] Take by weight percentage polypropylene 75.5%, the clay masterbatch M50 that embodiment 1 makes is 14%, talcum powder 10%, Irganox 1010 is 0.1%, Igrafos 168 is 0.1%, Negonox DSTP is 0.3%, in high-speed mixing Dry mix in the container for 5 minutes, then add to the twin-screw extruder to melt and extrude to granulate. 200°C, the rotational speed of the twin-screw extruder is 500 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance polypropylene nano composite material and a preparation method thereof, and belongs to the field of polymer modification and processing. The high-performance polypropylene nano composite material comprises the components in percent by weight: 39 to 98% of polypropylene, 1 to 15% organic clay, 0 to 30% of inorganic filling material, 0.1 to 6% of compatilizer, 0 to 20% of flexibilizer, 0.2 to 2% of stabilizer, and 0 to 4% of other additive. Through the cooperative modification of nanoscale organic clay and micron-sized talcum powder to polypropylene, a nano composite material with higher rigidity, higher tenacity and other performance is obtained at a lower material density.

Description

technical field [0001] The invention relates to a polypropylene nanocomposite material, specifically a high-performance polypropylene nanocomposite material and a preparation method of the composite material, belonging to the field of polymer modification and processing. Background technique [0002] Nanocomposite materials are a new field that develops very rapidly in material science in recent years. In general, it refers to composites with at least one dimension of the dispersed phase smaller than 100 nm. The special functions of nanocomposites mainly come from the small size effect of particles and numerous interfacial recombination effects. As long as a small amount of nanoparticles are added to the polymer by melt mixing or in-situ polymerization, the polymer can be greatly improved. Excellent mechanical properties, barrier properties and flame retardant properties, and can obtain much higher heat resistance, dimensional stability and electrical conductivity than conv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L53/00C08L51/06C08L23/08C08K13/06C08K9/04C08K3/34C08K3/26C08K3/30C08J3/22B29B9/06B29C47/92B29C48/92
CPCB29C47/92B29C48/04
Inventor 张锴张鹰张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com