Flexible physiological dry electrode and preparation method thereof
A dry electrode and physiological technology, applied in the field of biomedicine, can solve the problems of high contact impedance and poor safety performance, and achieve the effects of strong reliability, low cost and wide range of use.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] The present invention also provides a method for preparing a flexible physiological dry electrode, which includes the following steps:
[0033] (1) Stack the connecting buckle with a piece of foil and put it in a container;
[0034] In this example, the container is a petri dish. In practical applications, the container can be any of a petri dish, a beaker, and the like. The foil used in the present invention can be any material, and the thickness of the foil can be determined according to the thickness of the electrode. Preferably, the diameter of the foil is 0.5 cm-3 cm and the thickness is 1 mm-0.5 cm.
[0035] (2) Pour the polydimethylsiloxane into the container, fill the container and put it into the oven to cure the polydimethylsiloxane.
[0036] (3) After curing, take the polydimethylsiloxane connected with the connecting buckle and the foil out of the container, remove the foil, and form a groove on the cured dimethylsiloxane.
[0037] (4) Mix polydimethylsiloxane with c...
Example Embodiment
[0043] Example one
[0044] Such as Figure 2a to Figure 2d As shown, the foil 3 and the connecting buckle 2 are placed in a petri dish 4, injected with polydimethylsiloxane 5, and placed in an oven to cure at 70°C for 2 hours. After curing, remove the petri dish 3, turn the polydimethylsiloxane connection foil 3 and the connection buckle 2 over, remove the foil 3, and form a groove on the cured polydimethylsiloxane, and then The polydimethylsiloxane 6 doped with carbon nanotubes is cast into the groove 7 and cured in an oven at 70° C. for 2 hours. Finally, the polydimethylsiloxane 5 is removed to obtain the flexible physiological dry electrode of the present invention, such as figure 1 Shown.
[0045] The actual application requirements of this embodiment are as shown in Table 1, which is a set of preferred design parameters of the flexible physiological dry electrode of the present invention.
[0046] Foil diameter
[0047] Table I
[0048] The invention adopts the conductive ...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap