Preparation method of active carbon fiber phosphorous removal agent loaded with ferric oxide hydrate

A technology of activated carbon fiber and hydrated iron oxide, applied in analytical materials, scientific instruments, measuring devices, etc., can solve the problems of low phosphorus affinity, few adsorption sites, low removal rate, etc., and achieve low-cost adsorption performance, The effect of high adsorption performance and simple operation method

Inactive Publication Date: 2013-11-20
SHANGHAI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, activated carbon fiber has low affinity for phosphorus in environmental wastewater, few adsorption sites, and low removal rate. It is difficult to meet the standard for wastewater treatment only with activated carbon fiber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The concrete steps of this embodiment are:

[0022] 1. Prepare 10mL of 0.125mol / L ferric nitrate solution;

[0023] 2. Heat 40mL of deionized water to 100°C, gradually drop the ferric nitrate solution in a until the solution turns brown. Remove the beaker, stop heating, and obtain 0.025mol / L ferric hydroxide colloidal solution after cooling.

[0024] Reaction equation: Fe(NO 3 ) 3 +3H 2 O → Fe(OH) 3 (colloid)+3HNO 3 ;

[0025] 3. Cut the activated carbon fibers into 0.4-0.6cm cubes, wash with water for several times, soak in deionized water, filter and dry;

[0026] 4. Weigh 0.5 g of the activated carbon fiber obtained in step c, add it into the sol solution obtained in step b, and let it stand for impregnation;

[0027] 5. Dry the solid obtained in step d at a drying temperature of 105°C. After the drying is complete, cool to room temperature to obtain the phosphorus-removing adsorbent.

Embodiment 2

[0029] The concrete steps of this embodiment are:

[0030] 1. Prepare 10mL of 0.25mol / L ferric nitrate solution;

[0031] 2. Heat 40mL of deionized water to 100°C, gradually drop the ferric nitrate solution in a until the solution turns brown. Remove the beaker, stop heating, and obtain 0.05mol / L ferric hydroxide colloidal solution after cooling.

[0032] Reaction equation: Fe(NO 3 ) 3 +3H 2 O → Fe(OH) 3 (colloid)+3HNO 3 ;

[0033] 3. Cut the activated carbon fibers into 0.4-0.6cm cubes, wash with water for several times, soak in deionized water, filter and dry;

[0034] 4. Weigh 0.5 g of the activated carbon fiber obtained in step c, add it into the sol solution obtained in step b, and let it stand for impregnation;

[0035] 5. Dry the solid obtained in step d at a drying temperature of 105°C. After the drying is complete, cool to room temperature to obtain the phosphorus-removing adsorbent.

Embodiment 3

[0037] The concrete steps of this embodiment are:

[0038] 1. Prepare 10mL of 0.5mol / L ferric nitrate solution;

[0039] 2. Heat 40mL of deionized water to 100°C, gradually drop the ferric nitrate solution in a until the solution turns brown. Remove the beaker, stop heating, and obtain 0.1mol / L ferric hydroxide colloidal solution after cooling.

[0040] Reaction equation: Fe(NO 3 ) 3 +3H 2 O → Fe(OH) 3 (colloid)+3HNO 3 ;

[0041] 3. Cut the activated carbon fibers into 0.4-0.6cm cubes, wash with water for several times, soak in deionized water, filter and dry;

[0042] 4. Weigh 0.5 g of the activated carbon fiber obtained in step c, add it into the sol solution obtained in step b, and let it stand for impregnation;

[0043] 5. Dry the solid obtained in step d at a drying temperature of 105°C. After the drying is complete, cool to room temperature to obtain the phosphorus-removing adsorbent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of an active carbon fiber phosphorous removal agent loaded with ferric oxide hydrate, belonging to the technical field of preparation process of phosphorous adsorption removal agents. The preparation method in the invention has the characteristics of being short in preparation time, simple in steps, simple and practicable in operation and the like; and the obtained composite adsorbent has the advantages of being uniform in fiber surface load, large in load capability, excellent in adsorption performance, low in preparation cost and the like.

Description

Technical field [0001] The present invention involves a composite phosphorus removal method, which is the field of adsorption of phosphorus removal preparation process.That is, a solid gel preparation method that loads the activated carbon fiber with a hydrolysis iron oxide. Background technique [0002] At present, water pollution problems spread throughout the world, especially near cities and industrial areas. Water pollution is particularly serious. Even developed countries still fail to completely solve the problem of water pollution. Another problem in the world is the shortage of water resources.To a certain extent, the development of the regional economy has been restricted.With the rapid development of industries and the continuous improvement of rural urbanization, water supply tightness and sewage purification will become one of the main problems facing my country and even around the world.With the increasing number of human beings of the development and utilization of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/32
Inventor 张玲刘建勇周奇万里华刘凡清
Owner SHANGHAI UNIV