Preparation method of water-absorbable material by crofton weed

A kind of violet zebra, water-absorbing technology, applied in fiber raw material processing, textile and papermaking, etc., to achieve the effect of improving the ability of graft copolymerization

Inactive Publication Date: 2012-09-19
KUNMING UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with starch-based superabsorbent resins, there are relatively few studies on water-absorbent materials of natural plant tissue cells, and the research on water-absorbent resins based on Eupatorium adenophorum fiber is still a blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-absorbable material by crofton weed
  • Preparation method of water-absorbable material by crofton weed

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0025] Embodiment 1: the preparation method of the water-absorbing material of Erythrina japonica, the specific operation is as follows:

[0026] (1) The material preparation process of Erythrina japonica

[0027] The whole plant of Rhizoma chinensis is air-dried, and the air-dried plants with a moisture content of 15% are subjected to mechanical grinding treatment, and then they are screened by a 100-mesh sieve to be the qualified raw material of Rhododendron chinensis granules;

[0028] (2) Diethyl ether extraction treatment of the raw material of Zijianzelan granules

[0029] Weigh 5g of the raw material of E. japonica granules, wrap it with qualitative filter paper, tie it with cotton thread, put it into a 250ml Soxhlet extractor, add 250ml of analytical pure ether, install a condenser, connect the extraction instrument, as for the water bath In the pot, turn on the cooling water, adjust the heater of the water bath to make the ether boiling rate be 5 times per hour in th...

Embodiment 2

[0039] Example 2: The preparation method of the water-absorbing material of Echinacea, the specific operations are as follows:

[0040] (1) The material preparation process of Erythrina japonica

[0041] The whole plant of A. japonica is air-dried, and the air-dried plants with a moisture content of 7% are subjected to mechanical grinding treatment, and then sieved through a 300-mesh sieve to obtain a qualified raw material of E. japonica granules;

[0042] (2) The extraction process and method of ether from the raw material of Zijianzelan granules

[0043] Weigh 10g of qualified raw materials of E. japonica granules, wrap them with qualitative filter paper, tie them with cotton threads, put them into a 500ml Soxhlet extractor, add 500ml of analytical pure ether, install a condenser, and connect to the extraction instrument. , As for the water bath, turn on the cooling water, adjust the heater of the water bath to make the ether boiling rate be 4 times per hour in the Soxhle...

Embodiment 3

[0051] Example 3: The preparation method of the water-absorbing material of Echinacea, the specific operations are as follows:

[0052] (1) The material preparation process of Erythrina japonica

[0053] The whole plant of A. japonica is air-dried, and the air-dried plants with a moisture content of 12% are subjected to a mechanical grinding treatment, and then screened by a 400-mesh sieve to obtain a qualified raw material of E. japonica granules;

[0054] (2) The extraction process and method of ether from the raw material of Zijianzelan granules

[0055] Weigh 20g of qualified raw material of E. japonica granules, wrap it with qualitative filter paper, tie it with cotton thread, put it into a 1000ml Soxhlet extractor, add about 1000ml of analytical pure ether, install a condenser, and connect the extraction As for the instrument, as for the water bath, turn on the cooling water, adjust the heater of the water bath to make the ether boiling rate 3 times per hour in the So...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of water-absorbable material by harmful invasive species, i.e. crofton weed, which comprises the following steps of: carrying our air drying on the whole plant of crofton weed and grinding, extracting with diethyl ether after screening, removing hydrophobic poison components from particle raw materials, carrying out graft copolymerization synthesis on the extracted crofton weed particle-shaped raw material by an aqueous solution polymerization method, precipitating a graft copolymerization synthetic with absolute methanol, dispersing and washing, carrying out freeze drying, grinding, carrying out freeze drying again, and sealing, to obtain crofton weed water-absorbable resin; the water-absorbable material prepared by the method has the distilled water absorbing multiplying power of 930g / g highest, and the distilled water absorbing speed of 20min; the 0.9% sodium chloride water solution absorbing rate can reach to 320g / g highest, and the 0.9% sodium chloride water solution absorbing rate is 40min; and the preparation method is applicable to the soil conditioner water and the cultivation agent in the aspects of the agriculture, the forestry and the horticulture, and the desiccating agent and the dehydrating agent in the aspect of the industry.

Description

technical field [0001] The invention relates to a method for manufacturing a water-absorbing material by utilizing a harmful invasive species-Eupatorium adenophorum, and belongs to the technical field of natural polymer materials. Background technique [0002] Eupatorium adenophorum (Eupatorium adenophorum Spreng) belongs to the genus Eupatorium adenophorum in the family Asteraceae. It is named Eupatorium adenophorum because of its purple stem and petiole. The plant of Eupatorium adenophorum becomes lignified after 1.5 days of growth. It is a perennial, clustered semi-shrub plant with a height of 1.0-1.5 meters and a maximum height of about 3 meters. Eupatorium adenophorum is a harmful weed introduced from Southeast Asia to China in the 1950s. It is widely distributed in Yunnan, Guizhou, Sichuan, Guangxi, Tibet and other places. It is currently spreading to central and eastern China at a rate of about 60 hectares per year. Regional sprawl. In recent years, due to large-sca...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F291/00C08F251/02C08F289/00D21C5/00C08H7/00
Inventor 高欣张恒宁选起悉龙米小倩蔡云敏
Owner KUNMING UNIV OF SCI & TECH