A technology for resin materials and buttons is applied in the field of resin materials for preparing buttons, which can solve the problem of no button materials, and achieve the effects of low cost and good mechanical properties.
Inactive Publication Date: 2013-01-02
KUNSHAN JIEMING TEXTILE
View PDF0 Cites 10 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, in the field of garment manufacturing, there is no report a...
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0012] The resin material that is used to prepare button of present embodiment comprises:
[0013] 80 parts of isophthalic unsaturated polyester resins;
[0014] 20 parts of calcium carbonate powder;
[0015] 2 parts of methyl ethyl ketone peroxide;
[0016] 2 parts of cobalt naphthenate;
[0017] 3 parts of styrene;
[0018] 2 parts color paste.
Embodiment 2
[0020] The resin material that is used to prepare button of present embodiment comprises:
[0021] 80 parts of bisphenol A type unsaturated polyester resin;
[0022] 200 parts of talc and silicon dioxide;
[0023] 2-3 parts of methyl ethyl ketone peroxide;
[0024] 2-3 parts of cobalt isooctanoate;
[0025] 3-8 parts of ethyl methacrylate;
[0026] 8 parts pearl paste.
Embodiment 3
[0028] The resin material that is used to prepare button of present embodiment comprises:
[0029] 50 parts of isophthalic unsaturated polyester resins;
[0030] 100 parts of magnesium silicate;
[0031] 2 parts of methyl ethyl ketone peroxide;
[0032] 3 parts cobalt isooctanoate;
[0033] 5 parts of methyl acrylate;
[0034] 5 parts pearl paste.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a resin material used for preparing buttons. The material comprises the raw materials of, by weight: 80 parts of unsaturated polyester resin, 20-200 parts of inorganic powder, 2-3 parts of a curing agent, 2-3 parts of an accelerating agent, and 3-8 parts of a monomer diluent. The unsaturated polyester resin is isophthalic-type unsaturated polyester resin or bisphenol A-type unsaturated polyester resin. The inorganic powder is one or a combination of more than two selected from calcium carbonate, talcum powder, silica, and magnesium silicate. The curing agent is methyl ethyl ketone peroxide. The accelerating agent is cobalt naphthenate or cobalt isooctanoate. The monomer diluent is one or a combination of more than two selected from styrene, ethyl methacrylate, and methyl acrylate. Buttons prepared by using the material have the advantages of good mechanical properties and low cost.
Description
technical field [0001] In particular, the present invention relates to a resin material for making buttons. Background technique [0002] Generally, the main raw material used to make buttons is unsaturated polyester resin, which is made by adding appropriate amount of additives, gelling in specific equipment and molds, curing into pearlescent or non-pearlescent plates, and then mechanically processed. [0003] According to literature reports, when the product is prepared by filling unsaturated polyester resin with inorganic materials, the impact performance of the product is slightly improved at a low addition amount, and the impact performance will be significantly reduced after a certain amount is exceeded. For example, the published literature in "Research on the Toughening and Reinforcement of Unsaturated Resin by Nano-calcium Carbonate Particles" ("China Plastics", Issue 7, July 2002) shows that the impact performance of calcium carbonate can reach 5KJ.m when the a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more