Semitransparent plant culturing glue and preparation method thereof

A translucent, plant-based technology, applied in the direction of fertilizer mixtures, fertilizer forms, fertilization devices, etc., can solve the problems of short service life, poor transparency, excessive plant growth speed, etc., and achieve good decorative effects

Inactive Publication Date: 2012-09-19
浦江县富盛塑胶新材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing ornamental plant culture glue is made of industrial plastic as the main material, adding various softeners and industrial emulsifiers. This kind of plant culture glue is not only poor in transparency, but also poisonous and harmful, and the germination rate is low. Generally, the germination rate is between Between 25 and 40%, and the plants grow too fast, the leaves of the plants turn yellow and cau

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of translucent plant culture glue is made of the following components according to weight percentage:

[0043] Carrageenan: 20%;

[0044] Water: 47%;

[0045] Boric acid powder: 1.5%;

[0046] Sodium nitrate: 0.5%;

[0047] Potassium sulfate: 0.8%;

[0048] Magnesium sulfate: 7%;

[0049] Ammonium sulfate: 2%;

[0050] Copper sulfate: 2.7%;

[0051] Zinc sulfate: 2.5%;

[0052] Ammonium dihydrogen phosphate: 3.5%;

[0053] Superphosphate: 10%;

[0054] Carboresin: 2%;

[0055] Sodium propionate: 0.5%;

[0056] The preparation method of translucent plant culture glue comprises the following steps:

[0057] (1) Mix boric acid powder, sodium nitrate, potassium sulfate, magnesium sulfate, ammonium sulfate, copper sulfate, zinc sulfate, ammonium dihydrogen phosphate, and superphosphate in water and heat to 40-50°C, stir to dissolve, and obtain blue water solution;

[0058] (2) Pour water, carrageenan, carbo resin and sodium propionate into the emulsificat...

Embodiment 2

[0062] A kind of culture glue is made of the following components according to weight percentage:

[0063] Carrageenan: 18%;

[0064] Water: 46%;

[0065] Boric acid powder: 1%;

[0066] Sodium nitrate: 0.6%;

[0067] Potassium sulfate: 0.7%;

[0068] Magnesium sulfate: 7.3%;

[0069] Ammonium sulfate: 2.7%;

[0070] Copper sulfate: 3%;

[0071] Zinc sulfate: 2.6%;

[0072] Ammonium dihydrogen phosphate: 4.8%;

[0073] Superphosphate: 12%;

[0074] Carboresin: 1%;

[0075] Sodium propionate: 0.3%;

[0076] The translucent plant culture glue prepared in Example 1 has a transparency of 51% and a service life of 7-8 months.

Embodiment 3

[0078] A kind of culture glue is made of the following components according to weight percentage:

[0079] Carrageenan: 22%;

[0080] Water: 45%;

[0081] Boric acid powder: 2.5%;

[0082] Sodium nitrate: 0.8%;

[0083] Potassium sulfate: 0.8%;

[0084] Magnesium sulfate: 7.3%;

[0085] Ammonium sulfate: 2.4%;

[0086] Copper sulfate: 3%;

[0087] Zinc sulfate: 3.8%;

[0088] Ammonium dihydrogen phosphate: 5%;

[0089] Calcium superphosphate: 6%;

[0090] Carboresin: 1%;

[0091] Sodium propionate: 0.4%;

[0092] The translucent plant culture glue prepared in Example 1 has a transparency of 45% and a service life of 7-8 months.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a semitransparent plant culturing glue and a preparation method thereof. The invention provides the semitransparent plant culturing glue for culturing germination and growth of various phaseolus plants. The preparation method of the semitransparent plant culturing glue comprises the following steps of: mixing, stirring, dissolving, emulsifying and glue-making carrageenan,water, boric acid powder, sodium nitrate, potassium sulfate, ammonium sulfate, copper sulfate, zinc sulfate, ammonium dihydrogen phosphate, calcium superphosphate, Carbomer resin and sodium propionate. The semitransparent plant culturing glue has the advantages of freeness from toxicity and harmness, transparency of 45-65% and service life of 5-8 months; besides, phaseolus plants, cultured by using the semitransparent plant culturing glue, germinate slowly, so that the whole process of slow germination of plants can be clearly and directly observed without watering and fertilizing; and the semitransparent plant culturing glue has a good decorative effect as a decorative material in decorative parts.

Description

technical field [0001] The invention relates to a plant culture glue and a preparation method thereof, in particular to an ornamental plant culture glue for cultivating the germination and growth of Bean plants and a preparation method thereof. Background technique [0002] There are two types of plant culture glue, one is purely plant culture glue, and the other is culture glue for plant cultivation and indoor ornamental use. This kind of plant culture glue is generally translucent and placed in a transparent container inside as a decoration. The existing ornamental plant culture glue is made of industrial plastic as the main material, adding various softeners and industrial emulsifiers. This kind of plant culture glue is not only poor in transparency, but also poisonous and harmful, and the germination rate is low. Generally, the germination rate is between Between 25 and 40%, and the plants grow too fast, the leaves of the plants turn yellow and cause the plants to die q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C05G3/00C05G5/00
Inventor 杜京财
Owner 浦江县富盛塑胶新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap