Preparation method of bacterial cellulose base power generating fibers and yarns

A bacterial cellulose and superfine fiber technology, applied in the direction of single-component cellulose rayon, fiber treatment, plant fiber, etc., can solve the problems of reduced efficiency and mediocre work efficiency

Inactive Publication Date: 2014-09-03
ZHONGYUAN ENGINEERING COLLEGE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But current materials don't work very well due to their mediocre overall efficiency and drastic drop in efficiency in wet environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of the bacterial cellulose-based power generation fiber of the present embodiment comprises the following steps:

[0027] (1) Place the bleached bacterial cellulose wet film between a pair of holding rollers and feed it at a speed of 10 mm to 100 m / min; the diameter of the holding rollers used is 20 to 3000 mm.

[0028] (2) The cellulose film output from between the rollers is punctured, split and combed at a high speed by needle-punching on the surface of the licker-in roller, and the bacterial cellulose wet film is transformed into bacterial cellulose fibers; the bacterial cellulose fibers are filtered through a filter press treatment to prepare bacterial cellulose superfine fiber strips; take it out and freeze dry it for use; the moisture content of bacterial cellulose superfibers after pressure filtration is between 15% and 50000%, and the diameter of superfine fibers is between 10 and 50000%. 500nm, ultrafine fiber length between 200nm~200mm....

Embodiment 2

[0034] The preparation method of the bacterial cellulose-based power generation fiber of the present embodiment comprises the following steps:

[0035] (1) Place the bleached bacterial cellulose wet film between a pair of holding rollers and feed it at a speed of 10 mm to 100 m / min; the diameter of the holding rollers used is 50 to 1000 mm.

[0036](2) The cellulose film output from between the rollers is punctured, split and combed at a high speed by needle-punching on the surface of the licker-in roller, and the bacterial cellulose wet film is transformed into bacterial cellulose fibers; the bacterial cellulose fibers are filtered through a filter press treatment to prepare bacterial cellulose superfine fiber strips; freeze-dry after taking out, and stand-by; the moisture content of the bacterial cellulose superfibers processed by pressure filtration is preferably between 30% and 3000%, and the diameter of the superfine fibers is preferably between 30% and 3000%. 3~300nm, th...

Embodiment 3

[0042] The preparation method of the bacterial cellulose-based power generation fiber of the present embodiment comprises the following steps:

[0043] (1) Place the bleached bacterial cellulose wet film between a pair of holding rollers and feed it at a speed of 10 mm to 100 m / min; the diameter of the holding rollers used is 20 mm.

[0044] (2) The cellulose film output from between the rollers is punctured, split and combed at a high speed by needle-punching on the surface of the licker-in roller, and the bacterial cellulose wet film is transformed into bacterial cellulose fibers; the bacterial cellulose fibers are filtered through a filter press treatment to prepare bacterial cellulose superfine fiber strips; freeze-drying after taking out, and stand-by; the moisture content of bacterial cellulose superfibers treated by pressure filtration is between 15%, and the diameter of superfine fibers is 10nm. The length is between 200nm.

[0045] (3) Copper vacuum sputtering coatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A method for preparing bacterial cellulose-based power generation fibers, which comprises immersing bacterial cellulose superfine fiber strips in nano-ZnO sol to obtain bacterial cellulose B, which is taken out for use; the bacterial cellulose B is put into an amino zinc salt solution, reacted After a period of time, bacterial cellulose C is formed; the bacterial cellulose C is subjected to surface metallization treatment; bacterial cellulose fibers with power generation properties are prepared. The finished product made by the method of the invention is the bacterial cellulose-based power generation fiber and yarn, which can be further processed through the existing weaving and weaving technology. The formation of mechanical power generation components of different scales is widely used in fields such as environmental monitoring, biochip implantation in the body, automobiles, construction, military, etc. that have different size power requirements for self-generating components.

Description

technical field [0001] The invention relates to a preparation method of bacterial cellulose-based power-generating fibers and yarns, in particular to a preparation method of bacterial cellulose-based power-generating fibers and yarns that can be applied to self-generating power sources of miniature and high-performance electronic devices and sensors. Background technique [0002] With the development of economy and society, electricity has become an indispensable part of society. The current situation of electricity in our country is lack of electricity in cities, remote areas without electricity, valleys in spring and autumn, and peaks in winter and summer. Although the country has started the west-to-east power transmission project, the power loss of long-distance power transmission and the high cost of laying lines have made the cost of power rise instead of falling. According to data released by the China Electricity Council, my country's electricity consumption reached...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M11/83D06M13/358D06M13/432D06M11/60D06M13/328D06M11/74D06M15/61D06M15/37D01F2/00D01D5/42D02G3/02D06M101/06
Inventor 张迎晨吴红艳
Owner ZHONGYUAN ENGINEERING COLLEGE