Sensing and heating method of high-magnetic induction oriented silicon steel

A high magnetic induction orientation and induction heating technology, applied in the field of steel rolling heating, can solve problems such as low performance stability of finished products, low slab temperature control accuracy, abnormal disturbances, etc., to increase investment and production costs and control effects. Significant and guaranteed heating effect

Active Publication Date: 2014-03-19
BEIJING SHOUGANG CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, most of the electromagnetic induction heating furnace equipment used in industrial production in the world is provided by Japanese complete sets. The control technology of the slab in the induction heating process mostly adopts the constant voltage temperature open-loop control method, and the temperature rise curve control is single, which cannot be carried out. Flexible adjustment; during the heating process, the working state of the pyrometer feedback value used for temperature detection is unstable, and there are abnormal disturbances; the accuracy of the slab temperature control is not high, and there is a trend of temperature oscillation in the soaking section, and the deviation from the target temperature is within 5°C-10 Between ℃
The above control defects are not conducive to the adjustment and optimization of grain-oriented silicon steel process parameters. After the slab is heated, the performance stability of the finished product is not high, the temperature technical requirements after rough rolling cannot be guaranteed, and the material preparation requirements of the downstream cold rolling process cannot be met in batches.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sensing and heating method of high-magnetic induction oriented silicon steel
  • Sensing and heating method of high-magnetic induction oriented silicon steel
  • Sensing and heating method of high-magnetic induction oriented silicon steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] An induction heating method for high magnetic induction oriented silicon steel provided in the embodiment of the present invention includes the following steps, and the specific parameters are shown in Table 1:

[0028] Table 1 Specific parameters of each heating step

[0029]

[0030] Step A Put the slab of high magnetic induction grain-oriented silicon steel with the brand Q01G and the specification of 200*1130 into the induction heating furnace for heating, and use the inverter to set the basic voltage, wherein, in this embodiment, the basic voltage is 2300V . Then carry out constant voltage rapid temperature rise, the longest heating time is no more than 25min, the slab temperature after heating is 1320°C, wherein, the temperature of the slab entering the furnace is controlled above 900°C, the oxygen content in the furnace is kept below 1000PPM, and the nitrogen in the furnace is kept 2 The ambient positive pressure difference is 3 Pa. The purpose of this is to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sensing and heating method of high-magnetic induction oriented silicon steel, which belongs to the technical field of the heating of roll steel. The sensing and heating method comprises following steps that a high-magnetic induction oriented silicon steel plate blank is placed into a sensing and heating furnace to be controlled and heated in stages, basic voltage is set by an inverter on a starting heating stage, constant-voltage rapid heating is conducted, then a variation relation between the temperature of the plate blank and the voltage of the inverter is established, a temperature increase curve of the plate blank is set, closed-loop temperature increase is conducted by a temperature closed-loop controller according to the temperature increase curve, finally the closed-loop soaking control is conducted by adopting a variable-voltage temperature closed-loop controller, and the maximal soaking time is not greater than 30min. The stable and precise control of the temperature is fed back by a radiation high-temperature gauge through a temperature filter control technology in the heating process of the plate blank. Due to the adoption of the sensing and heating method, the problem that the control precision is not high under the temperature open-loop control mode and the control disturbance problem caused by the abnormal fluctuation of the temperature of the high temperature gauge occurred in the heating process can be effectively solved.

Description

technical field [0001] The invention belongs to the technical field of rolling steel heating, and relates to an induction heating method for high magnetic induction oriented silicon steel. Background technique [0002] In order to improve the production efficiency of high magnetic induction grain-oriented silicon steel and maintain the stability of mass production, many steel mills have been devoting themselves to the development and research of low temperature heating-high temperature rolling rolling route in the hot rolling process. Among them, the induction heating technology of the electromagnetic induction furnace is the most superior. The electromagnetic induction heating furnace is based on the principle of electromagnetic induction. The intermediate slab with a temperature above 1000°C placed horizontally on the roller table is turned over and moved horizontally on the roller table through the slab turning and conveying device, and then vertically loaded into the indu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/42C21D11/00
CPCY02P10/25
Inventor 武振威刘彦曹恒李冰周广成刘志民
Owner BEIJING SHOUGANG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products