Manufacture method for staining resistant artificial quartz stone

A technology of artificial quartz stone and manufacturing method, which is applied in the field of stain-resistant artificial quartz stone, which can solve the problems of poor stain resistance and easy pollution on the surface of artificial quartz stone, and achieve increased gloss, easy operation, and strong stain resistance The effect of the characteristic

Inactive Publication Date: 2012-08-22
BENYEE NEW MATERIAL CO
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] After ordinary artificial quartz stone is processed into finished products, it is directly polished and polished withou

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for manufacturing a stain-resistant artificial quartz stone, comprising the following steps:

[0028] 1) Surface modification of the raw material quartz silt: mix the raw material of quartz silt with the dispersion medium at a mass ratio of 100:0.5, and use a stirring ball mill to activate the surface of the modified quartz silt; the raw material of the quartz sand is 20-40 mesh quartz Sand 23%, 40-70 mesh quartz sand 37%, 70-100 mesh 40%; 400 quartz powder is 48.6% of the total mass of quartz sand;

[0029] 2) Mixing and pressing: Mix the above-mentioned surface-treated quartz stone silt with m-phenylene unsaturated polyester resin and curing agent according to the mass percentage of quartz stone silt 92%, m-benzene unsaturated polyester resin 7.3%, and curing agent 0.7% After uniformity, pressurize for 120 seconds under the action of a 100-ton exciting force of a press to form an artificial quartz slab;

[0030] 3) Glue curing: mix water-based nano-silica ge...

Embodiment 2

[0032] A method for manufacturing a stain-resistant artificial quartz stone, comprising the following steps:

[0033] 1) Surface modification of the raw material quartz silt: mix the raw material of quartz silt with the dispersion medium at a mass ratio of 100:0.2, and use a stirring ball mill to activate the surface of the modified quartz silt; the raw material of the quartz sand is 20-40 mesh quartz Sand 20%, 40-70 mesh quartz sand 45%, 70-100 mesh 35%; 400 quartz powder is 42% of the total mass of quartz sand;

[0034] 2) Mixing and pressing: Mix the above-mentioned surface-treated quartz stone silt with m-phenylene unsaturated polyester resin and curing agent according to the mass percentage of quartz stone silt 90%, m-benzene unsaturated polyester resin 9.2%, and curing agent 0.8% After uniformity, pressurize for 150 seconds under the action of a 100-ton exciting force of a press to form an artificial quartz slab;

[0035] 3) Glue curing: mix water-based nano-silica gel,...

Embodiment 3

[0037] A method for manufacturing a stain-resistant artificial quartz stone, comprising the following steps:

[0038] 1) Surface modification of the raw material quartz silt: mix the raw material of quartz silt with the dispersion medium at a mass ratio of 100:0.5, and use a stirring ball mill to activate the surface of the modified quartz silt; the raw material of the quartz sand is 20-40 mesh quartz 18% sand, 35% quartz sand of 40-70 mesh, 47% of 70-100 mesh; 400 quartz parts account for 50% of the total mass of quartz sand;

[0039] 2) Mixing and pressing: Mix the above-mentioned surface-treated quartz stone silt with m-phenylene unsaturated polyester resin and curing agent according to the mass percentage of quartz stone silt 91%, m-benzene unsaturated polyester 8%, and curing agent 1% Finally, under the action of 100 tons of exciting force of the press, pressurize for 150 seconds to press and form, and obtain the artificial quartz slab;

[0040] 3) Glue curing: mix water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention particularly relates to a manufacture method for a staining resistant artificial quartz stone, which includes the steps of quartz stone powder sand surface modification, mixed pressing, sizing and solidifying and the like to generate a transparent film on the surface of the artificial quartz stone. The manufacture method has the advantages that by means of mechanical activation and modification of quartz stone powder sand serving as raw materials of the artificial quartz stone, flowability of the quartz stone powder sand during pressing is enhanced so that the quartz stone powder sand tends to be accumulated orderly and most densely, and binding of the quartz stone powder sand and resin during solidification is enhanced; the proportion and the grain distribution range are strictly controlled in an artificial quartz stone formula so that micron-sized pore quantity on the surface of the artificial quartz stone is decreased maximally; the surface of the artificial quartz stone is filled to form chemical adsorption so as to improve glossiness of the surface of the artificial quartz stone; and the micron-sized film formed on the surface of the artificial quartz stone has the hydrophobic feature, oil stains within 24 hours can be cleaned by wet cotton cloth, and hidden dirt and bleeding are effectively prevented, therefore, the artificial quartz stone is high in staining resistance. The manufacture method is simple in process, easy in operation and short in consumed time.

Description

[0001] technical field [0002] The invention relates to a method for manufacturing a stain-resistant artificial quartz stone, in particular to a method for manufacturing a stain-resistant artificial quartz stone. [0003] Background technique [0004] Artificial quartz stone (or diamond / diamond) originated in Spain. It was called Celite when it entered China in 2005. When artificial quartz stone was recognized by more and more consumers, in 2006, some people in China began to develop artificial quartz stone. Quartz stone, in 2007, many manufacturers have launched domestic artificial quartz stone. [0005] At present, artificial quartz stone is composed of about 90% natural quartz and about 10% additives such as colorants, resins and curing agents. It is formed by negative pressure vacuum, high-frequency vibration, heating and curing (the temperature depends on the type of curing agent); its texture is hard (Mohs hardness 5-7), and the structure is dense (density 2.3-2.5g / ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/18C04B41/65C04B14/06
Inventor 范美意梁成
Owner BENYEE NEW MATERIAL CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap