Polypropylene filling master batch

A technology of filling masterbatch and polypropylene, which is applied in the field of materials, can solve problems such as easy delamination and difficult dispersion of inorganic fillers, and achieve the effects of increasing surface gloss, reasonable formula, and improving dimensional stability

Inactive Publication Date: 2012-09-19
青阳县红远塑业有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to alleviate the deficiencies and defects of the prior art, the purpose of the present invention is to provide a polypropylene filler masterbatch. The formulation of the present invention is reasonable, and solves the problems of difficult dispersion and easy layering of inorganic fillers. It not only has the advantages of easy dispersion and high efficiency Advantages, but also play a role in toughening, strengthening, improving dimensional stability and increasing surface gloss of polypropylene resin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: polypropylene filling masterbatch, the weight portion of its composition raw material is: polypropylene 12-20kg, stearic acid 1kg, antioxidant 0.3kg, coupling agent 1kg, paraffin 3-5kg, stone powder 100kg, polyethylene Wax 2-3kg and whitening agent 0.1kg.

[0013] Preparation method: Weigh each raw material according to the weight of the constituent raw materials, first mix it with a high-temperature mixer for 15 minutes at a temperature of 130 degrees, and then extrude and granulate it with a twin-screw extruder.

[0014] The performance detection of the polypropylene filler masterbatch that the present invention makes:

[0015] Polypropylene filler masterbatch of the present invention Tensile strength (Mpa) 36 Elongation at break (%) 583 Bending strength (Mpa) 25.56 Impact strength 7.4 Melting temperature (°C) 178 melt finger 23.5g / 10min Moisture and volatile content ≤0.3%

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polypropylene filling master batch, which consists of the following raw materials in parts by weight: 12-20 parts of polypropylene, 1 part of stearic acid, 0.3 part of an antioxidant, 1 part of a coupling agent, 3-5 parts of paraffin, 100 parts of stone dust, 2-3 parts of polyethylene wax and 0.1 part of a brightening agent, and is prepared by the following steps of: mixing by using a high-temperature mixing machine for 15 minutes at the temperature of 130 DEG C; and extruding and granulating with a double-screw extruder. The polypropylene filling master batch has a reasonable formula, contributes to solving the problems of difficulty in dispersing an inorganic filler, easiness in dispersing and the like, has the advantages of easiness in dispersing and high efficiency, and plays a role in toughening and enhancing a polypropylene resin, improving size stability and increasing surface gloss.

Description

technical field [0001] The invention relates to a polypropylene filler masterbatch, which belongs to the field of materials. Background technique [0002] Polypropylene resin is currently one of the most widely used general-purpose plastics. The method of polypropylene modification is usually to fill with inorganic fillers during processing, such as talcum powder, calcium carbonate, and hollow glass microspheres. [0003] Calcium carbonate is the most widely used, most convenient and cheap filler in the plastic and rubber industry. Filling plastic products with calcium carbonate can reduce costs, save raw materials, and improve molding processing performance. Talc powder is a unique natural mineral with scales. structure, has many excellent physical and chemical properties, such as flexibility, whiteness, hydrophobicity, chemical inertness, etc., and the price of talc powder is also relatively cheap. It is widely used in the plastic processing industry; glass microspher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K13/02C08K3/34C08K5/09C08K5/01C08J3/22
Inventor 高红兵
Owner 青阳县红远塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap