Transparent polyurethane elastomer and preparation method as well as application

A polyurethane elastomer and polyurethane elasticity technology, which is applied in the polyether polyurethane elastomer material and preparation, and the application field of cleaning scrapers, can solve the problems of high tensile strength, low rebound temperature dependence, high transparency, etc., and achieve high Transparency, good comprehensive mechanical properties, solve the effect of not easy transparency

Active Publication Date: 2012-07-25
GUANGDONG LEPUTAI NEW MATERIAL TECH
View PDF8 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the printer cleaning blade synthesized in the above materials can only meet the mechanical properties, or meet the individual mechanical properties under the condition of satisfying the optical properties, and cannot simultaneously meet the requirements of high transparency, high impact resilience, and high tensile strength under the conditions of satisfying the optical properties. Mechanical properties such as tensile strength, high tear strength and low temperature dependence of rebound

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent polyurethane elastomer and preparation method as well as application
  • Transparent polyurethane elastomer and preparation method as well as application
  • Transparent polyurethane elastomer and preparation method as well as application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The above-mentioned transparent polyurethane elastomer preparation method comprises the following steps:

[0036] (1) Preparation of isocyanate prepolymer:

[0037] Adding 30-60% diphenylmethane diisocyanate and 40-70% polytetrahydrofuran polyol to the reaction kettle in sequence, stirring evenly, heating and reacting to obtain an isocyanate prepolymer with an isocyanate content of 10-18%;

[0038] (2) Preparation of polyol polymer:

[0039] Add 20-70% polytetrahydrofuran polyol and 30-80% small molecule diol chain extender into the reaction kettle in sequence, stir at a set speed, and dehydrate under a certain temperature and pressure to obtain polyol polymerization thing;

[0040] (3) Preparation of transparent polyurethane elastomer:

[0041] Mix 60-90% of the isocyanate prepolymer and 10-40% polyol polymer prepared in step (1) and step (2) evenly, defoam, then pour into a mold and cool to obtain a hardness of 65-85 Asker A. Transparent polyurethane with tensile ...

Embodiment 1

[0049] (1) Preparation of isocyanate prepolymer:

[0050] Add 42.90g of diphenylmethane diisocyanate (containing 95% of 4,4 and 5% of 2,4) and 57.10g of polytetrahydrofuran polyol (molecular weight 2000) in the reaction kettle and stir evenly (stirring speed is 150 ~300rpm), the temperature was raised to 80°C, and the reaction was carried out for 1.5h to obtain a prepolymer with an isocyanate content of 12%.

[0051] (2) Polyol polymer preparation:

[0052] Add 29.40g of polytetrahydrofuran polyol (molecular weight: 2000), 63.2g of 1,6-hexanediol and 37.9g ​​of diethylene glycol successively into the reaction kettle, stir (stirring speed is 200~300rpm) and mix uniformly, heat up to 100 ~120°C, start the vacuum device, control the internal pressure of the reactor at -0.095MPa ~ -0.098MPa, dehydration reaction for about 2h, to obtain polyol polymer.

[0053] (3) Cleaning scraper preparation process:

[0054] Preheat the isocyanate prepolymer and polyol polymer prepared in ste...

Embodiment 2

[0057] (1) Preparation of isocyanate prepolymer:

[0058] Add 58.80g diphenylmethane diisocyanate (containing 95% 4,4 body and 5% 2,4 body) and 41.20g polytetrahydrofuran polyol (molecular weight 1000) in the reaction kettle successively and stir evenly (stirring speed is 150 ~300rpm), the temperature was raised to 80°C, and the reaction was carried out for 1.5h to obtain a prepolymer with an isocyanate content of 18%.

[0059] (2) Polyol polymer preparation:

[0060] together with the examples.

[0061] (3) Cleaning scraper preparation process:

[0062] Preheat the isocyanate prepolymer and polyol polymer prepared in steps (1) and (2) to 80°C and mix and stir in a weight ratio of 60:40 (stirring speed 200-300rpm), vacuum defoaming, pour 130 After about 1 hour of vulcanization in the mold at ℃, demould, and secondary curing in an oven at 100 ℃ for more than 4 hours.

[0063] The prepared cleaning blade has excellent optical and mechanical properties, see Table 1 for detail...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a transparent polyurethane elastomer, which contains the following components in percentage by weight: 60-90 percent of structurally symmetric cyanate ester prepolymer and 10-40 percent of chain extender, wherein the structurally symmetric cyanate ester prepolymer is obtained by reacting 30-60 percent of isocyanate or a derivative thereof and 40-70 percent of polyol polymer; and the chain extender is obtained by mixing 20-70 percent of polyol polymer and 30-80 percent of small molecular glycol type chain extender. The invention also provides a preparation method of the transparent polyurethane elastomer. The polyurethane elastomer prepared by the invention is colorless and transparent, the hardness is 65-85 Asker A, the tensile strength is greater than 30 MPa, the fracture productivity is greater than 400 percent, the tear strength is greater than 50 kN / m, the resilience rate is greater than 50 percent, the resilience temperature dependency is less than 30 percent, and the permanent deformation at definite elongation is less than 3 percent. The transparent polyurethane elastomer is mainly used for cleaning scrapers in a printer or other electronic photographic equipment.

Description

【Technical field】 [0001] The invention relates to the field of materials for printers, in particular to a polyether polyurethane (urethane) elastomer material, a preparation method and the application of the material to cleaning blades in printers and other electrophotographic equipment. 【Background technique】 [0002] see figure 2 , In the working process of printers and other electrophotographic equipment, in order to repeatedly use the electrophotographic photoreceptor or transfer, etc., a cleaning blade is usually used to remove the toner on the toner image carrier. Since this cleaning blade needs to be pressed on the surface of the toner drum for a long time to work, the cleaning blade has the following basic requirements: colorless and transparent, good tensile tearing performance and good wear resistance. The use of polyurethane as a cleaning blade is due to the good wear resistance of polyurethane. However, polyurethanes with better tensile tear properties are gene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G18/76C08G18/66C08G18/48C08G18/32C08G18/10C08L75/08
Inventor 孙变张海清韩昌哲
Owner GUANGDONG LEPUTAI NEW MATERIAL TECH