Method for brazing SiO2f/SiO2 composite ceramic and metal material

A technology of composite ceramics and metal materials, which is applied in the field of welding, can solve the problems of the lack of effective methods to relieve the thermal stress of joint welding, and achieve the effects of reducing residual thermal stress, avoiding cracking, and avoiding poor thermal expansion coefficients

Active Publication Date: 2013-02-13
AVIC BEIJING INST OF AERONAUTICAL MATERIALS
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Invention patent (inventors: Xiong Huaping, Chen Bo, Cheng Yaoyong, Li Xiaohong, Mao Wei. A kind of SiO 2f /SiO 2 Brazing process of composite ceramics and metal materials, patent application date: August 31, 2010, patent number: ZL 2010 1 0266686.0, authorization announcement date: September 26, 2012) It is proposed that the SiO 2f /SiO 2 The surface to be welded of the composite ceramics is grooved, and then the AgCu-Ti active solder is placed on the SiO 2f /SiO 2 At the groove of the surface of the composite ceramic to be welded, and in the welded SiO 2f /SiO 2 Add AgCu-Ti solder to the interface to be we...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for brazing SiO2f/SiO2 composite ceramic and metal material
  • Method for brazing SiO2f/SiO2 composite ceramic and metal material
  • Method for brazing SiO2f/SiO2 composite ceramic and metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] See attached Figure 1~2 As shown, before welding, the SiO 2f / SiO 2 The welded surface of the composite ceramic is processed with a through-shaped open groove 1, the shape of the lower part of the open groove 1 is approximately conical or square, and the two side walls 2 of the open groove 1 are in contact with the welded SiO 2f / SiO 2 The included angle of the composite ceramic surface is 60°~80°; the opening groove (1) is in SiO 2f / SiO 2 The surface of the composite ceramic to be welded is in a through shape, the opening width of the opening groove (1) is 3.0mm-15.0mm, the opening depth is 3.0mm-15.0mm, and the distance between adjacent opening grooves (1) is 5.0mm- 15.0mm;

[0028] Next, separately process the mosaic block 3 whose size matches the cross-sectional shape of the above-mentioned opening groove 1. The material of the mosaic block 3 can be metal Cu, or Nb, or Mo, or Fe, or Ti, or W, or respectively An alloy based on one of Cu, Ni, Nb, Mo, Fe,...

Embodiment 2

[0032] See attached image 3 As shown, before welding, the SiO 2f / SiO 2 The annular welded surface of the composite ceramic is processed with an open groove 1, the shape of the lower part of the open groove 1 is approximately conical, and the two side walls 2 of the open groove 1 are in contact with the welded SiO 2f / SiO 2 The included angle of the composite ceramic surface is 60°~80°; the opening groove (1) is in SiO 2f / SiO 2 The surface of the composite ceramic to be welded is in a through shape, the opening width of the opening groove (1) is 3.0mm-15.0mm, the opening depth is 3.0mm-15.0mm, and the distance between adjacent opening grooves (1) is 5.0mm- 15.0mm;

[0033] Next, separately process the mosaic block 3 whose size matches the cross-sectional shape of the above-mentioned opening groove 1. The material of the mosaic block 3 can be metal Cu, or Nb, or Mo, or Fe, or Ti, or W, or respectively An alloy based on one of Cu, Ni, Nb, Mo, Fe, Ti, W, or the meta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for brazing a SiO2f/SiO2 composite ceramic and a metal material. The method comprises the following steps of: uniformly processing a plurality of open grooves in a surface to be brazed of the SiO2f/SiO2 composite ceramic; correspondingly singly processing mosaic blocks of which the sizes are matched with those of the open grooves and the quantity is the same as that of the open grooves; assembling the mosaic blocks into the open grooves in the surface layer of the brazed SiO2f/SiO2 composite ceramic one by one; filling AgCu-based active solders on an interface between each metal mosaic block and each open groove and on the interface to be brazed between the brazed SiO2f/SiO2 composite ceramic and the brazed metal material; and effectively binding the SiO2f/SiO2 composite ceramic of a large size with the metal material in a vacuum brazing heating mode. The method is also suitable for binding between C/C composite materials, Cf/SiC composite materials, SiCf/SiC composite materials, Al2O3 ceramics, SiC ceramics as well as Sialon ceramics of the larger size and the metal material.

Description

technical field [0001] The present invention is a SiO 2f / SiO 2 The invention relates to a brazing method for composite ceramics and metal materials, which belongs to the technical field of welding. Background technique [0002] Quartz fiber reinforced quartz composite ceramics (SiO 2f / SiO 2 ) is a promising high-temperature structural ceramic matrix composite material. However, due to the special requirements for the combination of performance in some engineering applications, it is necessary to form a composite structure with metal materials for application. [0003] SiO 2f / SiO 2 The connection of composite ceramics is generally suitable for brazing or diffusion welding methods, but direct SiO 2f / SiO 2 The bonding of composite ceramics to metals is very difficult because SiO 2f / SiO 2 The thermal expansion coefficients of composite ceramics and metals are very different (the former is about 0.3×10 -6 K -1 , the latter is generally about 5.5~15×10 -6 K -1 ,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B37/02
Inventor 熊华平陈波郭绍庆毛唯
Owner AVIC BEIJING INST OF AERONAUTICAL MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap