Hydrogenation active protective agent with alkaline earth metal-containing alumina as carrier, preparation and application

A technology for hydrogenation activity protection and hydrogenation activity, applied in metal/metal oxide/metal hydroxide catalysts, physical/chemical process catalysts, chemical instruments and methods, etc., can solve problems such as deactivation of downstream catalysts

Active Publication Date: 2015-07-29
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Residual oil contains a large amount of metal impurities such as Ni, V, Fe, Ca and solid impurities. If these impurities cannot be effectively removed, it will have an adverse effect on the downstream hydrogenation catalyst and easily deactivate the downstream catalyst.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogenation active protective agent with alkaline earth metal-containing alumina as carrier, preparation and application
  • Hydrogenation active protective agent with alkaline earth metal-containing alumina as carrier, preparation and application
  • Hydrogenation active protective agent with alkaline earth metal-containing alumina as carrier, preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Take by weighing the dry rubber powder (dry basis is 73% that Changling Refinery Catalyst Factory produces, and wherein pseudo-boehmite content is 68%, and gibbsite content is 5 weight %, and surplus is amorphous alumina) 1000 Gram,, 30 grams of Tianjing powder (product of Henan Lankao Tianjing Rubber Factory), 30g of hydroxymethyl cellulose are mixed, then add 1200 milliliters of aqueous solutions containing 7g of magnesium nitrate, and extrude into an outer diameter of 2.5mm on a plunger type extruder , a Raschig ring strip with an inner diameter of 1.0mm. The wet strip was dried at 120°C for 4 hours and calcined at 960°C for 3 hours to obtain carrier Z1. The physical and chemical properties of carrier Z1 are shown in Table 1.

[0038] Table 1

[0039] carrier number

Embodiment 2

[0042] Get the carrier Z1200 grams that embodiment 1 prepares, use 500 milliliters to contain V 2 o 5 50 g / L, NiO14 g / L mixed solution of ammonium metavanadate and nickel nitrate was impregnated for 1 hour, filtered, dried at 120°C for 4 hours, and calcined at 400°C for 3 hours to obtain protective agent C1. The composition of protective agent C1 is listed in Table 2.

Embodiment 3

[0046] Get the carrier Z1200 grams that embodiment 1 prepares, use 500 milliliters to contain V 2 o 5 18 g / L, NiO 28 g / L mixed solution of ammonium metavanadate and nickel nitrate was impregnated for 1 hour, filtered, dried at 120°C for 4 hours, and calcined at 400°C for 3 hours to obtain protective agent C2. The composition of protectant C2 is listed in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hydrogenated active protective agent taking alumina containing alkali earth metals as a carrier, as well as the preparation and the application of hydrogenated active protective agent. The hydrogenated active protective agent comprises an alumina carrier containing alkali earth metals and hydrogenated active metallic component loaded on the carrier, and is characterized in that the hydrogenated active metallic component is at least one metallic component chosen from VIII group and at least one metallic component combination chosen from VB group, in percentage by weight, the content of the VIII group metallic component is 0.2 to 15%, and the content of the VB group metallic component is also 0.2 to 15% on basis of oxide and by taking the protective agent as standard. Compared with the hydrogenated protective agent provided in the prior art, the hydrogenated active protective agent provided by the invention has good hydrodemetallization activity.

Description

technical field [0001] The invention relates to a hydrogenation active protective agent, its preparation and application. Background technique [0002] As crude oil becomes heavier and inferior, the difficulty of crude oil processing increases, and the yield of light oil products decreases. However, the market demand for high-quality light oil products continues to increase, and environmental protection regulations are becoming more and more inclusive. strict. At present, the processing and full utilization of heavy oil, especially residual oil, is becoming a major topic of concern in the global oil refining industry, and residual oil hydrogenation technology is a widely used processing technology in heavy oil processing technology, and is recognized as an economical and environmentally friendly deep processing technology . Residual oil contains a large amount of metal impurities such as Ni, V, Fe, Ca and solid impurities. If these impurities cannot be effectively removed,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/847B01J27/195B01J27/198C10G45/04C10G45/06
Inventor 贾燕子杨清河聂红李丁健一孙淑玲胡大为李大东
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com