Preparation method and applications of electrode plate

A technology of electrode sheet and conductive agent, applied in the field of electronics, can solve the problems of easy breakage and brittleness of the electrode sheet, and achieve the effects of improving flexibility, improving liquid absorption and excellent conduction effect.

Active Publication Date: 2012-11-21
SHENZHEN ZHENHUA FU ELECTRONICS
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the embodiment of the present invention provides a method for preparing an electrode sheet, which solves the technical problem of high brittleness and easy fracture of the electrode sheet in the prior art; and, the application of the prepared electrode sheet in a supercapacitor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and applications of electrode plate
  • Preparation method and applications of electrode plate
  • Preparation method and applications of electrode plate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] see figure 1 , figure 1 A flow chart showing a method for preparing an electrode sheet according to an embodiment of the present invention includes the following steps:

[0023] S01, respectively provide activated carbon, conductive agent, carboxymethyl cellulose and binder, the mass percentage of the activated carbon is 60-80%, the mass percentage of conductive agent is 10-30%, carboxymethyl cellulose The mass percentage of the binder is 0.5-5%, and the mass percentage of the binder is 5-10%;

[0024] S02, mixing activated carbon, conductive agent and carboxymethyl cellulose to obtain the first mixture;

[0025] S03, mixing the binder and water to obtain a second mixture;

[0026] S04, under the stirring condition, mix the first mixture and the second mixture, let stand for 2-8 hours, dry, and press to form an electrode sheet.

[0027] Specifically, in step S01, the activated carbon is in the form of powder, the particle size is 0.5-10 μm, and the mass percentage o...

Embodiment 1

[0038] The gac that mass percentage composition is 65% is provided respectively, and mass percentage composition is 24.5% conductive agent, and mass percentage composition is 0.5% carboxymethyl cellulose, and mass percentage composition is 10% binding agent (total amount 50g);

[0039] The activated carbon, conductive agent and carboxymethyl cellulose were added to the stirrer and stirred for 2 hours to obtain the first mixture;

[0040] The adhesive was added into 100g of water, and stirred for 1.5h to obtain the second mixture;

[0041] Add the second mixture to the mixer, stir for 2 hours, and then stand for emulsification for 2 hours; put it in a blast drying oven and dry it at 100°C for 6 hours to obtain the electrode sheet precursor; use the electrode sheet precursor with a pair of rollers The electrode sheet is formed by machine pressing, and the thickness of the electrode sheet is 0.4mm.

[0042] Preparation of supercapacitors:

[0043] Put the electrode sheet and d...

Embodiment 2

[0046] The gac that mass percentage composition is 75% is provided respectively, and mass percentage composition is 15% conductive agent, and mass percentage composition is 5% carboxymethyl cellulose, and mass percentage composition is 5% binding agent (total amount 50g);

[0047] The activated carbon, conductive agent and carboxymethyl cellulose were added to the stirrer and stirred for 2.5 hours to obtain the first mixture;

[0048] The adhesive was added into 200g of water, and stirred for 1h to obtain the second mixture;

[0049]Add the second mixture to the mixer, stir for 2.5 hours, and then stand for emulsification for 4 hours; put it in a blast drying oven and dry it at 100°C for 8 hours to obtain the electrode sheet precursor; use the electrode sheet precursor The electrode sheet is formed by machine pressing, and the thickness of the electrode sheet is 0.4mm.

[0050] Preparation of supercapacitors:

[0051] Put the electrode sheet and diaphragm into the stainless...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
internal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention is suitable for the technical field of electronics and provides a preparation method and applications of an electrode plate. The preparation method of the electrode plate comprises the following steps: respectively providing active carbon, a conductive additive, carboxymethylcellulose and a binder; mixing the active carbon, the conductive additive and the carboxymethylcellulose to obtain a first mixture; mixing the binder with water to obtain a second mixture; under an agitating condition, mixing the first mixture with the second mixture, standing the mixtures for 2-8 hours, and drying, pressing and molding the electrode plate. According to the preparation method of the electrode plate, the carboxymethylcellulose (CMC) can enable the mixed size to form stable rubber mass by adding the carboxymethylcellulose, standing and emulsifying the carboxymethylcellulose; layering of the mixed size caused by different specific gravities of each constituent can be prevented; the distribution stability of each constituent in the size is kept, and the flexibility, the tensile strength, the absorbency and the electrical conductivity of the prepared electrode plate are also improved.

Description

technical field [0001] The invention belongs to the field of electronic technology, and in particular relates to a preparation method and application of an electrode sheet. Background technique [0002] Supercapacitor is a new type of electronic component, which fills the gap between ordinary capacitors and batteries, and has the characteristics of high capacity, high power, safety, and no pollution. Supercapacitor is a breakthrough component to improve and solve the application of electric energy power performance. It has huge application value and market potential in electric vehicles, diesel locomotive starting, electric power, transportation, communication, consumer electronics, aerospace, military fields, etc., and is favored by the world States attach great importance to it. [0003] The production process of button supercapacitors is the most important step in the manufacturing process of supercapacitors. The quality of the electrode sheets directly affects important...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G9/04
CPCY02E60/13
Inventor 邓梅根丁晓鸿李建辉陈英放
Owner SHENZHEN ZHENHUA FU ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com