Method for producing copper-coated aluminum magnesium conductor wire for communication cable

A technology of copper-clad aluminum-magnesium and manufacturing methods, which is applied in the direction of cable/conductor manufacturing, metal/alloy conductors, circuits, etc., can solve the problems that the related performance cannot fully meet the functional requirements of communication cables, and the cost of raw materials is high, so as to save copper resources, The effect of reducing raw material costs and advanced technology

Inactive Publication Date: 2012-07-18
SHENZHEN SHENZHOU CABLE
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the technical problems existing in the prior art that when the pure aluminum wire is used as the inner conductor of the communication cable, its related performance cannot fully meet the functional requirements of the communication cable, and when the pure copper wire is used as the inner conductor of the communication cable, the raw material cost is too high, etc., the present invention provides A method for manufacturing copper-clad aluminum-magnesium conductor wires for communication cables

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing copper-coated aluminum magnesium conductor wire for communication cable
  • Method for producing copper-coated aluminum magnesium conductor wire for communication cable
  • Method for producing copper-coated aluminum magnesium conductor wire for communication cable

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Embodiment 1: The diameter of the raw material aluminum-magnesium core rod composed of the copper-clad aluminum-magnesium conductor wire for the communication cable is 8.60 mm ± 0.10 mm, according to the volume of the copper-clad aluminum-magnesium conductor wire for the communication cable. For the regulation of 18% to 22%, the thickness of the copper layer is selected to be 0.500mm±0.005mm, and the volume of the copper layer accounts for 19.748% of the volume of the copper-clad aluminum-magnesium conductor wire for communication cables.

Embodiment 2

[0042] Embodiment 2: the diameter of the raw material aluminum-magnesium core rod composed of copper-clad aluminum-magnesium conductor wire for the communication cable is 9.60 mm ± 0.10 mm, according to the volume of the copper layer accounting for the volume of the copper-clad aluminum-magnesium conductor wire for the communication cable For the requirement of 18% to 22%, the thickness of the copper layer is selected to be 0.560 mm ± 0.005 mm, and the volume of the copper layer accounts for 19.804% of the volume of the copper-clad aluminum-magnesium conductor wire for communication cables.

Embodiment 3

[0043] Embodiment 3: the diameter of the raw material aluminum-magnesium core rod composed of the copper-clad aluminum-magnesium conductor wire for the communication cable is 8.60 mm ± 0.10 mm, according to the volume of the copper layer accounted for the volume of the copper-clad aluminum-magnesium conductor wire for the communication cable 18% to 22%, the thickness of the copper layer is selected to be 0.520 mm ± 0.005 mm, and the volume of the copper layer accounts for 20.413% of the volume of the copper-clad aluminum-magnesium conductor wire for communication cables.

[0044] In the technical solution of the present invention, the aluminum content in the aluminum-magnesium core rod is 98.6%-98.8%, the magnesium content is 1.0%-1.4%, and the cadmium content is 0.10%-0.20%.

[0045] In the preferred technical solution of the present invention, the aluminum content in the aluminum-magnesium core rod is 98.65%, the magnesium content is 1.2%, and the cadmium content is 0.15%.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing a copper-coated aluminum magnesium conductor wire for a communication cable, which comprises an aluminum magnesium core bar and a copper layer. The aluminum magnesium core bar is coated with the copper layer evenly and concentrically, and the volume of the copper layer accounts for 18%-22% of that of the copper-coated aluminum magnesium conductor wire for the communication cable. Method for producing the copper-coated aluminum magnesium conductor wire for the communication cable comprises the steps of melting; coating and welding; and drawing and annealing. The copper-coated aluminum magnesium conductor wire for the communication cable is reasonable in structure, electric properties, mechanical properties and environmental performances can meet the technical specifications of conductors used for communication cables, transmission performances of signals, images and data are completely in conformity with the high-frequency transmission line skin effect, a copper resource is saved by using aluminum instead of copper, energy is saved, emission is reduced, and the cost of raw materials is greatly reduced.

Description

【Technical field】 [0001] The invention relates to a method for manufacturing a conductor wire, in particular to a method for manufacturing a copper-clad aluminum-magnesium conductor wire for communication cables used in the communication field. 【Background technique】 [0002] In the field of communication, communication cables usually use pure aluminum wire or pure copper wire as the inner conductor. Pure aluminum wire (density is about 2.703 kg / m3), although the cost of raw materials is relatively low, but its tensile strength, ductility, weldability and other mechanical properties, electrical properties and environmental performance cannot fully meet the needs of communication cables. application requirements; while pure copper wires can meet the application requirements of communication cables with tensile strength, elongation, weldability and other mechanical properties, electrical properties and environmental performance, but pure copper wires (density is about 8.89 kg / ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B1/02
Inventor 鲁正荣
Owner SHENZHEN SHENZHOU CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com