Planar vacuum glass welded by metal solders in microwave manner and subjected to edge sealing by groove, and manufacturing method of glass

A vacuum glass and welding surface technology, which is applied in glass manufacturing equipment, glass production, glass molding, etc., can solve the problems of inappropriateness, restriction of radiation heat transfer, and large space occupied by auxiliary seals, etc.

Inactive Publication Date: 2013-03-06
戴长虹
View PDF10 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the patent CN94192667.2 "Method for Manufacturing Vacuum Glass Windows", the edge sealing structure is designed so that the upper glass is slightly smaller than the lower glass in the two glasses, and the low melting point glass solder is placed on the edge steps formed by the two glasses, and the melted glass Solder flows into the gap between two pieces of glass due to capillary phenomenon. This method is the most representative and practical edge sealing technology at present, but it has the disadvantages of large amount of solder, uneven edges and high stress; patent CN95108228.0 "vacuum Flat glass and its manufacturing method" and CN96208977.X "vacuum flat glass", the edge of the glass plate is used to "chamfer" first, and the solder is placed in the chamfering groove. This method has the difficulty of distributing and the low-melting point glass solder is heated. Deficiencies that are easily lost during fusing and sealing; the patent CN02256440.3 "vacuum glass edge sealing structure" is to put auxiliary sealing strips on the upper periphery of the lower flat glass to prevent the loss of solder liquid. Although this method solves the problem of solder liquid's outward loss , but the process is complicated, and the auxiliary sealing strip takes up a large space, and it cannot solve the problem that the solder liquid flows into the glass; the edge sealing method of the vacuum glass proposed in the patent CN200620070302.7 "fully transparent vacuum glass" is to make the edge of the glass together with the glass The disadvantage is that the edge banding is not only expensive to manufacture but also cannot restrict the flow of low-temperature solder to the inside of the glass; patent CN200920314752.X "Edge banding structure of vacuum glass" is based on the glass and the The top glass and/or the base glass between the edge of the glass is made with a geometric filling groove, although it can improve the adhesion of the sealing filler between the base glass and the top glass, but the filling groove of the upper and lower glass is difficult. At the same time, the sealing packing is filled, and the random flow of the sealing packing cannot be restricted; Patent CN201010228110.5 "A Vacuum Glass Edge Sealing Method" is to put glass welding material around the periphery of the vacuum glass original plate, and set a layer inside the glass welding material The inner anti-seepage layer made of powdery or fibrous materials restricts the glass solder liquid from flowing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Planar vacuum glass welded by metal solders in microwave manner and subjected to edge sealing by groove, and manufacturing method of glass
  • Planar vacuum glass welded by metal solders in microwave manner and subjected to edge sealing by groove, and manufacturing method of glass
  • Planar vacuum glass welded by metal solders in microwave manner and subjected to edge sealing by groove, and manufacturing method of glass

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0061] Embodiment 1: see figure 1 , the vacuum glass is composed of upper and lower pieces of glass, one of which is low-emissivity glass. Edge sealing grooves are opened at the welding place, and edge grinding, chamfering, cleaning and drying are carried out, and low-temperature glass powder paste is printed on the upper glass with polyester screen to make edge sealing strips and supports; the upper glass has two There are two edge-sealed frames and the lower glass has two edge-sealed grooves. After the upper and lower glass are combined, the edge-sealed frame of the upper glass can be embedded in the edge-sealed groove of the lower glass; the width of the upper glass edge-sealed frame is 1.5 mm, the height is 0.3mm, the width of the lower glass edge sealing groove is 2.5mm, and the depth is 0.5mm. The support is a lattice arrangement of equilateral triangles with the smallest unit. The side length of the triangle is 30mm, and the support is cylindrical. , with a diameter of...

Example Embodiment

[0064] Example 2: see figure 1 , the vacuum glass is composed of upper and lower pieces of glass, both of which are ordinary float glass, and its production method is as follows: first, cut two pieces of flat glass of the required size according to the shape and size of the vacuum glass to be produced, and weld them on the periphery of the lower glass Edge sealing grooves are opened at the edge, and edge grinding, chamfering, cleaning and drying are carried out. On the upper glass, the low-temperature glass powder paste is printed into edge sealing strip frames by printing technology. The upper glass has two edge sealing strip frames, and the lower glass The glass has two edge-sealing grooves. After the upper and lower glass are combined, the edge-sealing strip frame of the upper glass can be embedded in the edge-sealing groove of the lower glass; secondly, the upper glass is sent to the high-temperature furnace, and the temperature of the high-temperature furnace is 550~650℃. ...

Example

[0066] Example 3: see figure 2 , one of the two pieces of vacuum glass is low-emissivity glass, and the other is tempered glass or half-tempered glass. For radiant glass, edge sealing grooves are set at the peripheral welding of the lower glass, and the edges are ground, chamfered, cleaned, and dried. On the upper glass, the low-temperature glass powder paste is printed on the upper glass to form an edge sealing strip frame. There is an edge banding frame, and the lower glass has an edge banding groove. After the upper and lower glass are combined, the edge banding frame of the upper glass can be embedded in the edge banding groove of the lower glass; First print or spray a layer of paste containing low-temperature glass powder on the position of the side groove, and then print or spray a layer of commercially available silver paste as a transition layer; secondly, send the upper glass into the tempering furnace, in the tempering furnace 650~ Under the action of high tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses vacuum glass. The vacuum glass consists of upper glass and lower glass and is characterized in that the welding periphery of the upper glass is provided with an edge sealing strip frame, and the welding periphery of the lower glass is provided with an edge sealing groove; and the upper and lower glass are welded together by metal or alloy solders in a microwave oven, so that the vacuum glass is simpler and more convenient to manufacture, and a sealing effect is ensured by the embedding combination of the edge sealing strip frame and the edge sealing groove. A manufacturing method of the vacuum glass provided by the invention is simple in process, low in cost and high in production efficiency, can ensure reliable sealing connection and the good sealing effect, can be used for manufacturing vacuum glass without extraction openings in mass by virtue of a one-step method, and can be used for manufacturing not only common vacuum glass but also tempered vacuum glass.

Description

technical field [0001] The invention relates to the processing and manufacturing of vacuum glass, in particular to a method for making vacuum glass and its products. Background technique [0002] Vacuum glass is a new type of energy-saving and environmentally friendly product, which can be widely used in industrial and agricultural fields such as building doors and windows, glass curtain walls, solar products, agricultural greenhouses, refrigerators and refrigerators, and daily necessities for residents. Soundproofing and finishing materials. In the process of making vacuum glass, the structure and technology of edge sealing is the key technology to ensure that the periphery of vacuum glass is not deformed, does not produce excessive stress, does not leak air, and maintains the characteristics of tempered glass. In the patent CN94192667.2 "Method for Manufacturing Vacuum Glass Windows", the edge sealing structure is designed so that the upper glass is slightly smaller than ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03B23/24
CPCY02P40/57
Inventor 戴长虹
Owner 戴长虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products