Production process of luminous ceramic product

A production process and technology of ceramic products, applied in the field of production technology of luminous ceramic products, can solve the problems of high firing temperature requirements, short luminous time, affecting the use and popularization of luminous products, and achieve the effect of low excitation conditions and easy promotion

Inactive Publication Date: 2013-01-30
张云龙
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the glow-in-the-dark products currently on the market have a short luminous time, and can only emit light for 2 hours when exposed to sunlight for 10 minutes or fluorescent lamps for 60 minutes.
Moreover, the production process of luminous product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1: The production process of luminous ceramic tiles, the steps are as follows:

[0039] Ⅰ. Making luminous glaze;

[0040] The ingredients of the luminous glaze include basic ingredients and luminous powder. The luminous powder accounts for 10% of the total mass;

[0041] The various components in the basic ingredients and their respective mass percentages in the total weight of the basic ingredients are:

[0042] si: 22%

[0043] AL: 6.3%

[0044] H 3 BO 3 37%

[0045] Na 7.7%

[0046] Sr 0.8%

[0047] F 0.5%

[0048] Pr 0.7%

[0049] Zn 3.5%

[0050] Ca 1.3%

[0051] Bi 8.2%

[0052] Mg 12%.

[0053] The manufacturing process of luminous glaze is as follows:

[0054] a. After weighing according to the formula, mix the basic ingredients uniformly, and then enter the kiln for calcination. The calcination temperature is 1350 degrees Celsius, and it is transparent at 900 degrees Celsius. After being fi...

Example Embodiment

[0064] Embodiment two:

[0065] The production process of luminous ceramic vase includes the following steps:

[0066] Ⅰ. Making luminous glaze;

[0067] The ingredients of the luminous glaze include basic ingredients and luminous powder. The luminous powder accounts for 39% of the total mass;

[0068] The various components in the basic ingredients and their respective mass percentages in the total weight of the basic ingredients are:

[0069] si: 22%

[0070] AL: 6.3%

[0071] H 3 BO 3 37%

[0072] Na 7.7%

[0073] Sr 0.8%

[0074] F 0.5%

[0075] Pr 0.7%

[0076] Zn 3.5%

[0077] Ca 1.3%

[0078] Bi 8.2%

[0079] Mg 12%.

[0080] The manufacturing process of luminous glaze is as follows:

[0081] a. After weighing according to the formula, mix the basic ingredients uniformly, and then enter the kiln for calcination. The calcination temperature is 1350 degrees Celsius, and it is transparent at 900 degrees Celsius. ...

Example Embodiment

[0091] Example three:

[0092] The production process of luminous ceramic knives includes the following steps:

[0093] Ⅰ. Making luminous glaze;

[0094] The ingredients of the luminous glaze include basic ingredients and luminous powder. The luminous powder accounts for 60% of the total mass percentage;

[0095] The various components in the basic ingredients and their respective mass percentages in the total weight of the basic ingredients are:

[0096] si: 22%

[0097] AL: 6.3%

[0098] H 3 BO 3 37%

[0099] Na 7.7%

[0100] Sr 0.8%

[0101] F 0.5%

[0102] Pr 0.7%

[0103] Zn 3.5%

[0104] Ca 1.3%

[0105] Bi 8.2%

[0106] Mg 12%.

[0107] The process of making luminous glaze is as follows:

[0108] a. After weighing according to the formula, mix the basic ingredients uniformly, and then enter the kiln for calcination. The calcination temperature is 1350 degrees Celsius, and it is transparent at 900 degrees Cels...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production process of a luminous ceramic product, which belongs to the field of production processes of ceramic materials, and particularly relates to a production process of a luminous ceramic product. A manufacturing process comprises the steps of manufacturing a luminous glaze material, printing, burning, reshaping and the like. The luminous ceramic product disclosed by the invention is a high-technology environment-friendly product, has unique decorating and warning functions, can be widely applied to warning sign systems and emergency evacuation systems of various public utilities, and can be specifically applied to places such as stairs, passages, wall sides, door number plates, floors, decks, lifeboats, buoyant apparatuses, firefighting devices and the like. The luminous ceramic product has the advantages of super-long afterglow, high weather resistance, no influence of weather on the luminous time, acid resistance, alkali resistance, and no change in 100 years.

Description

technical field [0001] The invention belongs to the field of production technology of ceramic materials, and in particular relates to a production technology of luminous ceramic products. Background technique [0002] Luminous products have been more and more widely used in all aspects of production and life, because they do not require electricity or other energy consumption, are easy to install, and are not affected by climate or other outdoor factors. They are very popular in the market. However, the glow-in-the-dark products currently on the market have a relatively short luminous time, and can only emit light for 2 hours under the condition of 10 minutes of sunlight or 60 minutes of fluorescent lamps. Moreover, the production process of luminous products is complicated, the firing temperature is high, and the radiation is strong, so it is difficult to meet the environmental protection requirements. The existence of these drawbacks has seriously affected the use and pop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 张云龙
Owner 张云龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap